RESUMO

This article demonstrates the possibility of producing hybrid cementitious materials (pastes, mortars, concretes, and precast elements) based on fly ash (FA) and construction and demolition wastes (CDW) using alkaline activation technology. Sodium sulfate was used as an activator and fine and coarse aggregates were obtained from CDW residues. An addition of Portland cement (OPC) (10 to 30%) allowed for improvement in the mechanical behavior of the hybrid cements and them to be cured at room temperature (25 °C). The FA and CDW cementitious materials obtained compressive strengths of 37 MPa and 32 MPa, respectively. The compressive strength of FA and CDW alkali-activated concretes at 28 days of curing was 22 MPa and 18 MPa, respectively, which identifies them as structural concretes according to NSR-10 title C in Colombia. The potential use of these concretes was validated by obtaining and classifying precast materials.

RESUMO

In this research, the mechanical behavior of masonry mortars made with partial substitution of sand by recycled fine aggregates (RFAs) of mortar (MT) and recycled clay brick (RCB) was compared. Mortar specimens were built in two groups (MT and RCB) considering different replacement proportions by dry weight. To reduce the water absorption of RFAs during mortar making, the prewetting method was utilized. All the mixtures were assembled with a volumetric cement-to-aggregate ratio of 1:4 and a consistency of 175 ± 5 mm. The properties in the fresh and hardening state of mortars were analyzed separately. The experimental results showed that the properties of mortars in a fresh state (bulk density and air content) were affected if RFA was added to the mixture; however, mortars assembled with up to 40% and 50% of MT and RCB, respectively, accomplished a compressive strength value of reference for new mixtures. Both mortar groups showed good results in adhesive strength values, with the RCB mortars standing up as they achieved greater adherence than the control mortar with substitution percentages of up to 30%. Therefore, the reutilization of both RFAs is feasible, notably in rendering and bonding functions.

RESUMO

The porosity of mortars with recycled ceramic aggregates (10, 20, 30, 50, and 100% as a replacement of natural aggregate) was evaluated and analyzed using three different techniques. The results of gas adsorption (N2), Scanning Electron Microscopy (SEM) image analysis and open porosity allowed establishing the relationship between the recycled aggregate content and the porosity of these mortars, as well as the relationship between porosity and the physical and mechanical properties of the mortars: absorption, density, compressive strength, modulus of elasticity, and drying shrinkage. Using the R2 coefficient and the equation typology as criteria, additional data such as Brunauer, Emmett, and Teller (BET) surface area (N2 adsorption) established significant correlations with the mentioned properties; with SEM image analysis, no explanatory relationships could be established; and with open porosity, revealing relationships were established (R2 > 0.9). With the three techniques, it was confirmed that the increase in porosity is related to the increase in the amount of ceramic aggregate; in particular with gas adsorption (N2) and open porosity. It was concluded that the open porosity technique can explain the behavior of these recycled mortars with more reliable data, in a simple and direct way, linked to its establishment with a more representative sample of the mortar matrix.

RESUMO

Recycling is an important habit to avoid waste. This paper evaluates the performance of masonry mortar, elaborated by replacing natural sand with recycled fine aggregate (RFA) obtained from mortar. Five families of mixtures were prepared with different replacement proportions: 20%, 40%, 60%, and 100%. A 1:4 volumetric cement-to-aggregate ratio was used for all mixtures by experimentally adjusting the amount of water to achieve the same consistency of 175 ± 5 mm. The effects of the following procedures were analyzed: (1) the use of a deconstruction technique to collect the RFA, (2) pre-wetting of the aggregates, and (3) the use of a commercial plasticizer. Experimental results show that it is possible to use this type of recycled fine aggregate as a substitute for natural sand by up to 60% in the manufacture of masonry mortar without significantly affecting its properties.

RESUMO

Recycled aggregates (RA) from construction and demolition can be used in permeable concretes (PC), improving the environment. PCs have a significant porous network, their cement paste and the interaction between the paste and the RA establishing their strength. Therefore, it is important to evaluate the porosity in the interfacial transition zones. The porosity of the cement paste, the aggregate and the interfacial transitional zones (ITZ) of a PC with recycled coarse aggregates (RCA) and silica fume (SF) is measured by means of image analysis-scanning electron microscope (IA)-(SEM) and by mapping the chemical elements with an SEM-EDS (energy dispersive spectrometer) detector microanalysis linked to the SEM and, as a contrast, the mercury intrusion porosimetry technique (MIP). In the IA process, a "mask" was created for the aggregate and another for the paste, which determined the porosity percentage (for the anhydrous material and the products of hydration). The results showed that using SF caused a reduction (32%) in the cement paste porosity in comparison with the PC with RA. The use of RA in the PC led to a significant increase (190%) in the porosity at different thicknesses of ITZ compared with the reference PC. Finally, the MIP study shows that the use of SF caused a decrease in the micropores, mesopores and macropores.

RESUMO

This paper aims to contribute to acoustical comfort in buildings by presenting a study about the polymer waste micronized poly (ethylene vinyl acetate) (EVA) to be used in mortars for impact sound insulation in subfloor systems. The evaluation method included physical, mechanical and morphological properties of the mortar developed with three distinct thicknesses designs (3, 5, and 7 cm) with replacement percentage of the natural aggregate by 10%, 25%, and 50% EVA. Microscopy analysis showed the surface deposition of cement on EVA, with preservation of polymer porosity. The compressive creep test estimated long-term deformation, where the 10% EVA sample with a 7 cm thick mortar showed the lowest percentage deformation of its height. The impact noise test was performed with 50% EVA samples, reaching an impact sound insulation of 23 dB when the uncovered slab was compared with the 7 cm thick subfloor mortar. Polymer waste addition decreased the mortar compressive strength, and EVA displayed characteristics of an influential material to intensify other features of the composite.

RESUMO

O objetivo deste artigo foi expor a atual conjuntura da geração de resíduos em Belo Horizonte de forma a apresentar as principais características dos resíduos de construção civil (RCC) acerca de sua tipologia, origem, predominância em sua composição, além de dados a respeito das obras que o geraram, como seu padrão construtivo e tipo de edificação. Os resultados demonstraram que a maior parte dos rejeitos gerados na capital é de base cerâmica, oriundos de obras de reformas residenciais de casas, classificadas em padrão normal de acabamento, localizadas, sobretudo, nas regionais Centro-sul e Pampulha. Pela determinação destas características foi possível estabelecer recomendações aplicáveis tanto às usinas de reciclagem como ao sistema de gerenciamento de resíduos da capital como forma de minimizar as causas da variabilidade dos agregados reciclados gerados a partir dos RCC.

The aim of this article was to expose the current state of affairs regarding the generation of waste in Belo Horizonte so as to present the main characteristics of construction civil waste (CCW) involving their typology, origin, predominance in their composition, as well as data about the construction sites that generated them, their construction pattern and type of building. The results show that the majority of the waste generated in Belo Horizonte is of ceramic base, deriving from house renovations construction sites classified as normal finishing standard located mainly in the center south and Pampulha areas. By determining these characteristics it was possible to establish recommendations applicable to the recycling plants as well as to the waste management system in Belo Horizonte to minimize the causes of the variability of the recycled aggregates generated from construction civil waste.