O efeito de diferentes níveis de PH em soluções de flúor a 1, 1% na corrosão de arcos NITI / The effect of different PH levels on fluoride solutions at 1. 1% on corrosion of NITI archs
Rev. odontol. Univ. Cid. São Paulo (Online)
; 29(3): [237-242], set-dez. 2017. figuras
Article
em Pt
| LILACS, BBO
| ID: biblio-908721
Biblioteca responsável:
BR1853.9
RESUMO
Objetivo:
Determinar o pH crítico para ocorrer a corrosão de arcos NiTi em soluções de flúor a 1,1%, variando o pH de 3,5 a 7,0.Materiais e Métodos:
Doze amostras com 10mm de comprimento de fio superelástico NiTi 0017 x 0025 (Abzil), obtidas do segmento distal dos arcos. As amostras foram aleatoriamente separadas e imersas dentro de recipientes contendo 40ml de seis soluções (água, soluções fluoretadas com pH 3,5; 4,0; 4,5; 5,0; 5,5; 6,0; 6,5 e 7,0), sob uma mesa agitadora durante 90 minutos. Todas as amostras foram, então, levadas ao MEV. As imagens das amostras imersas em água e soluções fluoretadas com pH 7,0, 6,5 e 6,0 não se apresentaram diferentes, no entanto a partir da solução fluoretada com pH 5,5, as imagens superficiais apresentaram características diferentes dos grupos anteriores.Conclusão:
Com base nos resultados obtidos neste estudo, o pH crítico para corrosão de arcos NiTi em soluções de flúor a 1,1% parece estar entre 6,0 e 5,5ABSTRACT
Objective:
To determine the critical pH to occur corrosion of NiTi arches in 1.1% fluoride solutions by varying the pH between 3.5 and 7.0. Materials andMethods:
Twelve samples of 10 mm length superelastic NiTi wire 0017 x 0025 (Abzil) obtained in the distal segment of the arcs. The samples were randomly separated and immersed in 40 ml of six solutions (water, fluoride solutions with pH 3.5; 4.0; 4.5; 5.0; 5.5; 6.0; 6.5 and 7.0) under a shaker table for 90 minutes. All samples were observed under SEM. The images of the samples immersed in water and fluoride solutions at pH 7.0, 6.5 and 6.0 did not show differences, however from the fluoride solution at pH 5.5, the surface characteristics of images presented differences from above groups.Conclusion:
Based on the results obtained in this study the critical pH for corrosion of NiTi arches in fluoride solutions to 1.1% appears to be between 6.0 and 5.5Palavras-chave
Texto completo:
1
Coleções:
01-internacional
Base de dados:
BBO
/
LILACS
Assunto principal:
Corrosão
/
Flúor
Tipo de estudo:
Clinical_trials
Idioma:
Pt
Revista:
Rev. odontol. Univ. Cid. São Paulo (Online)
Assunto da revista:
ODONTOLOGIA
Ano de publicação:
2017
Tipo de documento:
Article
País de afiliação:
Brasil
País de publicação:
Brasil