RESUMO
OBJECTIVES: To evaluate the volume and depth of enamel loss promoted by 37.5% and 7.5% hydrogen peroxide (HP) gels, and quantify the loss of calcium (Ca) and phosphate (P) ions by using ion chromatography (IC) analysis after bleaching. METHODS: Sixty bovine enamel specimens were randomly divided into three groups: Control - no bleaching gel; HP37.5%, application of HP 37.5% for 45 minutes for 14 days; and HP7.5%, application of HP 7.5% for 3 applications of 8 minutes. The surface analysis (n=5) was performed using a scanning electron microscope (SEM) and dispersive energy system (EDS) to calcium and phosphorus dosage. The micro-CT was used for the enamel loss analysis (n=5). IC was used to analyze extracted Ca and P (n=10). Data were analyzed by one-way ANOVA and two-way repeated measures ANOVA, followed by Tukey and Dunnett's tests (α=0.05). RESULTS: Significantly higher volume and depth of enamel loss were found for bleached groups compared with the control group. HP7.5% had significantly higher enamel change than HP37.5%. SEM showed higher enamel porosity for HP37.5% and HP7.5% compared to control. The IC demonstrated a significant increase of Ca incorporated into the gel, however, only HP7.5% had a higher P presence than the control group. The HP7.5% showed higher Ca and P ion exchange than HP37.5% (p<0.001). CONCLUSION: HP37.5% and HP7.5%, caused enamel mineral changes compared with the control group. The IC method was demonstrated to be an effective methodology for detecting enamel mineral loss by the bleaching gel.
Assuntos
Clareadores Dentários , Clareamento Dental , Animais , Bovinos , Cálcio , Clareamento Dental/métodos , Esmalte Dentário , Microtomografia por Raio-X , Peróxido de Hidrogênio/química , Minerais , Fosfatos , GéisRESUMO
OBJECTIVES: The aim of this study was to evaluate the mineral content, expressed by calcium (Ca) and phosphate (P), in dental enamel exposed to bleaching agents using micro-computed tomography (micro-CT), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), and atomic force microscopy (AFM). METHODS: Sixty bovine dental enamel specimens were randomly divided into three groups (n=20): HP35ca (bleached using 35% hydrogen peroxide with Ca); HP35wca (bleached using 35% hydrogen peroxide without Ca); and control (without bleaching). Five specimens from each group were used for SEM and EDS analyses, 10 specimens were used for AFM analysis, and the remaining five specimens were used for micro-CT analysis. The pH of the gels was measured using a pH meter. The EDS and micro-CT data were analyzed using one-way ANOVA and Pearson's correlation test. The AFM data were analyzed using one-way ANOVA (α=0.05). RESULTS: The weight percentages of Ca and P obtained using EDS were similar between the bleached and control groups. Small, superficial changes were observed by SEM in the HP35wca group. The HP35ca group showed similar patterns to the control group. AFM results showed no significant changes in the enamel roughness in any of the tested groups. No significant difference in the volume or depth of structural enamel loss was found between gels with and without Ca. No mineral loss was observed in the dentin substrate. The EDS and micro-CT analysis data exhibited a high correlation (p<0.001). CONCLUSION: The addition of Ca to the bleaching gel had no beneficial effect on the bleached tooth enamel in terms of composition, mineral loss, and surface roughness. Micro-CT results exhibited a high correlation with the EDS results.
Assuntos
Cálcio , Esmalte Dentário , Microscopia , Espectrometria por Raios X , Clareadores Dentários , Microtomografia por Raio-X , Animais , Cálcio/análise , Cálcio/química , Bovinos , Esmalte Dentário/química , Esmalte Dentário/efeitos dos fármacos , Géis/química , Peróxido de Hidrogênio/química , Peróxido de Hidrogênio/farmacologia , Microscopia/métodos , Microscopia de Força Atômica , Microscopia Eletrônica de Varredura , Fosfatos/análise , Distribuição Aleatória , Clareamento Dental/métodos , Clareadores Dentários/química , Clareadores Dentários/farmacologiaRESUMO
A prótese total sobre implantes é uma alternativa para pacientes totalmente edêntulos com rebordo ósseo que não proporciona retenção e nem estabilidade para uma prótese total convencional. A prótese implanto-suportada e implanto-retida é o tipo de prótese que os pacientes têm maior preferência, sendo uma das melhores formas de reabilitação para pacientes desdentados total, reestabelece a função mastigatória, deglutição e também a capacidade fonética, trazendo maior conforto e segurança para o paciente resultando em melhor qualidade de vida. O objetivo deste trabalho é mostrar uma técnica alternativa para reabilitação total superior com prótese total implanto-suportada cerâmica com infraestrutura de zircônia.
The total prosthetic implant is an alternative to edentulous patients with bone edge which does not provide retention and stability or for a conventional denture. The implant-supported and implant-retained prosthesis is the type of prosthesis that patients have more preferably, one of the best forms of rehabilitation for full edentulous patients, restores chewing, swallowing and also the phonetic capacity, providing greater comfort and safety to the patient resulting in improved quality of life. The objective of this work is to show an alternative technique for maxillary complete rehabilitation with implant-supported denture with ceramic zirconia infrastructure.
