Shape memory alloy (SMA) micro cables have a wide potential for attenuation of vibrations and structural health monitoring due to energy dissipation. This work evaluates the effect of SMA thermomechanical coupling during dynamic cycling and the fatigue life of NiTi SMA micro cables submitted to tensile loadings at frequencies from 0.25 Hz to 10 Hz. The thermomechanical coupling was characterized using a previously developed methodology that identifies the self-heating frequency. When dynamically loaded above this frequency, the micro cable response is dominated by the self-heating, stiffening significantly during cycling. Once above the self-heating frequency, structural and functional fatigues of the micro cable were evaluated as a function of the loading frequency for the failure of each individual wire. All tests were performed on a single wire with equal cross-section area for comparison purposes. We observed that the micro cable's functional properties regarding energy dissipation capacity decreased throughout the cycles with increasing frequency. Due to the additional friction between the filaments of the micro cable, this dissipation capacity is superior to that of the single wire. Although its fatigue life is shorter, its delayed failure compared to a single wire makes it a more reliable sensor for structural health monitoring.
Assuntos
Ligas de Memória da Forma , Titânio , Humanos , Teste de Materiais , Estresse Mecânico , Titânio/química , FadigaRESUMO
The mechanical loading frequency affects the functional properties of shape memory alloys (SMA). Thus, it is crucial to study its effect for the successful use of these materials in dynamic applications. Based on the superelastic cyclic behavior, this work presents an experimental methodology for the determination of the critical frequency of the self-heating of a NiTi Belleville conical spring. For this, cyclic compressive tests were carried out using a universal testing machine with loading frequencies ranging from 0.5 Hz to 10 Hz. The temperature variation during the cyclic tests was monitored using a micro thermocouple glued to the NiTi Belleville spring. Numerical simulations of the spring under quasi-static loadings were performed to assist the analysis. From the experimental methodology applied to the Belleville spring, a self-heating frequency of 1.7 Hz was identified. The self-heating is caused by the latent heat accumulation generated by successive cycles of stress-induced phase transformation in the material. At 2.0 Hz, an increase of 1.2 °C in the average temperature of the SMA device was verified between 1st and 128th superelastic cycles. At 10 Hz, the average temperature increase reached 7.9 °C and caused a 10% increase in the stiffness and 25% decrease in the viscous damping factor. Finally, predicted results of the force as a function of the loading frequency were obtained.