RESUMO

Objective: the purpose of the study was to evaluate the micro-shear bond strength of different cements to translucent zirconia before and after thermocycling aging. Material and methods: Twelve translucent zirconia ceramic discs were used in the study. Specimens were sandblasted using 50 µm aluminum oxide (Al2 O3 ) particles. The specimens were divided into three groups (n = 4) according to the cement type: Panavia resin cement (control group), resin modified glass ionomer (RMGI), and Activa bioactive cement. Each group was further sub-divided into two equal subgroups (n = 2) according to whether the specimens were subjected to thermocycling or not. Thermocycling was performed in distilled water at 5000 cycles between 5 o C - 55 o C. The micro-shear bond strength test (µSBS) was measured using universal testing machine. Kruskal-Wallis test was used to compare between the three cements. Dunn's test was used for pair-wise comparisons when Kruskal-Wallis test is significant. Mann-Whitney U test was used to compare between micro-shear bond strength before and after thermocycling P ≤ 0.05. Results: In non-aged subgroups, there was no significant difference between Panavia and Activa; both showed significantly the highest mean µSBS values (22.9 MPa, 31.3 MPa respectively). While, RMGI showed the lowest µSBS values (4.7 MPa). In thermocycled subgroups, Panavia showed significantly the highest mean µSBS values (32.2 MPa). There was no significant difference between RMGI and Activa; both showed the lowest significant mean µSBS values (3.2 MPa and 8.7 MPa respectively). Conclusions: RMGI and Activa couldn't be considered long-term reliable materials for cementing zirconia. However, Panavia provided the most durable bond to zirconia. (AU)

Objetivo: O objetivo do estudo foi avaliar a resistência de união ao microcisalhamento de diferentes cimentos à zircônia translúcida antes e após o envelhecimento da termociclagem. Material e métodos: Doze discos de zircônia translúcidos foram utilizados no estudo. As amostras foram jateadas com partículas de óxido de alumínio de 50 µm (Al2 O3 ). Os espécimes foram divididos em três grupos (n = 4), de acordo com o tipo de cimento: cimento resinado Panavia (grupo controle), ionômero de vidro modificado por resina (RMGI) e cimento bioativo Activa. Cada grupo foi subdividido em dois subgrupos iguais (n = 2), dependendo se as amostras foram submetidas ou não a termociclagem. A termociclagem foi realizada em água destilada a 5000 ciclos entre 5°C - 55°C. O teste de resistência de união por microcisalhamento (µSBS) foi medido usando uma máquina de teste universal. O teste de Kruskal-Wallis foi utilizado para comparar os três cimentos. O teste de Dunn foi usado para comparações entre pares quando o teste de Kruskal-Wallis foi significativo. O teste U de Mann-Whitney foi utilizado para comparar a resistência de união ao microcisalhamento antes e após a termociclagem (P ≤ 0,05). Resultados: Nos subgrupos sem envelhecimento por termociclagem, não houve diferença significativa entre Panavia e Activa; ambos mostraram significativamente os maiores valores médios de µSBS (22,9 MPa, 31,3 MPa, respectivamente). Por sua vez, o RMGI apresentou os menores valores de µSBS (4,7 MPa). Nos subgrupos termociclados, Panavia mostrou significativamente os maiores valores médios de µSBS (32,2 MPa). Não houve diferença significativa entre RMGI e Activa; ambos apresentaram os menores valores médios significativos de µSBS (3,2 MPa e 8,7 MPa, respectivamente). Conclusões: RMGI e Activa não puderam ser considerados materiais confiáveis para cimentação à zircônia a longo prazo. No entanto, a Panavia apresentou a ligação mais durável à zircônia. (AU)

