In vitro microhardness of glass ionomer cements.
Silva, R C; Zuanon, A C C; Esberard, R R; Candido, M S M; Machado, J S.
Afiliação
  • Silva RC; Department of Pediatric Dentistry and Orthodontic, Araraquara Dental School, University of São Paulo State, UNESP, São Paulo, Brazil.
J Mater Sci Mater Med ; 18(1): 139-42, 2007 Jan.
Article em En | MEDLINE | ID: mdl-17200824
This study evaluated the surface microhardness of four glass ionomer cements and a composite resin (Fuji IX, Ketac Molar, Vidrion R, Vitromolar and Z 250). Ten specimens of each glass ionomer cement with 8.0 mm diameter and 5.0 mm high dimensions were made and Vicker's microhardness measurements were taken at 1 day and 1 week after initial setting reaction. The results were analyzed using Student's T test and Tukey test (p < 0.05) and demonstrated that the values of microhardness increased after 1 week, with the exception of Fuji IX. Resin composite Z250 presented the greatest values for microhardness.
Assuntos
Buscar no Google
Adicionar na Minha BVS
Imprimir
XML
PubMed Links

Coleções: 01-internacional Base de dados: MEDLINE Assunto principal: Resinas Compostas / Cimentos de Ionômeros de Vidro Tipo de estudo: Evaluation_studies Idioma: En Revista: J Mater Sci Mater Med Assunto da revista: ENGENHARIA BIOMEDICA Ano de publicação: 2007 Tipo de documento: Article País de afiliação: Brasil País de publicação: Estados Unidos
Buscar no Google
Adicionar na Minha BVS
Imprimir
XML
PubMed Links

Coleções: 01-internacional Base de dados: MEDLINE Assunto principal: Resinas Compostas / Cimentos de Ionômeros de Vidro Tipo de estudo: Evaluation_studies Idioma: En Revista: J Mater Sci Mater Med Assunto da revista: ENGENHARIA BIOMEDICA Ano de publicação: 2007 Tipo de documento: Article País de afiliação: Brasil País de publicação: Estados Unidos