Resistência à união da liga de Ni-Cr a materiais utilizados para revestimento estético / Shear bond strength of esthetic materials associated to Ni-Cr alloy
Araraquara; s.n; 2000. 208 p. tab, ilus.
Thesis
em Pt
| BBO
| ID: biblio-864010
Biblioteca responsável:
BR39.2
Localização: BR39.2; A449r
RESUMO
O objetivo deste estudo foi avaliar a resistência da união de quatro materiais utilizados como revestimento estético de próteses fixas à uma liga de Ni-Cr. Para tanto, foram construidas 68 estruturas metálicas circulares e divididas em quatro grupos para cada material a ser testado porcelana feldspática convencional (Noritake EX-3) e três resinas compostas laboratoriais (sistema Artglass, Solidex e Targis) com seus respectivos agentes de união (Siloc Pre e Siloc Bond, Metal Photo Primer e Targis Link), que foram aplicados de acordo com as instruções dos fabricantes. Em seguida, os corpos-de-prova foram armazenados em água destilada a 37º C por 7 dias e, após, submetidos aos ensaios mecânicos de cisalhamento em máquina de ensaios universal com velocidade de 0,5 mm/min. Os tipos de falhas foram também avaliados macro e microscopicamente. Os resultados obtidos foram analisados estatisticamente, permitindo as seguintes conclusões:
(1) a resistência da união metal-porcelana, utilizada como parâmetro de qualidade, foi superior em relação à das resinas estudadas; (2) os sistemas Solidex e Targis apresentaram resistências de união resina-metal semelhantes entre si e superiores a do sistema Artglass; (3) para os sistemas Targis e Noritake EX-3, as falhas foram predominantemente mistas, enquanto para os sistemas Solidex e Artglas as falhas foram predominantemente adesivasABSTRACT
The purpose of this study was to evaluate the shear bond strength of four materials used as esthetic material associated to Ni-Cr alloy. Sixth eight alloy discs were prepared and divided equally into four groups and received four treatments for bonding systems conventional feldspatic porcelain (Noritake EX-3) and three adhesive bonding promoter (Siloc Pre and Siloc Bond - Artglass, Metal Photo Primer- Solidex and Targis Link - Targis) of a light-cured prosthodontic composite resin to metal. The esthetic materials were applied after metal structure conditioning in accordance with the manufacturers' recommendations. Specimens were stored in distilled water at 37º C for 7 days. An universal testing machine was used to measure the shear bond strength of the specimens at a cross head speed of 0.5 mm/min. Fractured specimens were examined by using both optical and scanning electron microscope. The results were statistically analyze and it was concluded that (1) the porcelain fused-to-metal bonding method showed significantly higher shear bond strength than the metal-resin bonding techniques; (2) the system Solidex was equivalent to system Targis in bond strength and exhibited greater strength than the system Artglass; (3) optical analysis of the fracture surfaces indicated that for Targis and Noritake EX-3 all failures were a mixture of both cohesive and adhesive patterns. Artglass and Solidex the fractures were mainly adhesive in nature
Palavras-chave
Buscar no Google
Coleções:
06-national
Base de dados:
BBO
Assunto principal:
Ligas de Cromo
/
Resinas Compostas
/
Resistência ao Cisalhamento
/
Facetas Dentárias
/
Prótese Parcial Fixa
Tipo de estudo:
Risk_factors_studies
Idioma:
Pt
Ano de publicação:
2000
Tipo de documento:
Thesis
País de publicação:
Brasil