Effect of Staining, Glazing and Polishing on the Survival Probability of Monolithic Zirconia Crowns.
Fiorin, Lívia; Poole, Stephanie Francoi; Oliveira, Paulo Eduardo Barros Souza; Faria, Adriana Claudia Lapria; Ribeiro, Ricardo Faria; Rodrigues, Renata Cristina Silveira.
Afiliação
  • Fiorin L; Department of Dental Materials and Prostheses, School of Dentistry of Ribeirao Preto, University of Sao Paulo (USP), São Paulo, Brazil.
  • Poole SF; Department of Dental Materials and Prostheses, School of Dentistry of Ribeirao Preto, University of Sao Paulo (USP), São Paulo, Brazil.
  • Oliveira PEBS; Department of Dental Materials and Prostheses, School of Dentistry of Ribeirao Preto, University of Sao Paulo (USP), São Paulo, Brazil.
  • Faria ACL; Department of Dental Materials and Prostheses, School of Dentistry of Ribeirao Preto, University of Sao Paulo (USP), São Paulo, Brazil.
  • Ribeiro RF; Department of Dental Materials and Prostheses, School of Dentistry of Ribeirao Preto, University of Sao Paulo (USP), São Paulo, Brazil.
  • Rodrigues RCS; Department of Dental Materials and Prostheses, School of Dentistry of Ribeirao Preto, University of Sao Paulo (USP), São Paulo, Brazil.
J Esthet Restor Dent ; 2024 Sep 03.
Article em En | MEDLINE | ID: mdl-39228147
ABSTRACT

OBJECTIVE:

The purpose of this in vitro study was to evaluate the effect of staining, glazing, and polishing on the survival probability of monolithic crowns manufactured with preshaded stabilized zirconia with 5 mol% of yttrium oxide (5Y-TZP). MATERIALS AND

METHODS:

Monolithic crowns in the shape of an upper canine (1.5 mm of thickness) were manufactured by CAD/CAM, adhesively cemented on metallic foundation, and divided into 6 groups (n = 21) C (control), S (staining), G (glazing), P (polishing), SG (staining and glazing), and SP (staining and polishing). The survival probability was determined by step-stress accelerated life testing with a load applied to the palatine concavity of the crown. First, the specimens were subjected to a single-load to fracture test (SLF) and next to the fatigue test (5 Hz, thermocycling immersed in water varying 5-55°C), including the light (n = 9), moderate (n = 6), and aggressive (n = 3) loading profiles (load ranged between 20% and 60% of SLF). The survival probability was calculated considering the cycles for failure (CFF) and fatigue failure load (FFL) and illustrated using a Kaplan-Meier graph. The comparison among groups was performed using a Log-Rank test (α = 0.05).

RESULTS:

The mean value of SLF was 586.7 N. There was no difference among groups in survival probability, considering CFF and FFL.

CONCLUSION:

Staining, glazing, and polishing can be performed safely without damaging the mechanical behavior of 5Y-TZP monolithic crowns. CLINICAL

SIGNIFICANCE:

Staining is used to characterize and improve the esthetic of zirconia monolithic crowns. It can be used to reproduce the color gradient in the cervical region of the crown and pigmented grooves. This study showed that staining, glazing, and polishing did not affect the survival probability and the use of finishing procedures (glazing or polishing) after staining did not improve the survival probability of zirconia monolithic crowns.
Palavras-chave
Texto completo
Adicionar na Minha BVS
Imprimir
XML
PubMed Links
Buscar no Google

Texto completo: 1 Coleções: 01-internacional Base de dados: MEDLINE Idioma: En Revista: J Esthet Restor Dent Assunto da revista: ODONTOLOGIA Ano de publicação: 2024 Tipo de documento: Article País de afiliação: Brasil País de publicação: Reino Unido
Texto completo
Adicionar na Minha BVS
Imprimir
XML
PubMed Links
Buscar no Google

Texto completo: 1 Coleções: 01-internacional Base de dados: MEDLINE Idioma: En Revista: J Esthet Restor Dent Assunto da revista: ODONTOLOGIA Ano de publicação: 2024 Tipo de documento: Article País de afiliação: Brasil País de publicação: Reino Unido