RESUMO
PURPOSE: To evaluate the radiopacity of luting cements submitted to different aging procedures. MATERIALS AND METHODS: Twenty discs (1 × 4 mm) of each of the following cements were prepared: zinc phosphate, RelyX Luting 2, Variolink 2, AllCem, RelyX U200, Multilink, Panavia F2.0, and RelyX ARC. Then, they were randomly divided into two groups (n = 10/group), according to the aging procedure: thermal cycling group and water storage group. Before and after aging procedures, specimens were x-rayed with an aluminum step-wedge (11 steps, 1 mm thick each) and three dental slices (1 mm thick). The radiopacity was evaluated by means of optical density, which was measured using ImageJ software. The values were converted into millimeters of aluminum with a logistic regression calibration curve. The data were analyzed by one-way ANOVA and Tukey post-hoc test (α = 0.05). RESULTS: In the thermal cycling group, RelyX Luting 2, RelyX U200, and Panavia F2.0 showed a statistically significant reduction in radiopacity (p < 0.05). In the water storage group, all cements showed a significant reduction in radiopacity (p < 0.05), and RelyX Luting 2 and Panavia F2.0 performed below the desired ISO 4049 standard. CONCLUSIONS: The radiopacity of luting cements can decrease after aging, especially after 1-year water storage.
Assuntos
Cimentos Dentários/efeitos adversos , Resinas Compostas/efeitos adversos , Resinas Compostas/química , Cimentos Dentários/química , Cimentos de Ionômeros de Vidro/efeitos adversos , Cimentos de Ionômeros de Vidro/química , Humanos , Fenômenos Ópticos , Radiografia Dentária , Cimentos de Resina/efeitos adversos , Cimentos de Resina/químicaRESUMO
O objetivo do estudo foi avaliar a influência da densidade tubular em diferentes profundidades dentinárias na estabilidade de união de dois cimentos de ionômero de vidro (CIV) de alta viscosidade. Vinte terceiros molares foram alocados em 6 grupos experimentais, de acordo com a profundidade da dentina - proximal, oclusal superficial ou oclusal profunda, e os CIVs - Fuji IX (GC Corp.) e Ketac(TM) Molar Easy Mix (3M/ESPE). Inicialmente os dentes foram cortados a fim de se obter fatias de aproximadamente 1 mm de espessura de dentina proximal, oclusal superficial e profunda. Em seguida, foi realizado uma análise topográfica das secções das diferentes superfícies e profundidades em microscopia confocal a laser (100X) para obtenção das médias da densidade tubular em cada profundidade. Cânulas de polietileno foram então posicionadas sobre as secções de dentina pré-tratadas e preenchidas pelos CIVs. Os espécimes foram armazenados em água destilada por 24 h e 12 meses a 37°C, em seguida foram submetidos ao ensaio de microcisalhamento (0,5 mm/min). Após o ensaio, foi realizada a análise do padrão de fratura em estereomicroscópio (400X). Os dados obtidos foram submetidos à Análise de Variância para dados repetidos, seguido do teste de Tukey (?=5%). Verificamos que a densidade dos túbulos dentinários, em diferentes profundidades de molares permanentes, é inversamente proporcional a resistência de união de cimentos de ionômero de vidro de alta viscosidade. Foi ainda observado em todos os grupos que a resistência de união após 24 horas é maior do que em 12 meses, indicando degradação da interface adesiva ao longo do tempo.
The aim of this study was to evaluate the influence of dentin tubule density of different depths in the bond stability of two high viscous glass ionomer cements (GIC). Twenty (third) molars were assigned into 6 experimental groups, according to the depth of dentin - proximal, superficial or deep occlusal occlusal and the GICs - Fuji IX (GC Corp.) and Ketac (TM) Molar Easy Mix (3M / ESPE). Initially, the teeth were cut to obtain slices approximately 1 mm thick for approximal, superficial and deep occlusal surfaces. Then it was performed a topographical analysis of sections of different depths surfaces and laser confocal microscopy (100X) to obtain averages of the tubular density at each depth. Polyethylene cannulae were then positioned on the pre-treated dentin sections and filled with GIC. The specimens were stored in distilled water for 24 h and 12 months at 37°C were then subjected to microshear bonding test (0.5 mm / min). After the test, a fracture analysis pattern was performed in stereomicroscope (400X). The data were submitted to ANOVA for repeated measures followed by the Tukey test (? = 5%). We found that the density of dentinal tubules at different depths of permanent molars, is inversely proportional to the bond strength of high viscosity glass ionomer cements. It was observed in all groups which bond strength after 24 hours is higher than in 12 months, indicating degradation of the interface over time.
