Comparative evaluation of pH and solubility of MTA Fillapex® endodontic sealer
Finger, Meiryelen Silva; Faraoni, Gislaine; Masson, Michel do Carmo; Santos, Rogério Aparecido Minini dos; Cimardi, Ana Claudia Baladelli Silva; Victorino, Fausto Rodrigo.
Afiliação
  • Finger, Meiryelen Silva; University Center of Maringá. Dentistry Course. Maringá. BR
  • Faraoni, Gislaine; University Center of Maringá. Dentistry Course. Maringá. BR
  • Masson, Michel do Carmo; University Center of Maringá. Dentistry Course. Maringá. BR
  • Santos, Rogério Aparecido Minini dos; University Center of Maringá. Dentistry Course. Maringá. BR
  • Cimardi, Ana Claudia Baladelli Silva; University Center of Maringá. Dentistry Course. Maringá. BR
  • Victorino, Fausto Rodrigo; University Center of Maringá. Dentistry Course. Maringá. BR
RSBO (Impr.) ; 11(1): 41-46, Jan.-Mar. 2014. tab
Article em En | LILACS | ID: lil-718004
Biblioteca responsável: BR97.1
ABSTRACT
Introduction and

Objective:

To evaluate pH and solubility of MTA Fillapex® cement. Material and

methods:

Patients were divided into four groups GI (MTA Fillapex®), GII (Sealer 26®), GIII (Sealapex®) and GIV (AH Plus®). Samples of each group with 10 mm in diameter and 2 mm in height were immersed into water at neutral pH and kept at 37ºC. After 3 hours, the first pH measurement was carried out and repeated at 24 hour intervals for seven days. The data were submitted to Anova (p < 0.05). To analyze the solubility, specimens with 20 mm in diameter and 1.5 mm in thickness were weighed after the setting time, and maintained in distilled water at 37ºC for seven days. After this period, the specimens were again weighed. The difference between their weighs represents the mass loss. The data were subjected to Student's t test for paired samples (p < 0.05).

Results:

GI and GIII showed pH increase at the first 24 hours, with a significant reduction compared with the other cements. GIV was the smallest mass loss, followed by GII, GIII and GI.

Conclusion:

MTA Fillapex® has higher solubility than that of resin cements, but its pH remained above 10 for seven days.
Palavras-chave
Texto completo
Adicionar na Minha BVS
Imprimir
XML
Buscar no Google
Texto completo: 1 Coleções: 01-internacional Base de dados: LILACS Idioma: En Revista: RSBO (Impr.) Assunto da revista: ODONTOLOGIA Ano de publicação: 2014 Tipo de documento: Article País de afiliação: Brasil País de publicação: Brasil
Texto completo
Adicionar na Minha BVS
Imprimir
XML
Buscar no Google
Texto completo: 1 Coleções: 01-internacional Base de dados: LILACS Idioma: En Revista: RSBO (Impr.) Assunto da revista: ODONTOLOGIA Ano de publicação: 2014 Tipo de documento: Article País de afiliação: Brasil País de publicação: Brasil