RESUMO
In this work, henequen and ixlte plant fibers were carbonized in a horizontal quartz tube furnace. Several carbonized and non-carbonized fiber fabric configurations were impregnated with a bio-based epoxy resin through the infuseon process. The infrared spectra revealed characteristic bands of styrene instead of organic compounds, representing that the carbonization procedure was adequate to carbonize the plant fibers. The porosity volume ratio for the non-carbonized henequen laminates showed the highest number of voids >1.9%, and the rest of the composites had a similar void density between 1.2-1.7%. The storage modulus of the non-carbonized and carbonized henequen laminates resulted in 2268.5 MPa and 2092.1 MPa, respectively. The storage modulus of the carbonized ixtle laminates was 1541.4 MPa, which is 37.8% higher than the non-carbonized ixtle laminates and 12% higher than henequen composites. The laminates were subject to thermal shock cycling, and tomography scans revealed no alterations on the porosity level or in the cracks after the cycling procedure. Thermal shock cycling promoted the post-curing effect by increasing the glass transition temperature. The viscoelastic results showed a variation in the storage modulus when the carbonized fiber fabrics were located between natural fiber fabrics, which was attributed to more excellent compaction during the infusion process. Variations in the viscoelastic behavior were observed between the different types of natural fibers, which influenced the mechanical properties.
RESUMO
Natural lignocellulosic fibers and corresponding fabrics have been gaining notoriety in recent decades as reinforcement options for polymer matrices associated with industrially applied composites. These natural fibers and fabrics exhibit competitive properties when compared with some synthetics such as glass fiber. In particular, the use of fabrics made from natural fibers might be considered a more efficient alternative, since they provide multidirectional reinforcement and allow the introduction of a larger volume fraction of fibers in the composite. In this context, it is important to understand the mechanical performance of natural fabric composites as a basic condition to ensure efficient engineering applications. Therefore, it is also important to recognize that ramie fiber exhibiting superior strength can be woven into fabric, but is the least investigated as reinforcement in strong, tough polymers to obtain tougher polymeric composites. Accordingly, this paper presents the preparation of epoxy composite containing 30 vol.% Boehmeria nivea fabric by vacuum-assisted resin infusion molding technique and mechanical behavior characterization of the prepared composite. Obtained results are explained based on the fractography studies of tested samples.
RESUMO
A laser-induced breakdown spectroscopy (LIBS) technique was used to evaluate the filler content in particulate epoxy-copper composites. A potential application for a direct and fast measurement of the filler in composites through the LIBS results is suggested using calibrated samples. The methodology used in this work makes possible the incorporation of LIBS as a quantitative technique for the study of particle metal-filled epoxy composites, providing a method to obtain a direct estimation of the filler volume fraction.
RESUMO
Composites with sustainable natural fibers are currently experiencing remarkably diversified applications, including in engineering industries, owing to their lower cost and density as well as ease in processing. Among the natural fibers, the fiber extracted from the leaves of the Amazonian curaua plant (Ananas erectifolius) is a promising strong candidate to replace synthetic fibers, such as aramid (Kevlar™), in multilayered armor system (MAS) intended for ballistic protection against level III high velocity ammunition. Another remarkable material, the graphene oxide is attracting considerable attention for its properties, especially as coating to improve the interfacial adhesion in polymer composites. Thus, the present work investigates the performance of graphene oxide coated curaua fiber (GOCF) reinforced epoxy composite, as a front ceramic MAS second layer in ballistic test against level III 7.62 mm ammunition. Not only GOCF composite with 30 vol% fibers attended the standard ballistic requirement with 27.4 ± 0.3 mm of indentation comparable performance to Kevlar™ 24 ± 7 mm with same thickness, but also remained intact, which was not the case of non-coated curaua fiber similar composite. Mechanisms of ceramic fragments capture, curaua fibrils separation, curaua fiber pullout, composite delamination, curaua fiber braking, and epoxy matrix rupture were for the first time discussed as a favorable combination in a MAS second layer to effectively dissipate the projectile impact energy.