Assuntos
Humanos , Masculino , Feminino , Cimentos Dentários/análise , Cimentos Dentários , Cimentos Dentários/efeitos adversos , Cimentos Dentários/metabolismo , Cimentos de Ionômeros de Vidro/análise , Cimentos de Ionômeros de Vidro , Cimentos de Ionômeros de Vidro/efeitos adversos , Cimentos de Ionômeros de Vidro/metabolismo , Cimentos de Ionômeros de Vidro/síntese química , Resistência FísicaRESUMO
Este estudo avaliou a influência da aceleração de presa de cimentos de ionômero de vidro de alta viscosidade (CIVAV) por meio de ultrassom, luz halógena e diodo emissor de luz (LED). Para as análises, os espécimes foram divididos em nove grupos de acordo com o material - CIVAV versão pó-líquido (Fuji Gold Label IX GPGC Corp.), CIVAV versão encapsulado (Equia Fill - GC Corp.) e a aceleração de presa inicial - controle negativo; aplicação de ultrassom por 20s, irradiados com luz halógena por 60s, irradiados com LED por 60s, além de um grupo controle positivo de cimento de ionômero de vidro modificado por resina (CIVMR) versão pó-líquido (Fuji II LC - GC Corp.). Para o teste de resistência flexural (RF) foram preparados 90 espécimes (25x2x2mm) (n=10), após armazenamento em água destilada por 24h a 37°C, os espécimes foram submetidos ao teste de RF de três pontos (1mm/min). Para a análise de rugosidade superficial (RS), 45 espécimes (n=5) previamente preparados para o teste de RF, foram selecionados aleatoriamente em cada grupo. A medida da RS (parâmetros Sa e Ra) do corpo de prova foi dada pela média de 5 leituras realizadas na superfície. Para o teste de resistência de união (RU), 90 molares decíduos (n=10) foram selecionados e cânulas de polietileno foram posicionadas sobre as superfícies planas de dentina pré-tratadas, preenchidas por um dos CIV e aplicado um dos aceleradores de presa de acordo com o grupo experimental. Após armazenamento em água destilada por 24h a 37°C, os espécimes foram submetidos ao teste de microcisalhamento (1,0 mm/min). O padrão de fratura foi analisado em microscópio esteroscópico (400 X). Para avaliar a interação dentina-CIV, foram selecionados 27 caninos decíduos (n=3), foi preparada uma cavidade (4x2x2mm) na superfície vestibular, então a cavidade foi restaurada com um dos
CIV propostos pelo estudo para então ser aplicado um dos aceleradores de presa de acordo com o grupo experimental. Após armazenados por 48h a 37ºC e 100% de umidade relativa, os dentes foram seccionados, resultando em fatias com 1mm de espessura. A fatia obtida foi observada em MEV para avaliar qualitativamente possíveis diferenças estruturais. Os valores dos testes de RF, RS e RU foram submetidos a Análise de Variância e teste de Tukey (?=5%). Como resultados na RF, a reação de presa com ultrassom resultou em maiores valores e semelhantes aos grupos controle negativo, independente da forma de apresentação do CIVAV. Para RS (Ra) o grupo Fuji IX mostrou maiores valores quando houve aplicação de ultrassom. Os demais grupos apresentaram resultados semelhantes. Para o parâmetro Sa houve diferença estatística em relação a apresentação do material e Equia Fill apresentou maiores valores de Sa. Para o teste de RU Fuji IX apresentou melhor desempenho nos grupos que receberam ativação por ultrassom e LED. Equia Fill não foi influenciado por nenhum tipo de fonte externa na RU. Com relação ao padrão de fratura, as fraturas adesivas/mistas apresentaram maior frequência independente do grupo experimental. As imagens de MEV mostram a região de interação do material com a dentina. Concluímos que o uso do ultrassom influenciou positivamente na RF, porém gerou maiores valores de RS (Ra) no grupo Fuji IX. Equia Fill tem maiores valores de RS (Sa). LED e ultrassom influenciaram positivamente o grupo Fuji IX na RU.
