Corrosion Behavior of Nitrogen-Containing Low-Nickel Weld Cladding in KCl-MgCl<sub>2</sub> Eutectic Molten Salt at 900 °C.

Yang, Taisen; Su, Yunhai; Dai, Zhiyong; Wang, Yingdi; Liang, Xuewei; Wei, Zuyong

Corrosion Behavior of Nitrogen-Containing Low-Nickel Weld Cladding in KCl-MgCl₂ Eutectic Molten Salt at 900 °C.

Yang, Taisen; Su, Yunhai; Dai, Zhiyong; Wang, Yingdi; Liang, Xuewei; Wei, Zuyong.

Afiliación

Yang T; School of Materials Science and Engineering, Shenyang University of Technology, Shenyang 110870, China.
Su Y; School of Materials Science and Engineering, Shenyang University of Technology, Shenyang 110870, China.
Dai Z; School of Materials Science and Engineering, Shenyang University of Technology, Shenyang 110870, China.
Wang Y; School of Materials Science and Engineering, Shenyang University of Technology, Shenyang 110870, China.
Liang X; School of Materials Science and Engineering, Shenyang University of Technology, Shenyang 110870, China.
Wei Z; School of Materials Science and Engineering, Shenyang University of Technology, Shenyang 110870, China.

Materials (Basel) ; 15(24)2022 Dec 10.

Article en En | MEDLINE | ID: mdl-36556636

Palabras clave

chloride molten salt; high-temperature corrosion; nitrogen-containing low-nickel weld cladding

Texto completo

Añadir a Mi BVS

Imprimir

XML

PubMed Links

Buscar en Google

Texto completo: 1 Colección: 01-internacional Base de datos: MEDLINE Idioma: En Revista: Materials (Basel) Año: 2022 Tipo del documento: Article País de afiliación: China Pais de publicación: Suiza

Texto completo

Añadir a Mi BVS

Imprimir

XML

PubMed Links

Buscar en Google