RESUMO
UNLABELLED: Dentin bonding performed with hydrophobic resins using ethanol-wet bonding should be less susceptible to degradation but this hypothesis has never been validated. OBJECTIVES: This in vitro study evaluated stability of resin-dentin bonds created with an experimental three-step BisGMA/TEGDMA hydrophobic adhesive or a three-step hydrophilic adhesive after one year of accelerated aging in artificial saliva. METHODS: Flat surfaces in mid-coronal dentin were obtained from 45 sound human molars and randomly divided into three groups (n=15): an experimental three-step BisGMA/TEGDMA hydrophobic adhesive applied to ethanol (ethanol-wet bonding-GI) or water-saturated dentin (water-wet bonding-GII) and Adper Scotchbond Multi-Purpose [MP-GIII] applied, according to manufacturer instructions, to water-saturated dentin. Resin composite crowns were incrementally formed and light-cured to approximately 5mm in height. Bonded specimens were stored in artificial saliva at 37 degrees C for 24h and sectioned into sticks. They were subjected to microtensile bond test and TEM analysis immediately and after one year. Data were analyzed with two-way ANOVA and Tukey tests. RESULTS: MP exhibited significant reduction in microtensile bond strength after aging (24h: 40.6+/-2.5(a); one year: 27.5+/-3.3(b); in MPa). Hybrid layer degradation was evident in all specimens examined by TEM. The hydrophobic adhesive with ethanol-wet bonding preserved bond strength (24h: 43.7+/-7.4(a); one year: 39.8+/-2.7(a)) and hybrid layer integrity, with the latter demonstrating intact collagen fibrils and wide interfibrillar spaces. SIGNIFICANCE: Coaxing hydrophobic resins into acid-etched dentin using ethanol-wet bonding preserves resin-dentin bond integrity without the adjunctive use of MMPs inhibitors and warrants further biocompatibility and patient safety's studies and clinical testing.
Assuntos
Colagem Dentária/métodos , Adesivos Dentinários , Dentina , Cimentos de Resina , Resinas Compostas , Coroas , Infiltração Dentária , Análise do Estresse Dentário , Permeabilidade da Dentina , Adesivos Dentinários/química , Etanol , Humanos , Interações Hidrofóbicas e Hidrofílicas , Teste de Materiais , Microscopia Eletrônica de Transmissão , Cimentos de Resina/química , Resistência à Tração , Fatores de Tempo , ÁguaRESUMO
OBJECTIVES: To evaluate the efficacy of simplified dehydration protocols, in the absence of tubular occlusion, on bond strength and interfacial nanoleakage of a hydrophobic experimental adhesive blend to acid-etched, ethanol-dehydrated dentine immediately and after 6 months. METHODS: Molars were randomly assigned to 6 treatment groups (n=5). Under pulpal pressure simulation, dentine crowns were acid-etched with 35% H(3)PO(4) and rinsed with water. Adper Scotchbond Multi-Purpose was used for the control group. The remaining groups had their dentine surface dehydrated with ethanol solutions: group 1=50%, 70%, 80%, 95% and 3x100%, 30s for each application; group 2 the same ethanol sequence with 15s for each solution; groups 3, 4 and 5 used 100% ethanol only, applied in seven, three or one 30s step, respectively. After dehydration, a primer (50% BisGMA+TEGDMA, 50% ethanol) was used, followed by the neat comonomer adhesive application. Resin composite build-ups were then prepared using an incremental technique. Specimens were stored for 24h, sectioned into beams and stressed to failure after 24h or after 6 months of artificial ageing. Interfacial silver leakage evaluation was performed for both storage periods (n=5 per subgroup). RESULTS: Group 1 showed higher bond strengths at 24h or after 6 months of ageing (45.6+/-5.9(a)/43.1+/-3.2(a)MPa) and lower silver impregnation. Bond strength results were statistically similar to control group (41.2+/-3.3(ab)/38.3+/-4.0(ab)MPa), group 2 (40.0+/-3.1(ab)/38.6+/-3.2(ab)MPa), and group 3 at 24h (35.5+/-4.3(ab)MPa). Groups 4 (34.6+/-5.7(bc)/25.9+/-4.1(c)MPa) and 5 (24.7+/-4.9(c)/18.2+/-4.2(c)MPa) resulted in lower bond strengths, extensive interfacial nanoleakage and more prominent reductions (up to 25%) in bond strengths after 6 months of ageing. CONCLUSIONS: Simplified dehydration protocols using one or three 100% ethanol applications should be avoided for the ethanol-wet bonding technique in the absence of tubular occlusion, as they showed decreased bond strength, more severe nanoleakage and reduced bond stability over time.
Assuntos
Condicionamento Ácido do Dente/métodos , Colagem Dentária/métodos , Dentina/ultraestrutura , Etanol/química , Cimentos de Resina/química , Solventes/química , Bis-Fenol A-Glicidil Metacrilato/química , Resinas Compostas/química , Infiltração Dentária/classificação , Materiais Dentários/química , Dessecação , Humanos , Interações Hidrofóbicas e Hidrofílicas , Teste de Materiais , Ácidos Fosfóricos/química , Polietilenoglicóis/química , Ácidos Polimetacrílicos/química , Coloração pela Prata , Estresse Mecânico , Propriedades de Superfície , Resistência à Tração , Fatores de Tempo , Água/químicaRESUMO
The aim of this study was to evaluate the ability of five experimental resins, which ranged from hydrophobic to hydrophilic blends, to seal acid-etched dentine saturated with water or ethanol. The experimental resins (R1, R2, R3, R4, and R5) were evaluated as neat bonding agents (100% resin) or as solutions solvated with absolute ethanol (70% resin/30% ethanol). Fluid conductance was measured at 20 cm H(2)O hydrostatic pressure after sound dentine surfaces were: (i) covered with a smear layer; (ii) acid-etched; or (iii) bonded with neat or solvated resins, which were applied to acid-etched dentine saturated with water or ethanol. In general, the fluid conductance of resin-bonded dentine was significantly higher than that of smear layer-covered dentine. However, when the most hydrophobic neat resins (R1 and R2) were applied to acid-etched dentine saturated with ethanol, the fluid conductance was as low as that produced by smear layers. The fluid conductance of resin-bonded dentine saturated with ethanol was significantly lower than for resin bonded to water-saturated dentine, except for resin R4. Application of more hydrophobic resins may provide better sealing of acid-etched dentine if the substrate is saturated with ethanol instead of with water.