Comparative evaluation of frictional characteristics between nano coated and non coated orthodontic brackets and arch wire configuration-An experimental in vitro study.
J Orthod Sci
; 12: 59, 2023.
Article
en En
| MEDLINE
| ID: mdl-37881666
OBJECTIVE: To compare and assess the coefficient of frictional resistance between nano-coated orthodontic brackets and orthodontic archwires with conventional orthodontic brackets and archwires. METHODOLOGY: In this experimental study, 128 samples were divided into 4 groups consisting of 32 orthodontic wires and brackets in each group. The samples were randomly allocated into GROUP A- ZNO nanoparticle coated archwires and brackets, GROUP B ZNO nanoparticle coated bracket and conventional archwire, GROUP C-ZNO nanoparticle coated archwire and conventional bracket, and GROUP D- conventional archwire and bracket after positioning them on special jigs frictional resistance was studied and evaluated. Bon - Ferroni test was used for inter group comparison and one way ANOVA was used for intr-group comparison. RESULTS: The lowest mean frictional resistance is seen with Group A (nanocoated archwire with nanocoated bracket) N = 0.3401 ± 0.420; and highest with Group D (conventional brackets with conventional archwires) N = 0.8413 ± 0.60. a significant difference in mean frictional resistance was observed between the groups (P ≤ 0.01). The frictional resistance for the groups was in the following order from lowest to highest: group A < B < C < D. CONCLUSION: The study showed decreased friction in ZNO nanoparticle coated archwires and brackets than conventional archwires and brackets.
Texto completo:
1
Colección:
01-internacional
Base de datos:
MEDLINE
Idioma:
En
Revista:
J Orthod Sci
Año:
2023
Tipo del documento:
Article
País de afiliación:
India
Pais de publicación:
India