This paper focuses on studying how mineral oil, sunflower, soybean, and corn lubricants influence friction and wear effects during the manufacturing of aluminum parts via the single point incremental forming (SPIF) process. To identify how friction, surface roughness, and wear change during the SPIF of aluminum parts, Stribeck curves were plotted as a function of the SPIF process parameters such as vertical step size, wall angle, and tool tip semi-spherical diameter. Furthermore, lubricant effects on the surface of the formed parts are examined by energy dispersive spectroscopy (EDS) and scanning electron microscope (SEM) images, the Alicona optical 3D measurement system, and Fourier-transform infrared spectroscopy (FTIR). Results show that during the SPIF process of the metallic specimens, soybean and corn oils attained the highest friction, along forces, roughness, and wear values. Based on the surface roughness measurements, it can be observed that soybean oil produces the worst surface roughness finish in the direction perpendicular to the tool passes (Ra =1.45 µm) considering a vertical step size of 0.25 mm with a 5 mm tool tip diameter. These findings are confirmed through plotting SPIFed Stribeck curves for the soybean and corn oils that show small hydrodynamic span regime changes for an increasing sample step-size forming process. This article elucidates the effects caused by mineral and vegetable oils on the surface of aluminum parts produced as a function of Single Point Incremental Sheet Forming process parameters.
RESUMO
This article focuses on obtaining ultra high molecular weight polyethylene (UHMWPE) material reinforced with functionalized single-walled carbon nanotubes (f-SWCNTs) and the manufacturing of unicompartmental knee implants via Single-Point Incremental Forming process (SPIF). The physicochemical properties of the developed UHMWPE reinforced with 0.01 and 0.1 wt% concentrations of f-SWCNTs are investigated using Raman and Thermogravimetic Analysis (TGA). Tensile mechanical tests performed in the nanocomposite material samples reveal a 12% improvement in their Young's modulus when compare to that of the pure UHMWPE material samples. Furthermore, the surface biocompatibility of the UHMWPE reinforced with f-SWCNTs materials samples was evaluated with human osteoblast cells. Results show cell viability enhancement with good cell growth and differentiation after 14 incubation days, that validates the usefulness of the developed nanocomposite material in the production of hip and knee artificial implants, and other biomedical applications.