Organotin compounds (OTC), mainly tributyltin (TBT), have been used since the 1970s as biocides in the composition of antifouling paints. Due to its physical-chemical characteristics, TBT has high toxicity to the marine environment affecting non-target organisms. The present study aims to develop a method of direct visual identification of TBT in antifouling paints using the cyclopalladate complex, 4- (2-thiazolylazo) resorcinol (TAR-Pd), synthesized in our laboratory. Tests were performed in blank and in the paint matrix with the following OTC: TBT-O; TBT-Cl; TPT-Cl; DBT-Cl (tributyltin oxide, tributyltin chloride, triphenyltin chloride, dibutyltin chloride), in addition to the SnCl4 and SnCl2 compounds (tin IV chloride and tin II chloride), all at a concentration of approximately 20 g/ kg of dry paint). The test was performed by applying paint samples to test bodies and scraping a few tens of milligrams of the dry paint film. The scraped paint samples were submitted to the test, showing a different staining reaction for the TBT-Cl and SnCl4 samples concerning blank and other samples (TBT-O, TPT, DBT-Cl, and SnCl2). Solution tests were performed to characterize reaction products by spectroscopy in the visible band. The method developed has potential for application in real samples, being selective for TBT-Cl and SnCl4 in an acid medium, obtaining a limit of detection, in the range of 1-10 mg/kg dry paint.

RESUMO

Antifouling coatings containing biocidal agents can be used to prevent the accumulation of biotic deposits on submerged surfaces; however, several commercial biocides can negatively affect the ecosystem. In this study, various formulations of a potential biocide product comprising copper nanoparticles and capsaicin supported on zeolite ZSM-5 were analyzed to determine the influence of the concentration of each component. The incorporation of copper was evidenced by scanning electron microscopy and energy dispersive spectroscopy. Similarly, Fourier-transform infrared spectroscopy confirmed that capsaicin was supported on the zeolite surface. The presence of capsaicin on the external zeolite surface significantly reduced the surface area of the zeolite. Finally, bacterial growth inhibition analysis showed that copper nanoparticles inhibited the growth of strains Idiomarina loihiensis UCO25, Pseudoalteromonas sp. UCO92, and Halomonas boliviensis UCO24 while the organic component acted as a reinforcing biocide.

RESUMO

Marine biofouling is a global issue with economic and ecological implications. Existing solutions, such as biocide-based antifouling paints, are toxic for the environment. The search for better antifouling agents remains crucial. Recent research focuses on eco-friendly antifouling paints containing natural compounds like enzymes. This study evaluates enzymatic extracts from fishery residues for antifouling potential. Extracts from Pleoticus muelleri shrimp, Illex argentinus squid, and Lithodes santolla king crab were analyzed. Proteolytic activity and thermal stability were assessed, followed by bioassays on mussel byssus thread formation and barnacle cypris adhesive footprints. All three extracts demonstrated proteolytic activity and 24-h stability at temperate oceanic temperatures, except I. argentinus. P. muelleri extracts hindered cyprid footprint formation and mussel byssus thread generation. Further purification is required for L. santolla extract to assess its antifouling potential activity. This study introduces the use of fishery waste-derived enzyme extracts as a novel antifouling agent, providing a sustainable tool to fight against biofouling formation.

Assuntos

RESUMO

Any solid, unprotected, and undefended surface in the aquatic environment will be fouled. Fouling, on the other hand, can affect a wide range of species that can tolerate some epibiosis. Several others, on the other hand, aggressively keep the epibionts off their body surface (antifouling). Antifouling defenses are built into marine plants like seaweed and seagrass. They do have a distinctive surface structure with tightly packed needle-like peaks and antifouling coverings, which may hinder settling bacteria's ability to cling. Chemical antifouling resistance is most probably a biological reaction to epibiosis' ecological drawbacks, especially for organisms capable of performing photosynthesis. The goal of this study was to see how effective natural compounds derived from littoral seaweeds were in preventing fouling. The brown mussel, an important fouling organism, was evaluated in laboratory bioassays against fifty-one populations' crude organic extracts including fort-two macroalgae species. Antifouling activity, exhibited a distinct phylogenetic pattern, with red macroalgae having the largest share of active species, subsequently brown macroalgae. Antifouling action in green seaweeds has never been significant. Seven species showed some level of induced antifouling defense. Our findings appear to back up previous findings about secondary metabolite synthesis in seaweeds, indicating that in the hunt for novel antifoulants, researchers should concentrate their efforts on tropical red macroalgae.

