RESUMO
Starch is a biodegradable biopolymer, a sustainable material that can replace conventional petrochemical-based plastics. However, starch has some limitations, as it must be processed by heating and treated mechanically with a plasticizer to become thermoplastic starch (TPS). Different variables such as mixing speeds, amount, and kind of plasticizers play a vital role in preparing TPS by melting. Despite this, the properties of the TPS are not comparable with those of traditional plastics. To overcome this limitation, microcellulose or nanocellulose is added to TPS by melt mixing, including the extrusion and internal mixing process, which enables large-scale production. This review aims to compile several studies that evaluate the effect of plasticizers, as well as the relevance of incorporating different cellulosic fillers of different dimensions on the properties of TPS obtained by melt mixing. Potential applications of these materials in food packaging, biomedical applications, and other opportunities are also described.
Assuntos
Celulose , Plastificantes , Amido , PlásticosRESUMO
The species of Candida present good capability to form fungal biofilms on polymeric surfaces and are related to several human diseases since many of the employed medical devices are designed using polymers, especially high-density polyethylene (HDPE). Herein, HDPE films containing 0; 0.125; 0.250 or 0.500 wt% of 1-hexadecyl-3-methylimidazolium chloride (C16MImCl) or its analog 1-hexadecyl-3-methylimidazolium methanesulfonate (C16MImMeS) were obtained by melt blending and posteriorly mechanically pressurized into films. This approach resulted in more flexible and less brittle films, which impeded the Candida albicans, C. parapsilosis, and C. tropicalis biofilm formation on their surfaces. The employed imidazolium salt (IS) concentrations did not present any significant cytotoxic effect, and the good cell adhesion/proliferation of human mesenchymal stem cells on the HDPE-IS films indicated good biocompatibility. These outcomes combined with the absence of microscopic lesions in pig skin after contact with HDPE-IS films demonstrated their potential as biomaterials for the development of effective medical device tools that reduce the risk of fungal infections.
RESUMO
Polypropylene composites with different filler contents were prepared by creating a masterbatch containing 3 wt%. filler. A variety of silanol groups were used to synthetized three compounds in different media trough a sol-gel process with acetic acid, formic acid and ammonium hydroxide as catalysts. Besides, four different nanotubular fillers were also used to analyze their behavior and compare it with the effect caused by the silanol groups. These tubular structures comprise: unmodified halloysite, carbon nanotubes and functionalized halloysite and carbon nanotubes. Morphological characterization in SEM and STEM/TEM showed dispersion in the polypropylene matrix. According to TGA and DSC measurements thermal behavior remain similar for all the composites. Mechanical test in tension demonstrate that modulus of the composites increases for all samples with a major impact for materials containing silanol groups synthetized in formic acid. Rheological measurements show a significantly increment in viscosity for samples containing unmodified and modified carbon nanotubes. No difference was found for samples containing silanol groups and halloysite when compared to neat polypropylene. Finally, the oxygen transmission rate increased for all samples showing high barrier properties only for samples containing natural and functionalized halloysite nanotubes.