This study evaluated the influence of acceleration setting reaction by ultrasound, halogen light and light emitting diode (LED). For the analysis, the specimens were divided into nine groups according to the material - HVGIC powder-liquid version (Fuji Gold Label IX GP- GC Corp.), HVGIC encapsulated version (Equia Fill - GC Corp.) and the acceleration setting reaction original - negative control; ultrasound application for 20 seconds, irradiated with halogen light for 60 seconds, irradiated with LED for 60 seconds, and a positive control group of resin modified glass ionomer cement (RMGIC) powder-liquid version (Fuji II LC - GC Corp.) . For flexural strength test (FS) there were prepared 90 specimens (25x2x2mm) (n=10). After storage in water for 24 hours at 37°C, specimens were subjected to the FS test three points (1min/min). For the surface roughness analysis (SR), 45 specimens (n=5) previously prepared to the FS test were randomly selected from each group, and the average of 5 readings was analysed in Sa and Ra parameters. For the bond strength test (BS) 90 primary molars (n = 10) were selected and polyethylene cannulae were positioned on the flat pretreated dentin surface filled by one of the GICs and apply one of the setting reaction accelerators according to the experimental group. After storage in distilled water for 24 hours at 37°C, specimens were subjected to microshear test (1.0 mm/min). The fracture pattern was analyzed in stereomicroscope (400X). To evaluate the interaction dentin-GIC were selected 27 deciduous canines (n= 3), a cavity (4x2x2mm) was prepared in the buccal surface and then restored with the GIC accordingly to groups. After stored for 48 hours at 37°C and 100% relative humidity, the teeth were sectioned, resulting in slices with 1mm thickness. The slice obtained was observed by scanning electron microscope
(SEM) to assess qualitatively possible structural differences. The values of FS testing, SR and BS were submitted to ANOVA and Tukey's test (? = 5%). As a result the FS, the ultrasound with setting reaction resulted in higher values and similar to the negative control group, regardless of the format of the HVGIC. SR for Ra parameter Fuji IX group showed higher values when there was application of ultrasound. The other groups showed similar results. For Sa parameter was no statistical difference regarding the presentation of material and Equia Fill showed higher Sa. For the BS Fuji IX test performed better in the groups receiving.
Assuntos
Humanos , Masculino , Feminino , Cimentos de Ionômeros de Vidro/efeitos adversos , Dente Decíduo/crescimento & desenvolvimento , Dente Decíduo , Dente Decíduo/metabolismo , Ciência dos Materiais/efeitos adversos , Ciência dos Materiais/estatística & dados numéricos , Ciência dos Materiais/métodos , Ciência dos Materiais/prevenção & controleRESUMO
We evaluated the effect of calcium hydroxide cement (CHC) and glass ionomer cement (GIC) on carious dentin and bacterial infections after partial caries removal and sealing. Sixty permanent teeth with deep lesions underwent partial caries removal, the application of CHC, GIC or wax, i.e. negative control (NC), and were then sealed for 3-4 months. After the partial caries removal and the sealing period, the dentin was clinically assessed (colour and consistency) and analysed by scanning electron microscopy to assess dentin organization and bacterial infections. The effect of the treatment in each group was assessed by the Wilcoxon and χ2 tests, differences among groups by the Kruskal-Wallis test and the correlations between variables by Spearman correlation. No clinical symptoms or radiographic signals of pulpits or pulp necrosis were observed during the study. Dentin darkening was observed after the sealing period in the CHC and NC groups (p < 0.05). However, there was no difference in the colour after treatment among the 3 groups (p > 0.05). Dentin hardening occurred in all groups after treatment (p < 0.05), also with no differences (p > 0.05). Dentin samples showed better organization after the sealing period than after partial caries removal, with total or partial obliteration of dentinal tubules (CHC p < 0.03, GIC p < 0.05, NC p < 0.01) and a reduction of bacterial infections (CHC p < 0.03, GIC p < 0.05, NC p < 0.03). No differences were observed. Correlations between the different criteria, except for colour and bacterial infection, were detected in all cases. Partial caries removal and sealing resulted in dentin hardening, decreased bacterial numbers and dentin reorganization, irrespective of the dentin protection used.
