The effect of production regime and crucible materials on the thermal properties of sodium phosphate glasses produced from salts.
J Biomed Mater Res B Appl Biomater
; 71(1): 22-9, 2004 Oct 15.
Article
en En
| MEDLINE
| ID: mdl-15368224
Changes in the thermal properties of sodium phosphate glasses during melt production have been investigated using Pt/Au and fused alumina crucibles. Glasses were produced from NaH(2)PO(4) as a starting material, providing an intrinsic Na(2)O:P(2)O(5) ratio of 1:1 and giving an O/P = 3, that is, a metaphosphate. In Pt/Au crucibles, glass transition temperatures rose to a plateau value of 295 degrees C at a rate determined by melt temperature. No contamination of the glass by platinum or gold was detected or indicated in the results. E(a) for the reaction was found to be 66.4 kJ mol(-1). In fused alumina crucibles, glass transition temperatures rose to over 450 degrees C, with these values showing some convergence at higher furnace temperatures. Extensive erosion of the alumina crucibles was observed. The amount of alumina incorporation within the glasses correlated well with the rise in glass transition temperature up to a maximum of 15.5 mol % Al(2)O(3) content. Al(2)O(3) incorporation above this value caused a reduction in the value of the T(g).
Buscar en Google
Colección:
01-internacional
Base de datos:
MEDLINE
Asunto principal:
Fosfatos
/
Vidrio
Idioma:
En
Revista:
J Biomed Mater Res B Appl Biomater
Asunto de la revista:
ENGENHARIA BIOMEDICA
Año:
2004
Tipo del documento:
Article
Pais de publicación:
Estados Unidos