The Substantiation of the Pre-Polymerization Heating Efficiency of the Dental Nanocomposite Material
Khabadze, Zurab; Kulikova, Alena; Abdulkerimova, Saida; Bakaev, Yusup; Bakaev, Yunus; Todua, David; Mordanov, Oleg; Adzhieva, Anzhela; Davreshyan, Georgy; Solimanov, Shamil; Nazhmudinov, Shamil.
Afiliação
  • Khabadze, Zurab; Peoples Friendship University of Russia. Medical Institute. Moscow. RU
  • Kulikova, Alena; Peoples Friendship University of Russia. Medical Institute. Moscow. RU
  • Abdulkerimova, Saida; Peoples Friendship University of Russia. Medical Institute. Moscow. RU
  • Bakaev, Yusup; Peoples Friendship University of Russia. Medical Institute. Moscow. RU
  • Bakaev, Yunus; Peoples Friendship University of Russia. Medical Institute. Moscow. RU
  • Todua, David; Peoples Friendship University of Russia. Medical Institute. Moscow. RU
  • Mordanov, Oleg; Peoples Friendship University of Russia. Medical Institute. Moscow. RU
  • Adzhieva, Anzhela; Peoples Friendship University of Russia. Medical Institute. Moscow. RU
  • Davreshyan, Georgy; Peoples Friendship University of Russia. Medical Institute. Moscow. RU
  • Solimanov, Shamil; Peoples Friendship University of Russia. Medical Institute. Moscow. RU
  • Nazhmudinov, Shamil; Peoples Friendship University of Russia. Medical Institute. Moscow. RU
Article em En | BBO, LILACS | ID: biblio-1135517
Biblioteca responsável: BR1264.1
ABSTRACT
Abstract

Objective:

To evaluate the effect of pre-polymerization heating of nanocomposite filling materials on their strength properties within one manufacture group. Material and

Methods:

Two nanocomposite filling materials Enamel Plus HRi Universal Dentin® and Universal Enamel® were used. The linear thermal expansion coefficient (LTEC), Young's modulus and penetration depth were determined during the tests. Changes in the structure of materials were evaluated using electron scanning microscopy.

Results:

Dentin nanocomposite samples after pre-heating and polymerization have higher LTEC after 30°C compared to dentine nanocomposite untreated samples with statistically significance started at 62°C (p<0.05) and higher temperature. Pre-polymerization heated samples had a statistically higher LTEC (p<0.05) at 57°С. It was revealed that Young's modulus of the dentin nanocomposite samples after thermal processing at 55°C was higher in total after the first heating cycle by 15% compared to the untreated dentin nanocomposite samples (p<0.05). The volume of total porosity after pre-heating decreased to 5-7% (p<0.05).

Conclusion:

The material that has undergone preliminary heat processing is significantly less deformed under load than the material that does not have thermal processing during the research was established and also has a denser structure.
Assuntos
Palavras-chave

Texto completo: 1 Coleções: 01-internacional Base de dados: BBO / LILACS Assunto principal: Teste de Materiais / Resinas Compostas / Materiais Dentários / Nanocompostos Tipo de estudo: Evaluation_studies País/Região como assunto: Asia / Europa Idioma: En Revista: Pesqui. bras. odontopediatria clín. integr Assunto da revista: ODONTOLOGIA Ano de publicação: 2020 Tipo de documento: Article País de afiliação: Federação Russa País de publicação: Brasil

Texto completo: 1 Coleções: 01-internacional Base de dados: BBO / LILACS Assunto principal: Teste de Materiais / Resinas Compostas / Materiais Dentários / Nanocompostos Tipo de estudo: Evaluation_studies País/Região como assunto: Asia / Europa Idioma: En Revista: Pesqui. bras. odontopediatria clín. integr Assunto da revista: ODONTOLOGIA Ano de publicação: 2020 Tipo de documento: Article País de afiliação: Federação Russa País de publicação: Brasil