Assuntos
Hidróxido de Cálcio , Cárie Dentária/terapia , Forramento da Cavidade Dentária , Cimentos Dentários/uso terapêutico , Dentina/patologia , Cimentos de Ionômeros de Vidro/uso terapêutico , Minerais , Adolescente , Adulto , Hidróxido de Cálcio/efeitos adversos , Distribuição de Qui-Quadrado , Criança , Cárie Dentária/microbiologia , Cárie Dentária/patologia , Preparo da Cavidade Dentária , Cimentos Dentários/efeitos adversos , Cimentos Dentários/química , Dentina/microbiologia , Dentina/ultraestrutura , Dentina Secundária/crescimento & desenvolvimento , Método Duplo-Cego , Cimentos de Ionômeros de Vidro/efeitos adversos , Humanos , Microscopia Eletrônica de Varredura , Minerais/efeitos adversos , Estudos Prospectivos , Estatísticas não Paramétricas , Descoloração de Dente/induzido quimicamente , Remineralização Dentária , Adulto JovemRESUMO
Objetivo: Avaliar a ação de escovas dentais macias e médias em cimentos de ionômero de vidro, analisando os parâmetros alteração de massa e rugosidade superficial. Método: Foram testados dois cimentos de ionômero de vidro de alta viscosidade (Ketac tm Molar Easymix/3M Espe e Vitro Molar/DFL), um convencional (Bioglass R/Biodinâmica) e uma resina composta microhíbrida (Z100 tm/3M Espe). Vinte corpos-de-prova de cada material foram submetidos à escovação simulada com creme dental diluído em água destilada (1:2), divididos em grupos de 10 para cada tipo de escova. Os valores de massa foram obtidos após pesagens consecutivas e estabilização do peso. A rugosidade superficial (Ra) foi determinada pela média aritmética de cinco leituras nas superfícies dos corpos-de-prova. Após registro dos valores iniciais de massa e rugosidade, os corpos-de-prova foram submetidos a 20.000 ciclos de escovação simulada e os valores finais de massa e rugosidade foram verificados. Os dados foram avaliados estatisticamente pelos testes t de Student e Anova com pós-teste de Tukey (p<0,05). Resultados: A escovação determinou desgaste em todos os materiais, sendo o menor valor verificado na resina composta Z100 tm, seguido pelos cimentos de ionômero de vidro Ketactm Molar Easymix, Vitro Molar e Bioglass R. O cimento de ionômero de vidro de alta viscosidade com menor valor de rugosidade superficial inicial e final foi o Ketac tm Molar Easymix, com valor médio de 0,50 μ m, sendo estatisticamente diferente dos outros cimentos de ionômero de vidro. Conclusão: As escovas dentais macias e médias causaram desgastes semelhantes.
Objective: To evaluate the action of soft- and middle-bristle toothbrushes on glass ionomer cements indicated for atraumatic restorative treatment by analyzing the parameters mass change and surface roughness. Method: One conventional (Bioglass R/Biodinâmica) and two high-viscosity (Ketac tm Molar Easymix/3M ESPE and Vitro Molar/DFL) glass ionomer cements and a microhybrid composite resin (Z100 tm/3M ESPE) were tested. Twenty specimens of each material were subjected to simulated toothbrushing with dentifrice diluted with distilled water (1:2), divided in groups of 10 specimens for each type of toothbrush. The mass values were obtained after consecutive recordings and weigh stabilization. Surface roughness (Ra) was determined by the arithmetic mean of five readings on specimen surface. After recording the initial mass and surface roughness values, the specimens were subjected to 20,000 cycles of simulated toothbrushing, and the final mass and surface roughness values were recorded. Data were analyzed statistically by the Students t-test and ANOVA with Tukeys post-test (p<0.05). Results: Toothbrushing produced wear of all materials; Z100 tm composite resin exhibited the highest value, followed by Ketac tm Molar Easymix, Vitro Molar® and Bioglass R glass ionomer cements. Ketac Molar Easymix was the high-viscosity glass ionomer cement with lower initial and final surface roughness (Ra= 0.50 μm) and differed significantly from the other glass ionomer cements. Conclusion: Soft- and medium-bristle toothbrushes caused similar wear on the materials.
Assuntos
Cimentos de Ionômeros de Vidro/análise , Cimentos de Ionômeros de Vidro/efeitos adversos , Desgaste de Restauração Dentária , Escovação Dentária/métodos , Tratamento Dentário Restaurador sem TraumaRESUMO
O objetivo deste estudo foi avaliar a microinfiltração do cimento de ionômero de vidro convencional Vidrion®R utilizando vários tipos de agentes de proteção superficial. Sessenta dentes decíduos foram obtidos pelo Banco de dentes Humanos do Centro de Pesquisas Odontológicas São Leopoldo Mandic. Todos os dentes foram restaurados com Vidrion®R. Os espécimes foram divididos em grupos controle (imersos em saliva artificial sem nenhum tipo de proteção superficial), Vidrion®V, vaselina líquida, vaselina sólida, esmalte para unhas e Vidrion®V após os espécimes serem imersos por 1 minuto em saliva. As amostras foram imersas em saliva artificial por 7 dias e então imersos em corante azul de metileno a 0,5 % por 4 horas e então seccionados longitudinalmente e avaliados. Os resultados mostraram que na parede gengival a vaselina sólida e o esmalte de unhas se mostraram mais efetivos na proteção comparando com o grupo controle (p<0,05). Vaselina sólida reduziu a infiltração do corante comparada a vaselina líquida e ao esmalte (p<0,05). Contaminação do CIV pela saliva 1 min antes da proteção causou um aumento da infiltração comparado com o verniz, as vaselinas e o esmalte. A vaselina sólida é mais indicadapara a proteção superficial de restaurações com Vidrion®R.
