Rangel, Elidiane C; de Souza, Eduardo S; de Moraes, Francine S; Duek, Eliana A R; Lucchesi, Carolina; Schreiner, Wido H; Durrant, Steven F; Cruz, Nilson C.
Afiliação
  • Rangel EC; Laboratório de Plasmas Tecnológicos, Universidade Estadual Paulista (UNESP), Avenida Três de Março 511, 18087-180 Sorocaba, SP, Brazil.
  • de Souza ES; Laboratório de Plasmas Tecnológicos, Universidade Estadual Paulista (UNESP), Avenida Três de Março 511, 18087-180 Sorocaba, SP, Brazil.
  • de Moraes FS; Laboratório de Plasmas Tecnológicos, Universidade Estadual Paulista (UNESP), Avenida Três de Março 511, 18087-180 Sorocaba, SP, Brazil.
  • Duek EA; Laboratório de Biomateriais, Departamento de Ciências Fisiológicas, Pontifícia Universidade Católica, Praça Dr. José Ermírio de Moraes 290, 18030-095 Sorocaba, SP, Brazil.
  • Lucchesi C; Laboratório de Biomateriais, Departamento de Ciências Fisiológicas, Pontifícia Universidade Católica, Praça Dr. José Ermírio de Moraes 290, 18030-095 Sorocaba, SP, Brazil.
  • Schreiner WH; Laboratório de Superfícies e Interfaces, Departamento de Física, Universidade Federal do Paraná, 81531-990 Curitiba, PR, Brazil.
  • Durrant SF; Laboratório de Plasmas Tecnológicos, Universidade Estadual Paulista (UNESP), Avenida Três de Março 511, 18087-180 Sorocaba, SP, Brazil.
  • Cruz NC; Laboratório de Plasmas Tecnológicos, Universidade Estadual Paulista (UNESP), Avenida Três de Março 511, 18087-180 Sorocaba, SP, Brazil.
ScientificWorldJournal ; 2014: 132308, 2014.
Article em En | MEDLINE | ID: mdl-25247202
To produce environments suitable for cell culture, thin polymer films were deposited onto commercial PVC plates from radiofrequency acetylene-argon plasmas. The proportion of argon in the plasmas, P(Ar), was varied from 5.3 to 65.8%. The adhesion and growth of Vero cells on the coated surfaces were examined for different incubation times. Cytotoxicity tests were performed using spectroscopic methods. Carbon, O, and N were detected in all the samples using XPS. Roughness remained almost unchanged in the samples prepared with 5.3 and 28.9% but tended to increase for the films deposited with P(Ar) between 28.9 and 55.3%. Surface free energy increased with increasing P(Ar), except for the sample prepared at 28.9% of Ar, which presented the least reactive surface. Cells proliferated on all the samples, including the bare PVC. Independently of the deposition condition there was no evidence of cytotoxicity, indicating the viability of such coatings for designing biocompatible devices.
Assuntos
Texto completo
Adicionar na Minha BVS
Imprimir
XML
PubMed Links
Buscar no Google

Texto completo: 1 Coleções: 01-internacional Base de dados: MEDLINE Assunto principal: Cloreto de Polivinila / Adesão Celular / Materiais Revestidos Biocompatíveis Limite: Animals Idioma: En Revista: ScientificWorldJournal Assunto da revista: MEDICINA Ano de publicação: 2014 Tipo de documento: Article País de afiliação: Brasil País de publicação: Estados Unidos
Texto completo
Adicionar na Minha BVS
Imprimir
XML
PubMed Links
Buscar no Google

Texto completo: 1 Coleções: 01-internacional Base de dados: MEDLINE Assunto principal: Cloreto de Polivinila / Adesão Celular / Materiais Revestidos Biocompatíveis Limite: Animals Idioma: En Revista: ScientificWorldJournal Assunto da revista: MEDICINA Ano de publicação: 2014 Tipo de documento: Article País de afiliação: Brasil País de publicação: Estados Unidos