RESUMEN
In 2020, the European Commission published a regulation that states all producers of white paints containing titanium dioxide (TiO2) must provide a warning label on their products. Exposure during the production and application of products containing TiO2 can be harmful, and therefore these products must be labeled as "may cause cancer." The paint industry is a major user of TiO2 pigment. This study focuses on pigment release from three TiO2-based paints and discusses the effect of paint formulation, more precisely the Pigment Volume Concentration (PVC), to predict TiO2 pigment release from the paints during a simulated use phase and at the end of life (EoL). The use phase considered mild abrasion of painted panels that simulated cleaning or touching. The EoL phase was studied using leaching tests simulating landfill disposal. TiO2 release during both activities was evident with a high discrepancy between the three paints. While dry rubbing was similar for all paints, activities involving water present a high release link to paint matrix degradation. The paint pigment volume concentration and the paint permeability determines the TiO2 release during wet rubbing and leaching. This work represents an attempt to identify the paint permeability as a matrix-related parameter to predict TiO2 release and a way to use of this parameter to develop safer products.
RESUMEN
This work investigated the suppression of photocatalytic activity of titanium dioxide (TiO2) pigment powders by extremely thin aluminum oxide (Al2O3) films deposited via an atomic-layer-deposition-type process using trimethylaluminum (TMA) and H2O as precursors. The deposition was performed on multiple grams of TiO2 powder at room temperature and atmospheric pressure in a fluidized bed reactor, resulting in the growth of uniform and conformal Al2O3 films with thickness control at sub-nanometer level. The as-deposited Al2O3 films exhibited excellent photocatalytic suppression ability. Accordingly, an Al2O3 layer with a thickness of 1 nm could efficiently suppress the photocatalytic activities of rutile, anatase, and P25 TiO2 nanoparticles without affecting their bulk optical properties. In addition, the influence of high-temperature annealing on the properties of the Al2O3 layers was investigated, revealing the possibility of achieving porous Al2O3 layers. Our approach demonstrated a fast, efficient, and simple route to coating Al2O3 films on TiO2 pigment powders at the multigram scale, and showed great potential for large-scale production development.