Avaliação do efeito da água de piscina sobre a rugosidade superficial de resinas compostas de esmalte / Evaluation of the pool water effect on the surface roughness of enamel composite resins
Rev. Ciênc. Méd. Biol. (Impr.)
; 16(3): 312-317, dez 19, 2017. tab, ilus
Article
em Pt
| LILACS
| ID: biblio-1293099
Biblioteca responsável:
BR342.1
RESUMO
Introdução:
a estabilidade de cor e a durabilidade de uma restauração em resina composta são influenciadas por sua lisura superficial. Características inerentes ao material, procedimentos de acabamento e polimento, dieta e hábitos dos indivíduos podem interferir nas suas propriedades superficiais.Objetivo:
avaliar a rugosidade superficial de resinas compostas de esmalte submetidas ao contato com água de piscina clorada e estimar se o uso de uma proteção mecânica limitaria esse contato e seus efeitos.Metodologia:
duzentos corpos de prova, de cinco diferentes resinas foram preparados e distribuídos, aleatoriamente, em quatro grupos (n=10), de acordo com o desafio a que foram submetidos imersão em água destilada sem e com proteção de moldeira de acetato; imersão em água clorada sem e com proteção de moldeira de acetato. Os corpos ficaram imersos por 30 dias, sendo as respectivas águas trocadas diariamente. Para avaliação da rugosidade superficial, utilizou-se um rugosímetro. Procedeu-se à análise estatística inferencial por meio da análise de variância a 3-critérios, avaliando-se a comparação múltipla dessas médias com auxílio do teste de Tukey (nível de significância de 5%).Resultados:
observou-se interação significativa entre os fatores água e condição experimental (p<0,0001) e maior rugosidade superficial para a resina Esthet-X HD, quando exposta à água clorada. O uso da moldeira resultou em maiores valores de rugosidade superficial para todas as resinas testadas quando expostas à água clorada.Conclusão:
o efeito da água de piscina foi material dependente. O uso da proteção mecânica pareceu aumentar a rugosidade superficial das resinas compostas expostas à água clorada.ABSTRACT
Introduction:
the color stability and durability of a composite resin restoration are influenced by its surface smoothness. Characteristics inherent to the material, finishing and polishing procedures, diet and habits of individuals may interfere with their surface properties.Objective:
to evaluate the surface roughness of enamel composite resins submitted to contact with chlorinated pool water and to estimate if the use of a mechanical protection would limit this contact and its effects.Methodology:
two hundred specimens of five different resins were prepared and randomly distributed into four groups (n = 10), according to the challenge they were subjected to immersion in distilled water, without and with acetate tray protection; immersion in chlorinated water, without and with acetate tray protection. The bodies were immersed for 30 days, and their waters were changed daily. To evaluate the surface roughness, a rugosimeter was used. Inferential statistical analysis was performed using 3-criteria analysis of variance, and a multiple comparison of these means was evaluated using Tukey's test (significance level of 5%).Results:
it was observed a significant interaction between water and experimental conditions (p <0.0001) and greater surface roughness for Esthet-X HD resin when exposed to chlorinated water. The use of the tray resulted in higher surface roughness values for all the resins tested when exposed to chlorinated water.Conclusion:
the effect of pool water was dependent material. The use of mechanical protection appeared to increase the surface roughness of composite resins exposed to chlorinated water.Palavras-chave
Texto completo:
1
Coleções:
01-internacional
Base de dados:
LILACS
Assunto principal:
Resinas Compostas
Tipo de estudo:
Clinical_trials
Idioma:
Pt
Revista:
Rev. Ciênc. Méd. Biol. (Impr.)
Assunto da revista:
BIOLOGIA
/
MEDICINA
Ano de publicação:
2017
Tipo de documento:
Article
País de afiliação:
Brasil
País de publicação:
Brasil