RESUMO
The increase in critical bone diseases and defects in the world's population increases the need for bone substitutes to restore form and function. Organic and inorganic scaffolds with antibacterial properties could provide advantages for bone regeneration. In this study, we obtained scaffolds of polycaprolactone (PCL) charged with calcium phosphates nanoparticles and impregnated with extracts of Colombian plants as an alternative for potential bone regeneration. Calcium phosphate nanoparticles were obtained via auto-combustion synthesis. The nanoparticles were incorporated into the PCL with a chemical dissolution-disperse process. The composite obtained was used to produce a filament to print Triply Periodic Minimal Surface (TPMS) based scaffolds. Such geometry facilitates cellular growth thanks to its interconnected porosity. The scaffolds were impregnated with extracts of Justicia cf colorifera (Acanthaceae), and Billia rosea (Sapindaceae) due to their ancestral medical applications. A physical and biological characterization was conducted. The process to print scaffolds with an enhanced geometry to facilitate the flux of biological fluids was successful. The scaffolds loaded with B. rosea showed strong antibacterial behavior, suggesting the presence of reported terpenoids with antibacterial properties. The approach used in this study evidenced promising prospects for bone defect repair.
RESUMO
Nanostructured catalysts of platinum (Pt) supported on commercial TiO2, as well as TiO2-CeO2 (1, 5 and 10 wt% CeO2), were synthesized through the Sol-Gel and impregnation method doped to 1 wt% of Platinum, in order to obtain a viable photocatalytic material able to oxidate organic pollutants under the visible light spectrum. The materials were characterized by different spectroscopy and surface techniques such as Specific surface area (BET), X-ray photoelectron spectroscopy (XPS), XRD, and TEM. The results showed an increase in the diameter of the pore as well as the superficial area of the supports as a function of the CeO2 content. TEM images showed Pt nanoparticles ranking from 2-7 nm, a decrease in the particle size due to the increase of CeO2. The XPS showed oxidized Pt2+ and reduced Pt0 species; also, the relative abundance of the elements Ce3+/Ce4- and Ti4+ on the catalysts. Additionally, a shift in the Eg band gap energy (3.02-2.82 eV) was observed by UV-vis, proving the facticity of applying these materials in a photocatalytic reaction using visible light. Finally, all the synthesized materials were tested on their photocatalytic oxidation activity on a herbicide used worldwide; 2,4-Dichlorophenoxyacetic acid, frequently use in the agriculture in the state of Jalisco. The kinetics activity of each material was measured during 6 h of reaction at UV-Vis 190-400 nm, reaching a removal efficiency of 98% of the initial concentration of the pollutant in 6 h, compared to 32% using unmodified TiO2 in 6 h.
RESUMO
A copolymer of poly(BuMA-co-EDMA) modified with C-tetra(nonyl)calix[4]resorcinarene was obtained via the impregnation method. The formation of the modified copolymer was confirmed and investigated using various techniques; in this way, the presence of calix[4]resorcinarene was confirmed by FT-IR spectroscopy and by high resolution transmission electron microscopy. The modified copolymer was used for the removal of highly toxic cations (Pb2+, Hg2+, and Cd2+) from aqueous solutions. To perform the removal, we used the batch sorption technique and the effects of time of contact, pH, and volume of sample on the effective sorption were determined. The best results were observed for Pb2+ extraction, which was comparatively more efficient. Adsorption-desorption experiments revealed that the modified copolymer could be used for several cycles without significant loss of adsorption capacity. Finally, the results showed that the modified copolymer application is highly efficient for the removal of lead ions from aqueous solutions.