Assuntos

RESUMO

Abstract Introduction Modern dentistry is reflected in the insertion of new materials with different adhesion forms in dental structures, such as the Universal adhesive system. Objective To evaluate the bond strength of the universal dentin adhesive system, in the form of self-etching and conventional application, compared with a simplified conventional adhesive system, in two distinct periods: 1 week and 6 months. Material and method 48 bovine incisors separated into 6 groups, stored for 7 days, were selected. Worn out the buccal enamel until dentin exposure. Adper Single Bond 2 (3M Espe) or SingleBond Universal (3M Espe) adhesives were applied, and catheters filled with Opallis Flow (FGM) composite were placed. After photoactivation, the catheters were removed and the specimens (n ​​= 48), stored in distilled water at 37 °C for one week and six months, were exposed. The specimens were fixed to a universal testing machine (EMIC DL 2000) with a speed of 0.5 mm / min. Bond strength (BS) was calculated in MPa, and data were statistically analyzed by Anova and Tukey test at 5% significance level. Result For Adper Single bond, the BS was equivalent in the times tested; for Universal conventional and self-conditioning time influenced the BS, with a decrease in the results. At 1 week, all stickers were different from each other, with higher BS for Universal conventional mode, followed by universal self-etching mode and then Adper Single bond. Conclusion The best results were achieved with universal adhesive in conventional mode for both tested times.

Resumo Introdução A odontologia moderna é refletida na inserção de novos materiais com diferentes formas de adesão nas estruturas dentárias, como o sistema adesivo Universal. Objetivo Avaliar a resistência adesiva do sistema adesivo universal em dentina, na forma de aplicação auto condicionante e convencional, comparando com um sistema adesivo convencional simplificado, em dois períodos distintos: 1 semana e 6 meses. Material e método Foram selecionados 48 incisivos bovinos separados em 6 grupos, armazenados por 7 dias. Desgastado o esmalte vestibular, até exposição da dentina. Aplicaram-se os adesivos Adper Single Bond 2 (3M Espe) ou SingleBond Universal (3M Espe), e sobre este, posicionados cateteres preenchidos com o compósito Opallis Flow (FGM). Após fotoativação, removeram-se os cateteres e expuseram-se os corpos de prova (n=48), armazenados em água destilada a 37 °C por uma semana e seis meses. Os corpos de prova foram fixados uma máquina universal de ensaios (EMIC DL 2000), com velocidade de 0,5 mm/min. A resistência de união (RU) foi calculada em MPa, e os dados foram analisados estatisticamente pela Anova e pelo teste de Tukey ao nível de 5% de significância. Resultado Para Adper Single bond, a RU foi equivalente nos tempos testados; para Universal modo convencional e autocondicionante o tempo influenciou na RU, havendo um decréscimo nos resultados. Em 1 semana, todos os adesivos foram diferentes entre si, com maior RU para Universal modo convencional, seguido por universal modo autocondicionante e então pelo Adper Single bond. Conclusão O melhor desempenho foi do adesivo universal na forma convencional nos dois tempos testados.

Assuntos

RESUMO

Um dos maiores desafios atuais da ciência dos materiais dentários é a obtenção de união efetiva e durável às cerâmicas de alto conteúdo cristalino. O objetivo do presente estudo foi avaliar a resistência de união, energia de superfície e tipos de fratura de dois sistemas cerâmicos após diferentes formas de tratamento de superfície associada à aplicação do plasma em pressão atmosférica. Para o estudo foram obtidas quarenta placas de zircônia (12 mm x 5 mm x 1,5 mm) de dois tipos de cerâmicas zircônia (E.max ZirCad e Calypso), polidas e limpas por ultrassom durante 5 minutos. Divididas aleatoriamente em 2 grupos de acordo com o sistema cerâmico e 4 subgrupos (n=5) de acordo com o tratamento de superfície, (I) controle (primer), (II) jateamento com partículas micrométricas de alumina (Al2O3) + primer, (III) jateamento com partículas micrométricas de alumina (Al2O3) + plasma + primer, (IV) plasma + primer. Foram confeccionados cento e vinte cilindros de resina composta (Z100), utilizando matrizes cilíndricas (1,0 mm x 3,0 mm) cimentadas com cimento resinoso, Multilink N, sobre as placas de zircônia. Os espécimes foram armazenados em água destilada durante 24 horas a 37° C, depois testados para microcisalhamento em máquina de teste Shimadzu EZ a 1,0 mm/min. Os dados obtidos foram submetidos à análise estatística para comparação entre os grupos E.max e Calypso em relação à resistência à união (força/área ­ MPa), ângulo de contato e os tipos de fratura. Os dados foram analisados pelos testes ANOVA One-Way e Kruskal-Wallis para resistência de união (p=0,003) e (p=0,005) e ângulo de contato (p<0,001) e (p<0,001). Não houve diferença significativa para os dados de fratura (p=0,145), pelo teste quiquadrado, com predomínio de fraturas mistas. Os valores de resistência de união das cerâmicas Y-TZP apresentaram maiores valores quando o plasma foi associado ao jateamento com óxido de alumínio e/ou primer e a aplicação somente do plasma não superou os valores alcançados pelas outras formas de tratamento da superfície. Essa associação resultou em menores valores dos ângulos de contato. Houve maior frequência de fraturas mistas quando realizado somente o tratamento com óxido de alumínio e quando em associação com o plasma.(AU)