The aim of this study was to evaluate microleakage of the conventional glass ionomer cement Vidrion®R using different agents of superficial protection. Sixty primary teeth were gotten of the Bank of Human Teeth of the Dentistry Research Center SLM. Black Class V had been confectioned in all teeth. All specimens restored with Vidrion®R control group, varnish Vidrion®V, liquid petroleum jelly, solid petroleum jelly, nail varnish, 1 minute in artificial saliva and Vidrion®V. The samples had been immersed in saliva and immersed in blue of methylene 0,5 % for 4 hours and splited longitudinally for evaluation of microinfiltration. The results showed that in the gingival wall solid petroleum jelly and the nail varnish had been more effective in the protection compared with the control group (p<0,05). Petroleum jelly reduced the dye infiltration compared to liquid petroleum jelly and the nail varnish (p<0,05). Contamination of the CIV in the saliva for 1 minute previously to the use of the varnish caused the increase of the dye infiltration compared with the varnish, petroleum jelly and the nail varnish. Solid petroleum jelly is more indicated for superficial protection of the Vidrion®R restorations.
Assuntos
Cimentos de Ionômeros de Vidro/efeitos adversos , Técnicas In Vitro , Infiltração Dentária/diagnóstico , Vaselina , Estatísticas não ParamétricasRESUMO
OBJECTIVES: To evaluate the tissue reaction of some pulpar protecting materials. METHOD AND MATERIALS: Standardized implants of calcium hydroxide (CH), glass-ionomer cement (GIC), and light-cured dentin adhesive (LDA), surgically introduced into the dorsal connective tissue of Wistar rats, were left for 15 and 30 days. For each of the 2 experimental times, a respective sham group (S) was studied. After experimentation, animals were sacrificed, and the material from implant sites was removed and studied with light microscopy and stereology (volume density of interstitial fibrosis, Vv[f], and numerical density of mast cells per area, NA[mast cell]). The implants and the surfaces of the fibrous capsule were analyzed with scanning electronic microscopy (SEM) adapted with microanalysis. RESULTS: The CH group had the smallest value of Vv[f] and the LDA group the greatest. At day 30, the Vv[f] of the LDA group showed an increase of 30% and was different from that of the CH group in the same period (P <.05). The NA[mast cell] was smaller in both the CH and the S group than in the LDA group (P <.05). The GIC group had intermediate values for Vv[f] and NA[mast cell] between CH and LDA values. There was light fibrosis in the surgical area with few mast cells associated to vessels in the S group. SEM detected presence of silica fragments in the fibrous capsule of the LDA group and calcium in the fibrous capsule of the CH group. CONCLUSIONS: All tested materials allowed healing of the implanted area; tissue reaction was smallest in the CH group.
Assuntos
Hidróxido de Cálcio/efeitos adversos , Materiais Dentários/efeitos adversos , Adesivos Dentinários/efeitos adversos , Fibrose/induzido quimicamente , Cimentos de Ionômeros de Vidro/efeitos adversos , Animais , Implantes Experimentais/efeitos adversos , Masculino , Mastócitos/efeitos dos fármacos , Ratos , Ratos WistarRESUMO
BACKGROUND: The purpose of this study was to histomorphometrically evaluate the response of periodontal tissues covering Class V resin restorations in dogs. METHODS: After raising a mucoperiosteal flap, bony defects measuring 5 x 5 mm were created on the buccal aspect of the canines of five dogs followed by cavity preparations on the root surface measuring 3 x 3 x 1 mm. Before repositioning the flap to cover the bone defect, the cavities were restored with composite resin (CR) or resin-modified glass ionomer cement (RMGIC) or were left unrestored as control (C). The dogs were euthanized 90 days after surgery. Specimens comprising the tooth and periodontal tissues were removed, processed routinely, cut into longitudinal serial sections in the buccolingual direction, and stained with hematoxylin and eosin (H&E) or Masson's trichrome. The most central sections were selected for histomorphometric analysis. RESULTS: Histomorphometric analysis revealed apical migration of epithelial tissue onto the restorative materials (RMGIC and CR). The C group presented significantly longer connective tissue attachment (P <0.05) than the RMGIC and CR groups and significantly higher bone regeneration (P <0.05) compared to the RMGIC group. Histologically, the cervical third (CT) of all groups had the most marked chronic inflammatory infiltrate. CONCLUSIONS: Within the limits of this study, it can be concluded that the restorative materials used exhibit biocompatibility; however, both materials interfered with the development of new bone and the connective tissue attachment process.
