OBJECTIVES: To evaluate the efficacy of simplified dehydration protocols, in the absence of tubular occlusion, on bond strength and interfacial nanoleakage of a hydrophobic experimental adhesive blend to acid-etched, ethanol-dehydrated dentine immediately and after 6 months. METHODS: Molars were randomly assigned to 6 treatment groups (n=5). Under pulpal pressure simulation, dentine crowns were acid-etched with 35% H(3)PO(4) and rinsed with water. Adper Scotchbond Multi-Purpose was used for the control group. The remaining groups had their dentine surface dehydrated with ethanol solutions: group 1=50%, 70%, 80%, 95% and 3x100%, 30s for each application; group 2 the same ethanol sequence with 15s for each solution; groups 3, 4 and 5 used 100% ethanol only, applied in seven, three or one 30s step, respectively. After dehydration, a primer (50% BisGMA+TEGDMA, 50% ethanol) was used, followed by the neat comonomer adhesive application. Resin composite build-ups were then prepared using an incremental technique. Specimens were stored for 24h, sectioned into beams and stressed to failure after 24h or after 6 months of artificial ageing. Interfacial silver leakage evaluation was performed for both storage periods (n=5 per subgroup). RESULTS: Group 1 showed higher bond strengths at 24h or after 6 months of ageing (45.6+/-5.9(a)/43.1+/-3.2(a)MPa) and lower silver impregnation. Bond strength results were statistically similar to control group (41.2+/-3.3(ab)/38.3+/-4.0(ab)MPa), group 2 (40.0+/-3.1(ab)/38.6+/-3.2(ab)MPa), and group 3 at 24h (35.5+/-4.3(ab)MPa). Groups 4 (34.6+/-5.7(bc)/25.9+/-4.1(c)MPa) and 5 (24.7+/-4.9(c)/18.2+/-4.2(c)MPa) resulted in lower bond strengths, extensive interfacial nanoleakage and more prominent reductions (up to 25%) in bond strengths after 6 months of ageing. CONCLUSIONS: Simplified dehydration protocols using one or three 100% ethanol applications should be avoided for the ethanol-wet bonding technique in the absence of tubular occlusion, as they showed decreased bond strength, more severe nanoleakage and reduced bond stability over time.