One of the major challenges today in the science of dental materials is the achievement of effective and durable bonding to ceramics with high crystalline content. The objective of the present study was to evaluate the efficacy of plasma at atmospheric pressure in the adhesion of ceramic zirconia through the bond strength, surface energy and type of fracture of two ceramic systems after different forms of surface treatment associated with the application of plasma at atmospheric pressure. For the study forty zirconia plates (12 mm x 5 mm x 1.5 mm) were obtained from two zirconia ceramics (E.max ZirCad and Calypso), polished and cleaned by ultrasound for 5 minutes. Randomly divided into 2 groups according to the ceramic system and 4 subgroups (n = 5) according to the surface treatment, control (primer), primer + blasting with micrometric alumina (Al2O3) particles, primer + blasting with micrometric particles of alumina (Al2O3) + plasma, primer + plasma. One hundred and twenty cylinders of composite resin (Z-100) were made using cylindrical matrices (1.0 mm x 3.0 mm) cemented on the zirconia plates. The specimens were stored in distilled water for 24 hours at 37°C, then tested for microshear on a Shimadzu EZ test machine at 0.5 mm / min. The obtained data were submitted to statistical analysis for comparison between the E.max and Calypso groups in relation to the bond strength (strength / area - Mpa), contact angle and fracture types. The data were analyzed by ANOVA One-Way and Kruskal-Wallis tests for bond strength (p=0.003) and (p=0.005) and contact angle (p<0.001) and (p<0.001). There was no significant difference for the fracture data (p = 0.145), by the chi-square test, with a predominance of mixed fractures. The bond strength values of the Y-TZP ceramics showed higher values when the plasma was associated with blasting with aluminum oxide and / or primer and the application of only the plasma did not exceed the values reached by the other forms of surface treatment. This association resulted in lower values of contact angles. It is a higher frequency of mixed fractures when only aluminum oxide treatment is performed and when it is associated with plasma.(AU)

Assuntos

RESUMO

Apesar de inúmeras vantagens, tal como alta resistência, a cimentação da zircônia ainda é crítica. No presente estudo nanotubos de TiO2 foram sintetizados e aplicados sobre a superfície da zircônia, essa superfície foi caracterizada e posteriormete foi conduzido o teste de resistência de união a um cimento resinoso. Os nanotubos de TiO2 foram produzidos por síntese alcalina, misturados com álcool isopropílico (50% em peso) e aplicados em fatias de zircônia pré-sinterizados (IPS e.max ZirCAD). As cerâmicas foram sinterizadas e as superfícies foram caracterizadas por microscopia confocal a laser, microscopia eletrônica de varredura (SEM) e análise de composição atômica por EDS. Para a resistência de união foram avaliados seis grupos (n = 16): 1) sem aplicação de nanotubos de TiO2 e Single Bond Universal; 2) com a aplicação de nanotubos de TiO2 e Single Bond Universal; 3) sem aplicação de nanotubos de TiO2 e Z-prime; 4) com aplicação de nanotubos de TiO2 e Z-prime; 5) sem aplicação de nanotubos de TiO2 e Signum Zirconia Bond ; 6) com aplicação de nanotubos de TiO2 e Signum Zirconia Bond. Após a sinterização, foram preparados cilindros de cimento resinoso (RelyX Ultimate) com um diâmetro de 1,40 mm e 1 mm de altura, fotopolimerizados por luz durante 40 s. Os espécimes foram armazenados durante 30 dias em água destilada a 37°C e submetidos a ensaio de microcisalhamento. Os nanotubos de TiO2 foram incorporados na superfície de zircônia e a análise EDS confirmou que os nanoaglomerados eram compostos de TiO2. O teste de microcisalhamento mostrou diferença estatística significativa entre os grupos analisados. Não houve diferença estatística significativa com a aplicação dos nanotubos, independentemente do grupo analisado. Pode-se concluir que foi possível incorporar nanotubos às superfícies de zircônia, porém esta incorporação não melhorou a resistência de união. (AU)

