RESUMO
This study investigated the effect of radiation timing on the bond strength of resin cement to intraradicular dentine. Fifty human teeth were distributed into 5 groups (n = 10): Control (nonirradiated teeth), Before-RCT (teeth irradiated before root canal treatment), After-CH (teeth irradiated after canal preparation and placement of calcium hydroxide intracanal dressing), After-RCT (teeth irradiated after completion of root canal treatment) and After-FPL (teeth irradiated after luting of a glass fibre post). Each tooth received 70 Gy irradiation. The roots were sectioned for push-out strength testing. After-RCT and After-FPL groups had significantly lower push-out strength than the control at the middle third (p < 0.05). Control and After-CH groups had a higher percentage of cohesive dentine failure. Radiotherapy after root canal obturation and post luting adversely affected the adhesiveness of resin cement to intraradicular dentine. Teeth irradiated before root canal treatment and after placement of calcium hydroxide had the best performance.
Assuntos
Colagem Dentária , Técnica para Retentor Intrarradicular , Humanos , Cimentos de Resina/uso terapêutico , Cimentos de Resina/química , Hidróxido de Cálcio/uso terapêutico , Dentina , Cavidade Pulpar , Preparo de Canal Radicular , Teste de Materiais , Vidro/química , Análise do Estresse DentárioRESUMO
To investigate the influence of post length and amount of remaining root tissue on the fracture resistance of roots restored with fibre posts relined with resin composite. Ninety upper canine teeth were divided into nine groups (n = 10). The post spaces were prepared resulting in different lengths, as follows: group 2/3, preparations with lengths of 10 mm; group 1/2, preparations with lengths of 7·5 mm; and group 1/3, preparations with lengths of 5 mm. Each group was divided into 3 subgroups according to amount of remaining root tooth tissue (2, 1 mm or 0·5 mm of thick root). Fibre posts relined with resin composite were cemented, and all teeth were restored with metal crowns. The samples were submitted to the fracture resistance test in a universal testing machine, at an angle of 135° and speed of 0·5 mm min(-1) . Failure modes were observed and the data of fracture resistance were submitted to the anova and Tukey's (α = 0·05). No statistically significant difference in fracture resistance was found among different post lengths (P > 0·05). Remaining dentin thickness of 2 and 1 mm did not differ statistically in fracture resistance (P > 0·05), which was higher than of 0·5 mm dentin thickness (P < 0·05). A prevalence of repairable failure was observed in all groups. It can be concluded that the length of fibre post relined with resin composite did not influence fracture resistance, but thickness was an important factor for the restoration of endodontically treated teeth.