RESUMO
Seeking to improve personal armor equipment by providing mobility and resistance to penetration, this research aimed to explore the potential of sustainable materials in order to assess their ability in ballistic applications. Titica vine fibers (TVFs) extracted from aerial roots of Heteropsis flexuosa from the Amazon region were incorporated at 10, 20, 30, and 40 vol% into an epoxy matrix for applications in ballistic multilayered armor systems (MASs) and stand-alone tests for personal protection against high-velocity 7.62 mm ammunition. The back-face signature (BFS) depth measured for composites with 20 and 40 vol% TVFs used as an intermediate layer in MASs was 25.6 and 32.5 mm, respectively, and below the maximum limit of 44 mm set by the international standard. Fracture mechanisms found by scanning electron microscopy (SEM) attested the relevance of increasing the fiber content for applications in MASs. The results of stand-alone tests showed that the control (0 vol%) and samples with 20 vol% TVFs absorbed the highest impact energy (Eabs) (212-176 J), and consequently displayed limit velocity (VL) values (213-194 m/s), when compared with 40 vol% fiber composites. However, the macroscopic evaluation found that, referring to the control samples, the plain epoxy shattered completely. In addition, for 10 and 20 vol% TVFs, the composites were fragmented or exhibited delamination fractures, which compromised their physical integrity. On the other hand, composites with 30 and 40 vol% TVFs, whose Eabs and VL varied between 166-130 J and 189-167 m/s, respectively, showed the best physical stability. The SEM images indicated that for composites with 10 and 20 vol% TVFs, the fracture mode was predominantly brittle due to the greater participation of the epoxy resin and the discrete action of the fibers, while for composites with 30 and 40 vol% TVFs, there was activation of more complex mechanisms such as pullout, shearing, and fiber rupture. These results indicate that the TVF composite has great potential for use in bulletproof vests.
RESUMO
Multilayered armor systems (MAS) with a front ceramic layer backed by a relatively unknown Amazonian guaruman fiber-reinforced (Ischnosiphon koem) epoxy composites, as second layer, were for the first time ballistic tested against the threat of 7.62 mm rifle ammunition. The amount of 30 vol% guaruman fibers was investigated in three distinct configurations: (i) continuous aligned, (ii) 0-90° cross-laid, and (iii) short-cut randomly dispersed. Additionally, single-target ballistic tests were also carried out in the best MAS-performed composite with cross-laid guaruman fibers against .22 caliber ammunition. The results disclosed that all composites as MAS second layer attended the US NIJ standard with corresponding penetration depth of (i) 32.9, (ii) 27.5, and (iii) 29.6 mm smaller than the lethal limit of 44 mm in a clay witness simulating a personal body. However, the continuous aligned guaruman fiber composite lost structural integrity by delamination after the 7.62 projectile impact. By contrast, the composite with cross-laid guaruman fibers kept its integrity for subsequent shootings as recommended by the standard. The single-target tests indicated a relatively higher limit velocity for .22 caliber projectile perforation, 255 m/s, and absorbed energy of 106 J for the cross-laid guaruman fibers, which are superior to corresponding results for other less known natural fiber epoxy composites.
RESUMO
The ballistic performance of plain woven jute fabric-reinforced polyester matrix composites was investigated as the second layer in a multilayered armor system (MAS). Volume fractions of jute fabric, up to 30 vol %, were mixed with orthophthalic polyester to fabricate laminate composites. Ballistic tests were conducted using high velocity 7.62 mm ammunition. The depth of penetration caused by the bullet in a block of clay witness, simulating a human body, was used to evaluate the MAS ballistic performance according to the international standard. The fractured materials after tests were analyzed by scanning electron microscopy (SEM). The results indicated that jute fabric composites present a performance similar to that of the much stronger Kevlar™, which is an aramid fabric laminate, as MAS second layer with the same thickness. The mechanism of this similar ballistic behavior as well as the comparative advantages of the jute fabric composites over the Kevlar™ are discussed.