Despite numerous advantages such as high strength, cementing zirconia is still critical. In the present study TiO2 nanotubes were synthesized and applied over zirconia surface. This surface was characterized and after that the bond strength test was conducted to a resin cement. TiO2 nanotubes were produced by alkaline synthesis, mixed with isopropyl alcohol (50 wt%) and applied on pre-sintered zirconia slices (IPS e.max ZirCAD). The ceramics were sintered and surfaces were characterized by confocal laser microscopy, scanning electron microscopy (SEM) and EDS analysis. For the bond strength, six groups (n = 16) were evaluated: 1) without application of TiO2 and Single Bond Universal; 2) with the application of TiO2 nanotubes and Single Bond Universal; 3) without application of TiO2 nanotubes and Z-prime; 4) with application of TiO2 nanotubes and Z-prime; 5) without application of TiO2 and Signum Zirconia Bond; 6) with application of TiO2 and Signum Zirconia Bond. After sintering, resin cement (RelyX Ultimate) cylinders with diameter of 1.40 mm and 1 mm in height were prepared and light cured for 40 s. The specimens were stored for 30 days in distilled water at 37°C and submitted to shear test. The nanotubes were incorporated in the zirconia surface and the EDS analysis has confirmed that the nanoagglomerates were composed of TiO2. The shear bond strength showed there was significant statistical difference among the analyzed groups. There was no significant statistical difference with the application of the nanotubes regardless of the analyzed group. It may be concluded that it was possible to incorporate nanotubes to the zirconia surfaces, however this incorporation did not improve the bond strength. (AU)

Assuntos

RESUMO

Laminados cerâmicos são utilizados em tratamentos conservadores para restabelecer estética e função com mínimo desgaste da estrutura dental. O objetivo deste estudo foi avaliar, in vitro, o efeito de dois tratamentos de superfície em espécimes cerâmicos ultrafinos de dissilicato de lítio na resistência de união com o cimento resinoso. Laminas ultrafinas de cerâmica (14 X 12 X 0,3 mm) foram distribuídas aleatoriamente em dois grupos (n=20) de acordo com o tratamento de superfície: ácido hidrofluorídrico 5% durante 20 s e silano (HF) e Monobond Etch & Prime (Ivoclar, Vivadent) por 60 s (MEP). Dois cilindros de cimento resinoso foram confeccionados utilizando matrizes cilíndricas. Após 24 h de armazenamento, os espécimes foram submetidos ao ensaio mecânico de microcisalhamento (1 mm/min) e o modo de falha foi estabelecido. Dados de resistência de união foram analisados pelo teste t de Student (α=0.05). O ângulo de contato foi determinado. Análise morfológica das superfícies cerâmicas por meio de microscopia de força atômica e eletrônica de varredura foi realizada. Através de análise por elementos finitos foi estudada a distribuição de tensão em incisivos centrais superiores restaurados com laminados cerâmicos ultrafinos de dissilicato de lítio (0,3 mm). O modelo tridimensional foi elaborado no software Rhinoceros e exportado para software de análise Ansys. Foram modelados e analisados 04 grupos sob duas condições: desgaste ou não de esmalte e tipo de preparo. Foi aplicada uma carga de 100 N e a tensão gerada analisada pelo critério de Tensão Máxima Principal. Não houve diferença estatística nos valores de resistência de união entre o grupo HF e MEP (p=0,117). O ângulo de contato foi influenciado pelo tratamento de superfície (p=0,001); espécimes sem tratamento de superfície tiveram o maior ângulo de contato (65, 37˚) entanto que o grupo HF exibiu o menor ângulo de contato (33,80˚). A análise morfológica mostrou que o condicionamento da superfície com HF foi mais obvio mostrando poros, irregularidades e maior rugosidade em comparação com o condicionamento com MEP. A análise por elementos finitos mostrou que o grupo com laminado cerâmico cimentado sobre o esmalte sem preparo apresentou as menores concentrações de tensão tanto no esmalte como no laminado. Laminados cimentados sobre esmalte preparado mostraram concentração de tensão na interface dente/laminado. O Monobond Etch & Prime se mostrou estatisticamente equivalente ao ácido fluorídrico e silano em termos de resistência de união. Laminados cerâmicos ultrafinos cimentados sobre esmalte hígido geram menos tensão na superfície do dente e laminado. Laminados cerâmicos cimentados sobre esmalte preparado não provocam concentração de tensão adicional no esmalte(AU)