Assuntos
Resinas Acrílicas/uso terapêutico , Materiais Biocompatíveis/uso terapêutico , Resinas Compostas/uso terapêutico , Cimentos de Ionômeros de Vidro/uso terapêutico , Doenças Periodontais/terapia , Poliuretanos/uso terapêutico , Raiz Dentária , Resinas Acrílicas/efeitos adversos , Animais , Materiais Biocompatíveis/efeitos adversos , Resinas Compostas/efeitos adversos , Cárie Dentária/terapia , Cães , Cimentos de Ionômeros de Vidro/efeitos adversos , Perda da Inserção Periodontal/induzido quimicamente , Doenças Periodontais/induzido quimicamente , Poliuretanos/efeitos adversos , Retalhos Cirúrgicos , Cicatrização/fisiologiaRESUMO
Os efeitos citotóxicos dos cimentos de ionômero de vidro podem ser atribuídos aos componentes liberados por estes materiais. Assim, o objetivo desta pesquisa foi avaliar a citotoxicidade dos extratos de um cimento de ionômero de vidro convencional (Ketac Fil Plus 3M/ESPE) e de um cimento de ionômero de vidro modificado por resina (Fuji II LC GC) aplicados sobre células da linhagem odontoblástica MDPC-23. Corpos de prova com dimensões padronizadas foram preparados, imersos em 1,1mL de meio de cultura (DMEM), e incubados por 24 horas em estufa a 37ºC com 5% de CO2. Os extratos obtidos foram filtrados, tiveram o pH ajustado para 7,4 e, foram incubados por 24 horas em contato direto com as células MDPC-23. DMEM puro foi utilizado como controle negativo. O metabolismo celular foi determinado pelo teste do MTT e os valores numéricos obtidos foram submetidos à análise estatística. A morfologia das células em contato com os extratos dos materiais experimentais ou controle (DMEM) foi avaliada em microscopia eletrônica de varredura (MEV). Os resultados obtidos pelo teste do MTT não mostraram diferença estatística significante entre os dois materiais e o grupo controle. Na análise em MEV, tanto para os cimentos de ionômero de vidro como para o grupo controle, foi observado um grande número de células com morfologia ligeiramente alongada e com múltiplos prolongamentos citoplasmáticos. Assim, foi possível concluir que os materiais ionoméricos avaliados apresentam baixo efeito citotóxico para as células de linhagem odontoblástica MDPC-23.
Assuntos
Cimentos de Ionômeros de Vidro/efeitos adversos , Técnicas In Vitro , OdontoblastosRESUMO
This study evaluated, in the dog, the periodontal response to resin-modified glass-ionomer cement or amalgam restorations placed in surgical windows and left for 124 days. Plaque control was performed in half of the sites. Histologic analyses showed that sites restored with amalgam were consistently more inflamed than sites restored with resin-modified glass-ionomer. Plaque control was associated with less inflammation in both cases. Some sites restored with resin-modified glass-ionomer presented bone repair and a connective tissue lining. The inflammatory response of the periodontium to resin-modified glass-ionomer restorations is less pronounced than that associated with amalgam restorations.
Assuntos
Amálgama Dentário/efeitos adversos , Restauração Dentária Permanente/efeitos adversos , Gengivite/etiologia , Cimentos de Ionômeros de Vidro/efeitos adversos , Periodontite/etiologia , Animais , Resinas Compostas/efeitos adversos , Tecido Conjuntivo/patologia , Ligas Dentárias/efeitos adversos , Placa Dentária/complicações , Restauração Dentária Permanente/métodos , Cães , Inserção Epitelial/patologia , Feminino , Gengivite/patologia , Ligamento Periodontal/patologia , Periodontite/patologiaRESUMO
Because the risk of dental caries increases with the use of orthodontic appliances and its control cannot depend only on the patient's self-care, this study evaluated the effect of a glass ionomer cement on reducing enamel demineralization around orthodontic brackets. Fourteen orthodontic patients were randomly divided into 2 groups of 7; they received 23 brackets fitted to their premolars, bonded with either Concise (3M Dental Products, St Paul, Minn), a composite resin (control group), or Fuji Ortho LC (GC America, Chicago, Ill), a resin-modified glass ionomer cement (experimental group). The volunteers lived in a city that has fluoridated water, but they did not use fluoridated dentifrices during the study. After 30 days, the teeth were extracted and longitudinally sectioned; in the enamel around the brackets, demineralization was assessed by cross-sectional microhardness. The determinations were made at the bracket edge cementing limits, and at occlusal and cervical points 100 and 200 microm away from them. In all of these positions, indentations were made at depths from 10 to 90 microm from enamel surface. Analysis of variance showed statistically significant effects for position, material, depth, and their interactions (P<.05). The Tukey test showed that the glass ionomer cement was statistically more efficient than the control, reducing enamel demineralization in all analyses (P<.05). The use of glass ionomer cement for bonding can be encouraged because it decreases the development of caries around orthodontic brackets.
