Application of Three-Dimension Printing Nano-Carbonated-Hydroxylapatite to the Repair of Defects in Rabbit Bone.
Wang, Shujie; Shao, Chunyan; Zhao, Xingkai; Guo, Yizhe; Song, Houhui; Shen, Lida; Zhou, Zhenlei; Li, Zhen.
Afiliación
  • Wang S; College of Veterinary Medicine, Nanjing Agricultural University, Nanjing, Jiangsu, 210095, People's Republic of China.
  • Shao C; College of Animal Science and Technology & College of Veterinary Medicine, Zhejiang Agriculture and Forestry University, Hangzhou, Zhejiang, 311300, People's Republic of China.
  • Zhao X; College of Animal Science and Technology & College of Veterinary Medicine, Zhejiang Agriculture and Forestry University, Hangzhou, Zhejiang, 311300, People's Republic of China.
  • Guo Y; College of Veterinary Medicine, Nanjing Agricultural University, Nanjing, Jiangsu, 210095, People's Republic of China.
  • Song H; College of Veterinary Medicine, Nanjing Agricultural University, Nanjing, Jiangsu, 210095, People's Republic of China.
  • Shen L; College of Animal Science and Technology & College of Veterinary Medicine, Zhejiang Agriculture and Forestry University, Hangzhou, Zhejiang, 311300, People's Republic of China.
  • Zhou Z; College of Mechanical and Electrical Engineering, Nanjing University of Aeronautics and Astronautics, Nanjing, Jiangsu, 210016, People's Republic of China.
  • Li Z; College of Veterinary Medicine, Nanjing Agricultural University, Nanjing, Jiangsu, 210095, People's Republic of China.
Int J Nanomedicine ; 19: 1667-1681, 2024.
Article en En | MEDLINE | ID: mdl-38406604
ABSTRACT

Introduction:

Hydroxylapatite (HAp) is a biodegradable bone graft material with high biocompatibility. However, the clinical application of HAp has been limited due to the poor absorption rate in vivo.

Methods:

In this study, carbonated hydroxylapatite (CHAp) with a chemical composition similar to natural bone was synthesized. HAp and CHAp scaffolds were fabricated by 3D printing. Each material was designed by two types of scaffold model with a maximum width of 8 mm and a thickness of 2 mm, ie, structure I (round shape) and structure II (grid shape). Then, the HAp scaffolds were loaded with lutein. These scaffolds were implanted into the 8 mm bone defect on the top of the rabbit skull within 3 hours in the morning. The curative effects of the scaffolds were assessed two months after implantation.

Results:

The 3D printed scaffolds did not cause severe inflammation or rejection after implantation. It showed that the porous structures allow bone cells to enter into the scaffolds. Furthermore, CHAp scaffolds were more biocompatible than HAp scaffolds, and showed a higher level of degradation and new bone formation after implantation. Structure II scaffolds with a smaller mineral content degraded faster than structure I, while structure I had better osteoconductive properties than structure II. Besides, the addition of lutein significantly enhanced the rate of new bone formation.

Discussion:

The uniqueness of this study lies in the synthesis of 3D printed CHAp scaffolds and the implantation of CHAp in rabbit bone defects. The incorporation of suitable carbonate and lutein into HAp can enhance the osteoinductivity of the graft, and CHAp has a faster degradation rate in vivo, all of which provide a new reference for the research and application of apatite-based composites.
Asunto(s)
Palabras clave
Texto completo
Añadir a Mi BVS
Imprimir
XML
PubMed Links
Buscar en Google

Texto completo: 1 Colección: 01-internacional Base de datos: MEDLINE Asunto principal: Materiales Biocompatibles / Durapatita Límite: Animals Idioma: En Revista: Int J Nanomedicine Año: 2024 Tipo del documento: Article Pais de publicación: Nueva Zelanda
Texto completo
Añadir a Mi BVS
Imprimir
XML
PubMed Links
Buscar en Google

Texto completo: 1 Colección: 01-internacional Base de datos: MEDLINE Asunto principal: Materiales Biocompatibles / Durapatita Límite: Animals Idioma: En Revista: Int J Nanomedicine Año: 2024 Tipo del documento: Article Pais de publicación: Nueva Zelanda