Avaliação da alteração dimensional de moldes dehidrocolóide irreversível submetidos à técnica de reembasamento / Evaluation of accuracy irreversible hydrocolloid impressions submitted to technical rebasing
Rev. flum. odontol
; 17(36): 53-58, jul.-dez. 2011. graf
Article
em Pt
| LILACS, BBO
| ID: lil-638429
Biblioteca responsável:
BR218.1
RESUMO
O objetivo deste trabalho foi avaliar as alterações dimensionais de moldes de alginato quando se emprega a técnica de reembasamento.A partir de um modelo padrão em aço inoxidável, contendo duas marcações, foram realizadas moldagens com AlginatoEzactKromm (Vigodent) e os modelos de gesso foram confeccionados com o gesso tipo IV Durone (Dentsply). As moldagensforam divididas em 2 grupos Grupo I 10 moldagens com alginato sem reembasamento e; Grupo II 10 moldagens com o alginatoutilizando o reembasamento. Os modelos de gesso foram confeccionados com espatulação a vácuo e levados ao Microscópio Comparador Mitutoyo para obtenção das medidas que foram comparadas com o modelo padrão de aço inoxidável. Os dados foram submetidos a análise estatística através do teste t de Student e obtivemos os seguintes resultados:
houve alteração dimensional estatisticamente significante no Grupo II (p<0,05) em comparação com o Grupo I e o modelo padrão. Concluiu-se que não é recomendado a realização da técnica de reembasamento em moldagem com Alginato, devido a alteração dimensional observada.ABSTRACT
The aim of this study was to evaluate the dimensional changes in alginate molds when employing the technique of relining. Froma standard stainless steel, with two appointments were made with alginate impressions EzactKromm (Vigodent) and plaster casts were made of gypsum type IV Durone (Dentsplay). The casts were divided into two groups Group I 10 impressions without relining and Group II 10 inpressions with alginate using the relining. The plaster casts were made with vacuum mixing and taken to the Comparator Mitutoyo Microscope to obtain measures that were compared with the standard model of stainless steel. The data were statistically analyzed by t test of Student and obtained the following results:
there was a statistically significant dimensional changes in Group II (p <0.05) compared with Group I and the standard model. It was concluded that it is not recommended to perform the technique of relining impression with alginate in, because the dimensional changes observed.
Buscar no Google
Coleções:
01-internacional
Base de dados:
BBO
/
LILACS
Assunto principal:
Materiais para Moldagem Odontológica
/
Odontologia
Idioma:
Pt
Revista:
Rev. flum. odontol
Ano de publicação:
2011
Tipo de documento:
Article
País de afiliação:
Brasil