Assuntos
Cárie Dentária/prevenção & controle , Cimentos de Ionômeros de Vidro/química , Braquetes Ortodônticos/efeitos adversos , Cimentos de Resina/química , Desmineralização do Dente/prevenção & controle , Resinas Acrílicas/efeitos adversos , Resinas Acrílicas/química , Adolescente , Silicatos de Alumínio/efeitos adversos , Silicatos de Alumínio/química , Análise de Variância , Bis-Fenol A-Glicidil Metacrilato/efeitos adversos , Bis-Fenol A-Glicidil Metacrilato/química , Criança , Colagem Dentária/efeitos adversos , Colagem Dentária/métodos , Cárie Dentária/etiologia , Esmalte Dentário/patologia , Cimentos de Ionômeros de Vidro/efeitos adversos , Humanos , Cimentos de Resina/efeitos adversos , Desmineralização do Dente/etiologiaRESUMO
The aim of this study was to assess microleakage in class V cavities prepared by air abrasion or high-speed dental bur and restored with different glass ionomer cements. Sixty bovine incisors were equally divided into 6 groups: I, II and III (preparation by high-speed) and IV, V and VI (preparation by air abrasion). Groups I and IV were restored with Fuji IX; groups II and V with Ketac Molar; and groups III and VI with Vitremer. After 24 h (37 degrees C), specimens were thermocycled, isolated with nail varnish, immersed in a 0.2% Rhodamine B solution for 24 hours, sectioned longitudinally and analyzed for microleakage using an optical microscope connected to a digital camera and a computer. The images were digitized and a software allowed the quantitative evaluation of microleakage in millimeters. Data were analyzed by Wilcoxon and Kruskal-Wallis tests. It was observed that there were significant differences (p < 0.05) between incisal (enamel) and cervical (dentine/cementum) margins, mainly for Ketac Molar; there was no difference (p > 0.05) between preparation methods, except for group II (high-speed/Ketac Molar) that showed higher infiltration; regarding the materials, Ketac Molar demonstrated the highest microleakage values (p < 0.05), and only Vitremer sealed completely both margins of restorations. It was concluded that air abrasion preparation did not influence microleakage in class V restorations with the employed glass ionomer cements.
Assuntos
Abrasão Dental por Ar/efeitos adversos , Abrasão Dental por Ar/métodos , Cimentação/métodos , Infiltração Dentária/fisiopatologia , Restauração Dentária Temporária/métodos , Cimentos de Ionômeros de Vidro/química , Incisivo/química , Incisivo/fisiopatologia , Animais , Bovinos , Cimentação/efeitos adversos , Infiltração Dentária/etiologia , Infiltração Dentária/prevenção & controle , Restauração Dentária Temporária/efeitos adversos , Difusão , Cimentos de Ionômeros de Vidro/efeitos adversos , Técnicas In Vitro , Porosidade , Resultado do TratamentoAssuntos
Cimentos de Ionômeros de Vidro/classificação , Cimentos de Ionômeros de Vidro/química , Cimentos de Ionômeros de Vidro/análise , Cimentos de Ionômeros de Vidro , Cimentos de Ionômeros de Vidro/efeitos adversos , Cimentos de Ionômeros de Vidro/normas , Cimentos de Ionômeros de Vidro/uso terapêuticoRESUMO
A finalidade deste trabalho foi verificar o grau de infiltraçäo marginal em cavidades classe V, vestibulares e linguais, em dentes pré-molares humanos extraídos por razöes ortodônticas e restaurados com resina composta condensável, resina composta híbrida, resina composta modificada por poliácidos e ionômero de vidro modificado por resina. Foram utilizados 50 dentes livres de cáries, que após a coleta foram limpos e fixados em formalina tamponada a 10 por cento e, a seguir, armazenados em água destilada. Foram realizadas cavidades classe V por vestibular e lingual com 3 mm de diâmetro e 1,5 mm de profundidade, e em seguida restaurados e agrupados segundo o material restaurador escolhido em : Grupo I: dentes restaurados com resina composta condensável Alert; Grupo II: dentes restaurados com resina composta condensável Solitaire; Grupo III: dentes restaurados com resina composta híbrida Z- 250 ; Grupo IV: dentes restaurados com compômero Dyract AP e Grupo V: dentes restaurados com ionômero de vidro Vitremer (grupo controle). Concluídas as restauraçöes os dentes foram imersos em água destilada a 37ºC por 24 horas; polidos