Análise química laboratorial da superfície de implantes após contato com pinça de titânio através do EDS estudo-piloto / Chemical analysis (EDS) of dental implant surface after contact with titanium tweezers a pilot study
ImplantNewsPerio
; 2(6): 1050-1059, nov.-dez. 2017. ilus, tab
Article
em Pt
| LILACS, BBO
| ID: biblio-880834
Biblioteca responsável:
BR510.1
RESUMO
Objetivo:
analisar a composição química da superfície de três implantes antes e depois de manter contato com pinça de titânio, e verificar se níveis importantes de elementos químicos contaminantes foram adsorvidos aos implantes. Material emétodos:
através de MEV (microscópio eletrônico de varredura) e EDS (espectrometria de energia dispersiva), as superfícies dos implantes foram caracterizadas quimicamente antes e após o contato com pinça de titânio utilizada rotineiramente em uma clínica odontológica.Resultados:
houve presença de titânio com 99,51% de média nas superfícies antes do contato com pinça de titânio, e 99,43% de média de titânio após o contato com pinça de titânio. Elementos como ferro, silício, cloro e alumínio foram encontrados em concentrações menores do que 0,55%, tanto antes quanto depois da manipulação com a pinça.Conclusão:
não houve contaminação química detectável pela metodologia empregada neste estudo da superfície dos implantes após o contato com a pinça de titânio, porém, uma amostra mais significativa e o emprego de critérios que possam definir com mais precisão as áreas de análise parecem ser necessários para resultados ainda mais consistentes.ABSTRACT
Objective:
to analyze the chemical composition surface of three implants before and after titanium tweezers contact and check whether important levels of contaminants chemical elements were adsorbed to the implants. Material andmethods:
through SEM (scanning electron microscope) and EDS (energy dispersive spectroscopy) the implants surfaces were characterized chemically before and after contact with titanium tweezers frequently used in dental clinic.Results:
the surfaces before contact with the titanium tweezers showed the presence of titanium 99.51% average and 99.43% average of titanium after contact with the titanium clamp. Elements such as iron, silicon, chlorine and aluminum have been found in lower concentrations than 0.55%, both before and after handling with forceps.Conclusion:
therefore, no chemical contamination was detected by the method used in this study of the implant surface after contact with titanium tweezers, however, a more signifi cant sample and the use of criteria that can defi ne more precisely the areas of analysis, appear to be required for further consistent results.Palavras-chave
Buscar no Google
Coleções:
01-internacional
Base de dados:
BBO
/
LILACS
Assunto principal:
Titânio
/
Técnicas de Química Analítica
/
Implantação Dentária
/
Poluição Ambiental
/
Fenômenos Químicos
Tipo de estudo:
Evaluation_studies
Aspecto:
Determinantes_sociais_saude
Limite:
Female
/
Humans
/
Male
Idioma:
Pt
Revista:
ImplantNewsPerio
Assunto da revista:
Odontologia
Ano de publicação:
2017
Tipo de documento:
Article
País de afiliação:
Brasil
País de publicação:
Brasil