For developing acid-/oxidative-resistant aliphatic-polymer-based cation-exchange membrane (CEM), macromolecular modification of poly(vinylidene fluoride-co-hexafluoropropylene) (PVDF-co-HFP) was carried out by controlled chemical grafting of 2-acrylamido-2-methyl-1-propanesulfonic acid (AMPS). To introduce the unsaturation suitable for chemical grafting, dehydrofluorination of commercially available PVDF-co-HFP was achieved under alkaline medium. Sulfonated copolymer (SCP) was prepared by the free radical copolymerization of dehydofluorinated PVDF-co-HFP (DHPVDF-co-HFP) and AMPS in the presence of free radical initiator. Prepared SCP-based CEMs were analyzed for their morphological characteristics, ion-exchange capacity (IEC), water uptake, conductivity, and stabilities (mechanical, chemical, and thermal) in comparison with state-of-art Nafion117 membrane. High bound water content avoids the membrane dehydration, and most optimal (SCP-1.33) membrane exhibited about ∼2.5-fold high bound water content in comparison with that of Nafion117 membrane. Bunsen reaction of iodine-sulfur (I-S) was successfully performed by direct-contact-mode membrane electrolysis in a two-compartment electrolytic cell using different SCP membranes. High current efficiency (83-99%) confirmed absence of any side reaction and 328.05 kJ mol-H2(-1) energy was required for to produce 1 mol of H2 by electrolytic cell with SCP-1.33 membrane. In spite of low conductivity for reported SCP membrane in comparison with that of Nafion117 membrane, SCP-1.33 membrane was assessed as suitable candidate for electrolysis because of its low-cost nature and excellent stabilities in highly acidic environment may be due to partial fluorinated segments in the membrane structure.