com discos Sof-Lex e impermeabilizados com Araldite e esmalte para unhas, preservando-se 2 mm ao redor da restauraçäo, sem impermeabilizaçäo. Uma vez secos, os dentes foram submetidos à ciclagem térmica com temperatura de 5ºC/ 55ºC, em um total de 200 ciclos, com 30 segundos em cada banho. Os dentes foram imersos em uma soluçäo aquosa de azul de metileno a 2 por cento por um período de 24 horas. Concluídos os procedimentos acima, os espécimes foram lavados e cortados longitudinalmente com disco diamantado, no sentido vestíbulo-lingual. Os dentes foram examinados com lupa com aumento de 7x e classificados segundo o grau de penetração máxima do corante, utilizando-se escores de 0 a 4, segundo o número de paredes infiltradas. A análise estatística aplicada aos resultados obtidos permitiu as seguintes conclusöes: a resina composta Alert demonstrou menor infiltraçäo marginal (P<0,05), seguida do Dyract AP, sendo que ambas comportaram-se estatisticamente melhor que os demais grupos. Näo houve diferença estatística significante entre a resina Z-250 e o Vitremer. A resina composta Solitaire teve o pior desempenho quanto à infiltraçäo marginal
Assuntos
Humanos , Resinas Compostas , Infiltração Dentária/etiologia , Dente Pré-Molar , Cimentos de Ionômeros de Vidro/classificação , Cimentos de Ionômeros de Vidro/efeitos adversos , Compômeros/efeitos adversos , Dentística Operatória , Materiais Dentários/classificação , Materiais Dentários/efeitos adversosAssuntos
Sensibilidade da Dentina , Adesivos Dentinários/classificação , Adesivos Dentinários/efeitos adversos , Cimentos de Ionômeros de Vidro/efeitos adversos , Cimentos Dentários/classificação , Cimentos Dentários/efeitos adversos , Resinas Compostas , Dentifrícios/efeitos adversos , Flúor/efeitos adversos , Hidróxido de Cálcio/efeitos adversos , Infiltração Dentária/etiologia , Iontoforese , Lasers , Preparo da Cavidade Dentária/efeitos adversosRESUMO
Neste trabalho foi realizada uma análise óptica da densidade óssea (níveis de cinza), na região de molares, de 31 hemimandíbulas secas. As imagens radiográficas digitais e as medidas de densidade, foram obtidas utilizando o sistema de radiografia computadorizada Digora (Soredex, Helsinque, Finlândia). As radiografias de cada hemimandíbula (HM) foram expostas em três situaçõesdistintas: 1- HM sem implante; 2- HM com a simulação da colocação de implante (implante fixado na placa de imagem); 3- HM com a simulação da colocação de implante einterposição de um simulador de tecidos moles (cera utilidade), entre a fonte de raios X e a região óssea selecionada. Os objetivos deste estudo foram avaliar alterações dos valores médios da densidade óssea periimplantar,por influência: 1- do implante de titânio; 2- de diferentes tamanhos de áreas de análise (6x50 e 2x50); 3- da distância existente entre a área de análise ao implante (justaposta e paralela) e 4- do simulador de tecidos moles. A análise dos dados pelo teste t de Student (p=0.05). Mostrou que houve uma diferença estatisticamente significativa entre os valores médios de densidade óssea na área periimplantar, das HM sem implantes e das HM com simulação de colocação de implante (p=0.002 área de 6x50 e p=0.000 área de 2x50). As diferentes dimensões de áreas de análise (6x50 e 2x50), nas HM com implantes, mostraram diferença de significância estatística entre elas (p=0.000). Em relação aos valores médios de densidade, obtidos a diferentes distâncias do implante, verificou-se que a área justaposta ao mesmo, apresentou valor maior que a área mais afastada e paralela (p=0.017). A interposição de um simulador de tecidos moles nas HM com implantes, aumentou significativamente o valor médio das densidades (p=0.010,área de 6x50 e p=0.007,área de 2x50). Com este trabalho conclui-se que: 1- o implante metálico aumenta os valores da leitura da densidade óssea na região periimplantar; 2- que áreas menores de análise (2x50) apresentaram valores de densidade maiores que as áreas de 6x50; 3- que a medida que a área de análise se afasta da imagem do implante o valor da leitura da densidade diminui; e 4- que o simulador de tecidos moles utilizado aumentou o valor da leitura da densidade óssea periimplantar de forma significativa