Resumo contaminada. A incrustação, por outro lado, pode afetar uma ampla gama de espécies que podem tolerar alguma epibiose. Vários outros, por outro lado, mantêm agressivamente os epibiontes fora de sua superfície corporal (anti-incrustante). As defesas anti-incrustantes são construídas em plantas marinhas como algas marinhas e ervas marinhas. Elas têm uma estrutura de superfície distinta com picos semelhantes a agulhas bem compactadas e coberturas anti-incrustantes, o que pode dificultar a capacidade de fixação das bactérias. A resistência química anti-incrustante é provavelmente uma reação biológica às desvantagens ecológicas da epibiose, especialmente para organismos capazes de realizar fotossíntese. O objetivo deste estudo foi verificar a eficácia dos compostos naturais derivados de algas marinhas do litoral na prevenção da incrustação. O mexilhão-marrom, importante organismo incrustante, foi avaliado em bioensaios de laboratório contra extratos orgânicos brutos de 51 populações, incluindo duas espécies de macroalgas. A atividade anti-incrustante exibiu um padrão filogenético distinto, com macroalgas vermelhas tendo a maior participação de espécies ativas, posteriormente macroalgas marrons. A ação anti-incrustante em algas verdes nunca foi significativa. Sete espécies apresentaram algum nível de defesa anti-incrustante induzida. Nossas descobertas parecem corroborar descobertas anteriores sobre a síntese de metabólitos secundários em algas marinhas, indicando que, na busca por novos anti-incrustantes, os pesquisadores devem concentrar seus esforços em macroalgas vermelhas tropicais.

Assuntos

RESUMO

Marine biofouling is a natural process by which many organisms colonize and grow in submerged structures, causing serious economic consequences for the maritime industry. Geniculate calcareous algae (GCA; Corallinales, Rhodophyta) produce bioactive secondary metabolites and are a promise for new antifouling compounds. Here, we investigated the antifouling activity of four GCA species-Amphiroa beauvoisii, Jania sagittata (formerly Cheilosporum sagittatum), Jania crassa, and Jania prolifera (formerly Amphiroa flabellata)-from the Brazilian coast against macro- and microorganisms. Simultaneously, metabolomic tools were applied to assess the chemical profiles of these seaweeds using gas chromatography coupled to mass spectrometry (GC-MS). Data analysis by principal component and molecular networking analyses used the global natural products social molecular networking platform (GNPS). Our results showed that all extracts were active against different strains of marine bacteria and that the J. sagittata (JsSI) extract showed the highest percentage of bacterial inhibition. The J. sagittata (JsSI) extract was the most active against the mussel Perna perna, showing 100% byssus inhibition. Regarding toxicity, only the J. crassa (JcP) extract showed a 20% mortality rate. The chemical profiles of the evaluated GCA extracts differed qualitatively and quantitatively. Yet, the steroid (3ß)-cholest-5-en-3-ol was the major compound commonly identified in all extracts, with the exception of J. sagittata (JsSI). Moreover, we observed intra- and interspecific chemical variabilities among GCA extracts for the different populations, which could explain their antifouling activity variability. This study contributed new information about the chemical compounds produced by this group of seaweeds and showed its antifouling potential. These GCA species may be the subject of future studies to obtain new bioactive compounds with biotechnological potential in maritime areas.