RESUMO
This study evaluated the effect of dentin pretreatment with 2% chlorhexidine (CHX) or 24% ethylenediamine tetra-acetic acid gel (EDTA) on the dentin microtensile bond strength (µTBS) of resin cements. Composite blocks were luted to superficial noncarious human dentin (n=10) using two resin cements (RelyX ARC [ARC] and RelyX U100 [U100]) and three dentin pretreatments (without pretreatment-control, CHX, and EDTA). CHX was applied for 60 seconds on the acid-etched dentin in the ARC/CHX group, and for the same time on smear layer-covered dentin in the U100/CHX group. EDTA was applied for 45 seconds on smear-covered dentin in the U100/EDTA group, and it replaced phosphoric acid conditioning in the ARC/EDTA group for 60 seconds. After storage in water for 24 hours, specimens were prepared for microtensile bond strength testing. The results were submitted to two-way analysis of variance (ANOVA) followed by Tukey test. ARC produced significantly higher µTBS (p<0.05) compared to the U100, except when EDTA was used. For ARC, no pretreatment and CHX produced higher µTBS than EDTA. For U100, EDTA produced higher µTBS; no statistical difference occurred between CHX pretreatment and when no pretreatment was performed. While CHX did not affect immediate dentin bond strength of both cements, EDTA improved bond strength of U100, but it reduced dentin bond strength of ARC.
Assuntos
Clorexidina/química , Colagem Dentária , Dentina/ultraestrutura , Ácido Edético/química , Inibidores de Metaloproteinases de Matriz , Cimentos de Resina/química , Condicionamento Ácido do Dente/métodos , Bis-Fenol A-Glicidil Metacrilato/química , Resinas Compostas/química , Análise do Estresse Dentário/instrumentação , Humanos , Teste de Materiais , Metacrilatos/química , Microscopia Eletrônica de Varredura , Polietilenoglicóis/química , Ácidos Polimetacrílicos/química , Camada de Esfregaço , Estresse Mecânico , Propriedades de Superfície , Resistência à Tração , Fatores de Tempo , Água/químicaRESUMO
AIM: To investigate ex vivo the influence of gamma irradiation therapy and restorative material on fracture resistance, fracture mode and strain of root filled human premolars. METHODOLOGY: Sixty extracted human maxillary premolar teeth were randomly divided into six groups (n = 10) determined by two study factors: (i) restorative materials: sound teeth, root filled teeth restored with composite resin, root filled teeth restored with amalgam; (ii) gamma irradiation: irradiated (subjected to 60 Gy of gamma irradiation in daily increments of 2 Gy) and nonirradiated. For the strain gauge test, two strain gauges per sample were attached on the buccal and palatal cusp surfaces (n = 5). Strain values were recorded during loading of 0-150 N. Fracture resistance (N) was assessed in a mechanical testing machine (n = 10). Strain gauge for each cusp and fracture resistance data were analysed by two-way anova (3 × 2) followed by the Tukey's honestly significant difference test (α = 0.05). The failure mode was evaluated using an optical stereomicroscope and classified according to the location of the failure. RESULTS: Gamma radiation therapy significantly reduced the fracture resistance of intact teeth. The strain was higher for teeth restored with amalgam than for those restored with composite resin. The teeth restored with composite resin had similar strain values to sound teeth. Nonirradiated teeth had more restorable failures than irradiated teeth. CONCLUSIONS: Gamma irradiation significantly reduced fracture resistance and increased cusp strain. The use of composite resin resulted in better biomechanical behaviour than amalgam for restoring root filled teeth whether or not they were submitted to radiotherapy.
Assuntos
Materiais Dentários/efeitos da radiação , Raios gama/efeitos adversos , Radioterapia/efeitos adversos , Tratamento do Canal Radicular , Fraturas dos Dentes/etiologia , Dente não Vital/complicações , Análise de Variância , Dente Pré-Molar/patologia , Dente Pré-Molar/efeitos da radiação , Fenômenos Biomecânicos , Estudos de Casos e Controles , Resinas Compostas/efeitos da radiação , Amálgama Dentário/efeitos da radiação , Falha de Restauração Dentária , Restauração Dentária Permanente , Análise do Estresse Dentário , Humanos , Maxila , Dosagem Radioterapêutica , Valores de Referência , Estatísticas não Paramétricas , Fraturas dos Dentes/patologiaRESUMO
AIM: To investigate ex vivo the influence of post system and amount of remaining coronal tooth tissue on the fracture resistance, fracture mode and strain of root filled molar teeth. METHODOLOGY: Seventy mandibular human molar teeth were divided into seven groups (n = 10), one control (sound teeth) and six experimental groups resulting from the interaction between the two study factors: post system (Pa, post absence; Gfp, glass fibre post; Cmp, cast Ni-Cr alloy post and core) and amount of remaining coronal tooth tissue (Fe, 2 mm of ferrule; NFe, no ferrule). Teeth in the experimental groups were restored with metal crowns. For the strain gauge test, two strain gauges per sample were attached on the buccal and proximal root surfaces, and the samples of each group (n = 5) were submitted to a load of 0-100N. Fracture resistance (N) was assessed in a mechanical testing device (n = 10). Strain gauge and fracture resistance data were analysed by two-way anova (3 × 2) followed by the Tukey's HSD and Duncan's test (α = 0.05). The failure mode was evaluated using an optical stereomicroscope and classified according to the location of the failure. RESULTS: The absence of ferrule was associated with lower fracture resistance regardless of the post system. Groups restored with glass fibre post and cast Ni-Cr alloy post and core had similar fracture resistance and higher values than groups without posts, regardless of the remaining coronal tooth tissue. Teeth with no ferrule and cast Ni-Cr alloy post and core resulted in catastrophic fractures and those with no ferrule and glass fibre post or no ferrule and post absence resulted in restorable failures. Buccal strain was higher in sound teeth and lower in teeth without posts. Glass fibre post insertion decreased the buccal strain compared to the teeth with ferrule and absence of post. CONCLUSIONS: Two millimetre of ferrule had a significant influence on cusp strain, fracture resistance and failure mode. The glass fibre post was as effective as the cast Ni-Cr alloy post and core in the restoration of root filled molars regardless of the remaining tooth tissue. Absence of a post decreased the fracture resistance and increased the cusp strain.