Fabrication and Physical Properties of Single-Crystalline Βeta-FeSi2 Nanowires.
Nanoscale Res Lett
; 15(1): 197, 2020 Oct 14.
Article
en En
| MEDLINE
| ID: mdl-33052458
In this study, self-catalyzed ß-FeSi2 nanowires, having been wanted but seldom achieved in a furnace, were synthesized via chemical vapor deposition method where the fabrication of ß-FeSi2 nanowires occurred on Si (100) substrates through the decomposition of the single-source precursor of anhydrous FeCl3 powders at 750-950 °C. We carefully varied temperatures, duration time, and the flow rates of carrier gases to control and investigate the growth of the nanowires. The morphology of the ß-FeSi2 nanowires was observed with scanning electron microscopy (SEM), while the structure of them was analyzed with X-ray diffraction (XRD) and transmission electron microscopy (TEM). The growth mechanism has been proposed and the physical properties of the iron disilicide nanowires were measured as well. In terms of the magnetization of ß-FeSi2, nanowires were found to be different from bulk and thin film; additionally, longer ß-FeSi2 nanowires possessed better magnetic properties, showing the room-temperature ferromagnetic behavior. Field emission measurements demonstrate that ß-FeSi2 nanowires can be applied in field emitters.
Texto completo:
1
Colección:
01-internacional
Base de datos:
MEDLINE
Idioma:
En
Revista:
Nanoscale Res Lett
Año:
2020
Tipo del documento:
Article
País de afiliación:
Taiwán
Pais de publicación:
Estados Unidos