Assuntos

RESUMO

Biofouling refers to the undesirable growth of microorganisms on water-submerged surfaces. Microfouling, the initial state of biofouling, is characterized by aggregates of microbial cells enclosed in a matrix of extracellular polymeric substances (EPSs). In seawater desalination plants, filtration systems, such as reverse-osmosis membranes (ROMs), are affected by microfouling, which decreases their efficiency in obtaining permeate water. The existing chemical and physical treatments are expensive and ineffective; therefore, controlling microfouling on ROMs is a considerable challenge. Thus, new approaches are necessary to improve the current ROM cleaning treatments. This study demonstrates the application of Alteromonas sp. Ni1-LEM supernatant as a cleaning agent for ROMs in a desalination seawater plant in northern Chile (Aguas Antofagasta S.A.), which is responsible for supplying drinking water to the city of Antofagasta. ROMs treated with Altermonas sp. Ni1-LEM supernatant exhibited statistically significant results (p < 0.05) in terms of seawater permeability (Pi), permeability recovery (PR), and the conductivity of permeated water compared with control biofouling ROMs and those treated with the chemical cleaning protocol applied by the Aguas Antofagasta S.A. desalination plant.

RESUMO

Biological fouling as termed biofouling is caused by varied living organisms and is difficult to eliminate from the environment thus becoming a major issue during membrane bioreactors. Biofouling in membrane bioreactors (MBRs) is a crucial problem in increasing liquid pressure due to reduced pore diameter, clogging of the membrane pores, and alteration of the chemical composition of the water which greatly limits the growth of MBRs. Thus, membrane biofouling and/or microbial biofilms is a hot research topic to improve the market competitiveness of the MBR technology. Though several antibiofouling strategies (addition of bioflocculant or sponge into MBRs) came to light, biological approaches are sustainable and more practicable. Among the biological approaches, quorum sensing-based biofouling control (so-called quorum quenching) is an interesting and promising tool in combating biofouling issues in the MBRs. Several review articles have been published in the area of membrane biofouling and mitigation approaches. However, there is no single source of information about biofouling and/or biofilm formation in different environmental settings and respective problems, antibiofilm strategies and current status, quorum quenching, and its futurity. Thus, the objectives of the present review were to provide latest insights on mechanism of membrane biofouling, quorum sensing molecules, biofilm-associated problems in different environmental setting and antibiofilm strategies, special emphasis on quorum quenching, and its futurity in the biofilm/biofouling control. We believe that these insights greatly help in the better understanding of biofouling and aid in the development of sustainable antibiofouling strategies.

Assuntos

RESUMO

Biofouling is responsible for structural and economic damage to man-made surfaces. Antifouling paints with biocides have been applied to structures to avoid organism adhesion; however, they have high toxicity and are not able to prevent all biofouling processes, necessitating the periodic mechanical removal of organisms and paint reapplication. Thus, there is an urgent demand for novel, effective, and environmentally friendly antifouling alternatives. As isonitrosoacetanilide is the precursor for many compounds with antibacterial activity, we believe that it could have antifouling activity against microfouling and, consequently, against macrofouling. The aim of this work was to investigate the antifouling potential of six isonitrosoacetanilide compounds and their toxicity. The compounds were employed at different concentrations (0.625-1.25-2.5-5-10 µg mL-1) in this study. The biofilm and planktonic bacteria inhibition and biofilm eradication potential were evaluated by crystal violet assay, while Amphibalus amphitrite barnacle settlement was evaluated by cyprid settlement assay. Toxicity evaluation (LC50 and EC50) was performed with A. amphitrite nauplii II and cyprid larvae. At least one of the tested concentrations of 4-Br-INA, 4-CH3-INA, and 2-Br-INA compounds showed nontoxic antifouling activity against microfouling (antibiofilm) and macrofouling (antisettlement). However, only 4-CH3-INA and 2-Br-INA also showed biofilm eradication potential. These compounds with antibiofilm activity and nontoxic effects could be combined with acrylic base paint resin or added directly into commercial paints in place of toxicant biocides to cover artificial structures as friendly antifouling agents.

