Li4Ti5O12@carbon nanotube arrays as high-performance anode for Li-ion batteries.
Zhu, Bin; Pu, Yi; Tang, Wu; Tang, Hui.
Afiliación
  • Zhu B; School of Materials and Energy, University of Electronic Science and Technology of China Chengdu 611731 P. R. China tang@uestc.edu.cn tanghui@uestc.edu.cn.
  • Pu Y; School of Materials and Energy, University of Electronic Science and Technology of China Chengdu 611731 P. R. China tang@uestc.edu.cn tanghui@uestc.edu.cn.
  • Tang W; School of Materials and Energy, University of Electronic Science and Technology of China Chengdu 611731 P. R. China tang@uestc.edu.cn tanghui@uestc.edu.cn.
  • Tang H; School of Materials and Energy, University of Electronic Science and Technology of China Chengdu 611731 P. R. China tang@uestc.edu.cn tanghui@uestc.edu.cn.
RSC Adv ; 14(39): 28779-28782, 2024 Sep 04.
Article en En | MEDLINE | ID: mdl-39257654
ABSTRACT
The innovation of advanced high-rate anodes is of great significance for the development of high-power and fast-charging lithium-ion batteries (LIBs). In this work, self-supported Li4Ti5O12@carbon (LTO@C) nanotube arrays as a high-quality anode are fabricated via anodizing and hydrothermal processes. Owing to the structure having a high contact surface area and good stability, as well as the incorporation of carbon, the LTO@C exhibits a remarkable rate capability (a reversible capability of 290 mA h g-1, 251.9 mA h g-1, 228.8 mA h g-1, and 208.7 mA h g-1 at 1C, 5C, 10C, and 20C, respectively) and cycling performance (71.7% capacity retention after 1000 cycles at 10C), which is superior to LTO. These features suggest the promising application of LTO@C in high-power energy storage areas.
Texto completo
Añadir a Mi BVS
Imprimir
XML
PubMed Links
Buscar en Google

Texto completo: 1 Colección: 01-internacional Base de datos: MEDLINE Idioma: En Revista: RSC Adv Año: 2024 Tipo del documento: Article Pais de publicación: Reino Unido
Texto completo
Añadir a Mi BVS
Imprimir
XML
PubMed Links
Buscar en Google

Texto completo: 1 Colección: 01-internacional Base de datos: MEDLINE Idioma: En Revista: RSC Adv Año: 2024 Tipo del documento: Article Pais de publicación: Reino Unido