Quantitative examination of factors influencing the colour reproduction ability of lithium disilicate glass-ceramics.
BMC Oral Health
; 24(1): 660, 2024 Jun 05.
Article
en En
| MEDLINE
| ID: mdl-38840111
ABSTRACT
BACKGROUND:
Effects of ceramic translucency, layer thickness, and substrate colour on the shade of lithium disilicate glass-ceramic restorations proved to be significant in several studies, however, quantitative, numerical results on the relationship between the colour difference and these parameters are still lacking. The purpose of this in vitro study was to quantitatively determine how the colour reproduction ability of a lithium disilicate glass-ceramic is affected by its translucency, layer thickness, and substrate colour.METHODS:
Ceramic samples were prepared from A2 shade IPS e.max CAD blocks with high and low translucencies (HT and LT) in a thickness range of 0.5-2.5 mm (+/- 0.05 mm). Layered samples were acquired utilizing composite substrates in 9 shades; transparent try-in paste was used. The spectral reflectance of the specimens was assessed under D65 standard illumination with a Konica Minolta CM-3720d spectrophotometer. The CIEDE2000 colour difference (ΔE00) between two samples was analysed using perceptibility and acceptability thresholds set at 5050%. Statistical analysis involved linear regression analysis and the Kruskal-Wallis test.RESULTS:
An increase in the thickness of 0.5 mm reduced the ΔE00 of the HT samples to 72.8%, and that of the T samples to 71.1% (p < 0.0001). 7 substrates with HT and LT specimens had significantly different results from the mean (p < 0.05). A thickness of 0.5 mm is not sufficient to achieve an acceptable result at any level of translucency, while the low translucency ceramic at a thickness of 1.5 mm gave acceptable results, except for severely discoloured substrates (ND8 and ND9).CONCLUSIONS:
The colour reproduction ability of lithium disilicate glass-ceramics is significantly affected by their translucency, layer thickness, and 7 substrates out of 9 substrates examined.Palabras clave
Texto completo:
1
Colección:
01-internacional
Base de datos:
MEDLINE
Asunto principal:
Cerámica
/
Color
/
Porcelana Dental
Límite:
Humans
Idioma:
En
Revista:
BMC Oral Health
Asunto de la revista:
ODONTOLOGIA
Año:
2024
Tipo del documento:
Article
País de afiliación:
Hungria
Pais de publicación:
Reino Unido