Assuntos

RESUMO

Reverse osmosis (RO) desalination is a technology that is commonly used to mitigate water scarcity problems; one of its disadvantages is the bio-fouling of the membranes used, which reduces its performance. In order to minimize this problem, this study prepared modified thin film composite (TFC) membranes by the incorporation of chitosan-silver particles (CS-Ag) of different molecular weights, and evaluated them in terms of their anti-biofouling and desalination performances. The CS-Ag were obtained using ionotropic gelation, and were characterized by Fourier transform infrared spectroscopy (FTIR), high-resolution scanning electron microscopy (HR-SEM), energy-dispersive X-ray spectroscopy (EDX), thermogravimetric analysis (TGA) and dynamic light scattering (DLS). The modified membranes were synthetized by the incorporation of the CS-Ag using the interfacial polymerization method. The membranes (MCS-Ag) were characterized by Fourier transform infrared spectroscopy (FTIR), atomic force microscopy (AFM) and contact angle. Bactericidal tests by total cell count were performed using Bacillus halotolerans MCC1, and anti-adhesion properties were confirmed through biofilm cake layer thickness and total organic carbon (%). The desalination performance was defined by permeate flux, hydraulic resistance, salt rejection and salt permeance by using 2000 and 5000 mg L-1 of NaCl. The MCS-Ag-L presented superior permeate flux and salt rejection (63.3% and 1% higher, respectively), as well as higher bactericidal properties (76% less in total cell count) and anti-adhesion capacity (biofilm thickness layer 60% and total organic carbon 75% less, compared with the unmodified membrane). The highest hydraulic resistance value was for MCS-Ag-M. In conclusion, the molecular weight of CS-Ag significantly influences the desalination and the antimicrobial performances of the membranes; as the molecular weight decreases, the membranes' performances increase. This study shows a possible alternative for increasing membrane useful life in the desalination process.

RESUMO

In humid environments, the formation of biofilms and microfouling are known to be the detrimental processes that first occur on stainless steel surfaces. This is known as biofouling. Subsequently, the conditions created by metabolites and the activity of organisms trigger corrosion of the metal and accelerate corrosion locally, causing a deterioration in, and alterations to, the performance of devices made of stainless steel. The microorganisms which thus affect stainless steel are mainly algae and bacteria. Within the macroorganisms that then damage the steel, mollusks and crustaceans are the most commonly observed. The aim of this review was to identify the mechanisms involved in biofouling on stainless steel and to evaluate the research done on preventing or mitigating this problem using nanotechnology in humid environments in three areas of human activity: food manufacturing, the implantation of medical devices, and infrastructure in marine settings. Of these protective processes that modify the steel surfaces, three approaches were examined: the use of inorganic nanoparticles; the use of polymeric coatings; and, finally, the generation of nanotextures.

RESUMO

Recent advances in nanotechnology have allowed the encapsulation of hazardous antifouling (AF) biocides in silica mesoporous nanocapsules (SiNC) reducing their short-term toxicity. However, the chronic effects of such novel nanoadditives remain understudied. The present study aimed to assess short- and long-term sub-lethal effects of soluble forms (DCOIT and Ag) and nanostructured forms (SiNC-DCOIT and SiNC-DCOIT-Ag) of two AF biocides and the "empty" nanocapsule (SiNC) on juveniles of Crassostrea gigas after 96 h and 14 days of exposure. Juvenile oysters exposed for a short period to free DCOIT and AgNO3 presented worse physiological status comparing with those exposed to the nanostructured forms. The long-term exposure to DCOIT and Ag+ caused an extensive biochemical impairment comparing with the tested nanomaterials, which included oxidative damage, activation of the antioxidant defense system, and neurotransmission impairment. Despite the negative effects mostly observed on the health condition index and AChE, the encapsulation of the abovementioned AF biocides into SiNC seems to be a technological advantage towards the development of AF nanoadditives with lower long-term toxicity comparing with the soluble forms of such biocides.

