OBJECTIVE: Gel aspiration-ejection (GAE) has recently been developed for the rapid production of dense, anisotropic collagen gel scaffolds with adjustable collagen fibrillar densities. In this study, a GAE system was applied to produce aligned Schwann cells within a type-1 collagen matrix to generate GAE-engineered neural tissues (GAE-EngNT) for potential nerve tissue engineering applications. APPROACH: The stability and mechanical properties of the constructs were investigated along with the viability, morphology and distribution of Schwann cells. Having established the methodology to construct stable robust Schwann cell-loaded engineered neural tissues using GAE (GAE-EngNTs), the potential of these constructs in supporting and guiding neuronal regeneration, was assessed both in vitro and in vivo. MAIN RESULTS: Dynamic mechanical analysis strain and frequency sweeps revealed that the GAE-EngNT produced via cannula gauge number 16 G (∼1.2 mm diameter) exhibited similar linear viscoelastic behaviors to rat sciatic nerves. The viability and alignment of seeded Schwann cells in GAE-EngNT were maintained over time post GAE, supporting and guiding neuronal growth in vitro with an optimal cell density of 2.0 × 106 cells ml-1. An in vivo test of the GAE-EngNTs implanted within silicone conduits to bridge a 10 mm gap in rat sciatic nerves for 4 weeks revealed that the constructs significantly promoted axonal regeneration and vascularization across the gap, as compared with the empty conduits although less effective regeneration compared with the autograft groups. SIGNIFICANCE: Therefore, this is a promising approach for generating anisotropic and robust engineered tissue which can be used with Schwann cells for peripheral nerve repair.