Evaluation of the ceramic laminate veneer-tooth interface after different resin cement excess removal techniques.
Clin Oral Investig
; 28(2): 136, 2024 Feb 06.
Article
em En
| MEDLINE
| ID: mdl-38319457
ABSTRACT
OBJECTIVES:
To compare, in vitro, resin cement excess removal techniques at the veneer-tooth interface. MATERIALS ANDMETHODS:
Anterior human teeth were restored with ceramic veneers and randomly divided according to the following techniques (n = 10) removal of excess resin cement with brush and dental floss, followed by light-curing with Valo (Group 1) or Elipar (Group 2) for 1 min and 40 s; tack-curing with Valo (Group 3) or Elipar (Group 4) for 1 s; and tack-curing with Valo (Group 5) or Elipar (Group 6) for 5 s. The tack-curing was followed by removal of excess with probe and dental floss and light-curing for 1 min and 40 s. The area of excess resin cement (mm2) was measured in micro-CT images using AutoCAD program. The failures at the cervical margin in the X, Y, and Z axes (µm) of greater value were measured using the DataViewer program. The specimens were submitted to microleakage with 2% basic fuchsin.RESULTS:
According to the Kruskal-Wallis and multiple comparison test, the highest area of excess resin cement was found in Group 1 (5.06 mm2), which did not differ statistically from Groups 2 (3.70 mm2) and 5 (2.19 mm2). Groups 2, 3 (1.73 mm2), 4 (1.14 mm2), and 5 (2.18 mm2) did not differ statistically. Group 6 (0.77 mm2) obtained the lowest value, which did not differ statistically from Groups 3 and 4. According to the Kruskal-Wallis and Dunn test, there was no significant difference in failures in X (p = 0.981), Y (p = 0.860), and Z (p = 0.638) axes and no significant difference in microleakage (p = 0.203) among the groups.CONCLUSIONS:
Tack-curing for 1 s or 5 s, followed by removal of excess resin cement using a probe and a dental floss, tended to result in a lower amount of excess material around the margin. CLINICAL RELEVANCE The technique used for resin cement excess removal influences the amount of excess leaved at the veneer-tooth interface. Tack-curing for 1 s or 5 s is recommended to mitigate the excess resin cement.Palavras-chave
Texto completo:
1
Coleções:
01-internacional
Base de dados:
MEDLINE
Assunto principal:
Cerâmica
/
Cimentos de Resina
Limite:
Humans
Idioma:
En
Revista:
Clin Oral Investig
Assunto da revista:
ODONTOLOGIA
Ano de publicação:
2024
Tipo de documento:
Article
País de afiliação:
Brasil
País de publicação:
Alemanha