Assuntos

RESUMO

In this study, we provide a baseline assessment of introduced marine species along the extensive (~600 km) Brazilian semiarid coast. We reported 27 introduced and 26 cryptogenic species. Moreover, the main vectors of introduction were ballast water, shipping lines, oil and gas activities, biofouling, and rafting on plastic debris. The taxa were Ascidiacea (17 species) and Bryozoa (17), followed by Crustacea (6), Mollusca (6), Cnidaria (3), Echinodermata (3), and Porifera (1). Among these invertebrates, some species are recognized as drivers of impacts such as the invasive corals (Tubastraea tagusensis and Tubastraea coccinea), the bivalves Isognomom bicolor and Perna viridis, the crab Charybdis hellerii, the brittle star Ophiothela mirabilis, and, finally, the bryozoan Membraniporopsis tubigera. These species threaten the biodiversity of unique ecosystems such as intertidal sandstone reefs, shallow-water coral reefs, and mesophotic ecosystems. Moreover, the up-to-date results highlight that this region is a hotspot of bioinvasion in the tropical South Atlantic.

Assuntos

RESUMO

Photovoltaic panels can be colonized by a highly diverse microbial diversity, despite life-threatening conditions. Although they are distributed worldwide, the microorganisms living on their surfaces have never been profiled in tropical regions using 16S rRNA high-throughput sequencing and PICRUst metagenome prediction of functional content. In this work, we investigated photovoltaic panels from two cities in southeast Brazil, Sorocaba and Itatiba, using these bioinformatics approach. Results showed that, despite significant differences in microbial diversity (p < 0.001), the taxonomic profile was very similar for both photovoltaic panels, dominated mainly by Proteobacteria, Bacteroidota and lower amounts of Cyanobacteria phyla. A predominance of Hymenobacter and Methylobacterium-Methylorubrum was observed at the genus level. We identified a microbial common core composed of Hymenobacter, Deinococcus, Sphingomonas, Methylobacterium-Methylorubrum, Craurococcus-Caldovatus, Massilia, Noviherbaspirillum and 1174-901-12 sharing genera. Predicted metabolisms focused on specific genes associated to radiation and desiccation resistance and pigments, were detected in members of the common core and among the most abundant genera. Our results suggested that taxonomic and functional profiles investigated were consistent with the harsh environment that photovoltaic panels represent. Moreover, the presence of stress genes in the predicted functional content was a preliminary evidence that microbes living there are a possibly source of metabolites with biotechnological interest.

Assuntos

RESUMO

The objective of this study was to report, for the first time, the presence of an invasive coral (Tubastraea tagusensis) in an oil platform on the Brazilian equatorial continental shelf. This structure is located more than 1200 km north from other oil and gas structures colonized by this coral. We also discussed the retirement and decommissioning of old biofouling-encrusted oil and gas platforms (~62 platforms) from decreased production and the current oil crisis, exacerbated by the COVID-19 pandemic. This presents an ecological concern due invasive coral range expansion and potential impacts to poorly studied ecosystems such as marginal shallow-water coral reefs and mesophotic ecosystems. It is imperative that mindful risk analysis and rigorous environmental studies must precede the installation of new oil and gas platforms. In addition, decommissioning of retired structures should take into consideration marine restoration and non-indigenous species dispersal, and more specifically, Tubastraea bioinvasion.

Assuntos

RESUMO

In the last decades, the incorporation of copper in polymeric membranes for water treatment has received greater attention, as an innovative potential solution against biofouling formation on membranes, as well as, by its ability to improve other relevant membrane properties. Copper has attractive characteristics: excellent antimicrobial activity, high natural abundance, low cost and the existence of multiple cost-effective synthesis routes for obtaining copper-based materials with tunable characteristics, which favor their incorporation into polymeric membranes. This study presents a comprehensive analysis of the progress made in the area regarding modified membranes for water treatment when incorporating copper. The notable use of copper materials (metallic and oxide nanoparticles, salts, composites, metal-polymer complexes, coordination polymers) for modifying microfiltration (MF), ultrafiltration (UF), nanofiltration (NF), forward osmosis (FO) and reverse osmosis (RO) membranes have been identified. Antibacterial and anti-fouling effect, hydrophilicity increase, improvements of the water flux, the rejection of compounds capacity and structural membrane parameters and the reduction of concentration polarization phenomena are some outstanding properties that improved. Moreover, the study acknowledges different membrane modification approaches to incorporate copper, such as, the incorporation during the membrane synthesis process (immobilization in polymer and phase inversion) or its surface modification using physical (coating, layer by layer assembly and electrospinning) and chemical (grafting, one-pot chelating, co-deposition and mussel-inspired PDA) surface modification techniques. Thus, the advantages and limitations of these modifications and their methods with insights towards a possible industrial applicability are presented. Furthermore, when copper was incorporated into membrane matrices, the study identified relevant detrimental consequences with potential to be solved, such as formation of defects, pore block, and nanoparticles agglomeration during their fabrication. Among others, the low modification stability, the uncontrolled copper ion releasing or leaching of incorporated copper material are also identified concerns. Thus, this article offers modification strategies that allow an effective copper incorporation on these polymeric membranes and solve these hinders. The article finishes with some claims about scaling up the implementation process, including long-term performance under real conditions, feasibility of production at large scale, and assessment of environmental impact.

RESUMO

This study aimed to investigate the toxicity of innovative antifouling nanostructured biocides DCOIT and silver associated to silica nanocapsules (SiNC) on the tropical microcrustacean Mysidopsis juniae. The toxicity of the tested compounds can be summarized as follows (acute tests): DCOIT > SiNC-Ag > SiNC-DCOIT > SiNC-DCOIT-Ag > SiNC > Ag; (chronic tests): SiNC-Ag > SiNC-DCOIT-Ag > DCOIT > Ag > SiNC, although it was not possible to determine the chronic toxicity of SiNC-DCOIT. In general, our data demonstrated that mysids were more sensitive than most temperate species, and it was possible to conclude that the combination SiNC-DCOIT-Ag showed less acute toxicity in comparison to the isolated active compounds, reinforcing data obtained for species from temperate environments on the potential use of nanomaterial to reduce toxicity to non-target species. However, despite representing less risk to the environment, the compound SiNC-DCOIT-Ag is still very toxic to the non-target tropical mysid.

Assuntos

RESUMO

Examining the effects of disturbances within marine urban communities can shed light on their assembly rules and invasion processes. The effects of physical disturbance, through the removal of dominant native habitat-builders, were investigated in the recolonization of disturbed patches and colonization of plates on pier pilings, in a Chilean port. On pilings, disturbance substantially affected community structure after 3 months, although it slowly converged across treatments after 10 months. On plates, cryptogenic and non-indigenous species richness increased with removal severity, which was not observed in natives. Opportunistic taxa took advantage of colonizing at an early successional stage, illustrating a competition-colonization trade-off, although indirect effects might be at play (e.g. trophic competition or selective predation). Recovery of the habitat-builders then occurred at the expense of cryptogenic and non-indigenous taxa. Whether natives could continue winning against increasing propagule and colonization pressures in marine urban habitats deserves further attention. The interactions between disturbance and biological invasions herein experimentally shown in situ contribute to our understanding of multiple changes imposed by marine urbanization in a growing propagule transport network.

Assuntos

RESUMO

Abstract The golden mussel is an aquatic invasive species that was introduced in South America in the '90s, including Brazil, and was firstly registered in 2001 in the Paraná state. This bivalve causes macrofouling issues because adhere in substrates and form dense aggregations, affecting especially hydroelectric power plants, and water treatment facilities, apart from the native biodiversity. The present research aimed to diagnose the distribution of Limnoperna fortunei in the Paraná state using environmental DNA (eDNA) from 174 sites from 12 basins, and scientific and technical previous records. L. fortunei eDNA was found in 90 sites from 11 hydrographic basins sampled. Most of the positive samples were detected in Iguaçu (42), Tibagi (15), and Ivaí (10) rivers basins. We also registered the first occurrence for five basins: Cinzas, Itararé, Ivaí, Pirapó e Ribeira rivers. Together, our and previous data recorded L. fortunei in 118 sites, between adult, larvae, and eDNA detection. Moreover, the results evidenced that eDNA is a low coast and reliable tool, and it may be very recommended for L. fortunei early detection and diagnosis. The present research was the greatest and most widespread survey for golden mussel prospection in a state in Brazil, supported a worrying scenario for Parana, with the urgent need for intense and continuous monitoring and prevention actions for controlling and mitigation of the L. fortunei impacts.

RESUMO

The influence of the lateral size and the content of graphene oxide (GO) flakes in specific oxygenate functional groups on the anti-biofouling properties and performance of thin-film composite membrane (TFC) was studied. Three different multidimensional GO samples were prepared with small (500-1200 nm), medium (1200-2300 nm), and large (2300-3600 nm) size distribution, and with different degrees of oxidation (GO3 > GO2 > GO1), varying the concentration of the hydrogen peroxide amount during GO synthesis. GO1 sheets' length have a heterogeneous size distribution containing all size groups, whilst GO2 is contained in a medium-size group, and GO3 is totally contained within a small-size group. Moreover, GO oxygenate groups were controlled. GO2 and GO3 have hydroxyl and epoxy groups at the basal plane of their sheets. Meanwhile, GO1 presented only hydroxyl groups. GO sheets were incorporated into the polyamide (PA) layer of the TFC membrane during the interfacial polymerization reaction. The incorporation of GO1 produced a modified membrane with excellent bactericidal properties and anti-adhesion capacity, as well as superior desalination performance with high water flow (133% as compared with the unmodified membrane). For GO2 and GO3, despite the significant anti-biofouling effect, a detrimental impact on desalination performance was observed. The high content of large sheets in GO2 and small sheet stacking in GO3 produced an unfavorable impact on the water flow. Therefore, the synergistic effect due to the presence of large- and small-sized GO sheets and high content of OH-functional groups (GO1) made it possible to balance the performance of the membrane.

RESUMO

Biofilm in reverse osmosis (RO) membranes is a common problem in water treatment at haemodialysis facilities. Bacteria adhere and proliferate on RO membranes, forming biofilms, obstructing and damaging the membranes and allowing the transfer of bacteria and/or cellular components potentially harmful to the health of haemodialysis patients. Our aim was to characterize the bacterial community associated to biofilm of RO membranes and to identify potentially pathogenic bacteria present in the haemodialysis systems of two dialysis centres in Chile. The diversity of the bacterial communities present on RO membranes and potable and osmosed water samples was evaluated using Illumina sequencing. Additionally, bacteria from potable water, osmosed water and RO membrane samples were isolated, characterized and identified by Sanger's sequencing. The molecular analyses of metagenomics showed that the phyla having a greater relative abundance in both dialysis centres were Proteobacteria and Planctomycetes. Pseudomonas, Stenotrophomonas, Agrobacterium, Pigmentiphaga, Ralstonia, Arthrobacter, Bacteroides and Staphylococcus were bacterial genera isolated from the different samples obtained at both haemodialysis centres. Pseudomonas spp. was a bacterial genus with greater frequency in all samples. Pseudomonas and Staphylococcus showed higher levels of resistance to the antibiotics tested. Results demonstrated the presence of potentially pathogenic bacteria, showing resistance to antimicrobials on RO membranes and in osmosed water in both dialysis centres studied.