Laminate veneers are becoming a technique used in the conservative treatments by the ability to restore aesthetics and function. This study aimed to evaluate, in vitro, the effect of two surface treatments on ultrathin lithium disilicate specimens in bond strength between treated ceramics and resin cement. Ceramic ultrathin laminates (12 X 14 X 0.3 mm) were obtained and randomly distributed into two groups (n=20) according to the surface treatment: 5% hydrofluoric acid for 20 s and silane (HF) and Monobond Etch & Prime (Ivoclar, Vivadent) for 60 s (MEP). Two resin cement cylinders were made using cylindrical matrices. After 24 h storage, microshear bond strength tests were performed in a universal testing machine (1 mm/min) and failure mode was analyzed. Bond strength data were submitted to Student's t-test (α=0.05). The contact angle was measured. Micromorphogical analyses of representatives specimens were also performed (atomic force and scanning electron microscopy). Finite element analysis studied the distribution of stress in maxillary central incisors restored with ultrathin laminate veneers of lithium disilicate (0.3 mm). 3D model was elaborated in CAD Rhinoceros® software and exported to analysis software Ansys®. Four groups were modeled and analyzed under two experimental conditions: wear or non-enamel and type of preparation. A load of 100 N was applied at the palatal face. The stress was analyzed by Maximum Principal Stress criteria. Microshear bond strength values showed that HF group was not statistically different from MEP group (p=0.117). Microshear bond strength values showed that HF group was not statistically different from MEP group (p=0.117). Contact angle was influenced by surface treatments (p=0.001); specimens without surface treatment had the highest contact angle (65.37˚) whereas HF group exhibited the lowest contact angle (33.80˚). Surface morphological evaluation showed that hydrofluoric acid etching promoted a more obvious surface pattern regarding pores and irregularities with higher surface roughness in comparison to self-etching glass ceramic primer. Finite element analysis showed that laminates without enamel prepared generated the lowest stress in the enamel and in the laminate. Laminates with enamel prepared showed the stress concentration in the finishing lines of preparation in the tooth/laminate interface. Monobond Etch & Prime obtained statistically equivalent results in terms of bond strength to hydrofluoric acid and silane. Ultrathin laminate veneer cemented over sound enamel generate less stress on the surface of the tooth and laminate. Laminates veneers on prepared enamel do not cause additional tension in the tooth structure(AU)

Assuntos

RESUMO

O objetivo deste estudo foi avaliar o efeito do tratamento ultrassônico comotratamento de superfície da zircônia tetragonal policristalina estabilizada por ítria (YTZP)e depois da sinterização final, por meio de mensuração da rugosidadesuperficial e teste de resistência adesiva por microsisalhamento. Para tanto, discosde Y-TZP foram confeccionados e distribuídos em 4 grupos (n=7), conforme otratamento de superfície: 1-PRE: sonicação pré-sinterização; 2-POS: sonicação póssinterização;3-JAT: jateamento com partículas óxido de alumínio 50μm; 4-CON:sem tratamento. Os espécimes foram polidos e padronizados e posteriormentesubmetidos aos tratamentos de acordo com cada grupo. Os grupos POS, JAT eCOM foram sinterizados previamente ao tratamento e o grupo PRE após asonicação. Os grupos PRE e POS foram submetidos a tratamento em processadorultrassonico (Sonics VCX-750) em potência nominal de 30% durante 15 minutos. Ogrupo JAT foi jateado com partículas de alumínio 50μm a uma distância de 15 cm,enquanto o grupo CON não recebeu nenhum tratamento. A mensuração derugosidade superficial média (Ra) foi feita em Microscópio Confocal (MC), emseguida cilindros de cimento resinoso foram preparados e fotoativados na superfíciedo Y-TZP para serem submetidos ao ensaio mecânico de microcisalhamentorealizado em máquina de ensaios universal (INSTRON). Os valores de rugosidadesuperficial e resistência de união obtidos foram submetidos a ANOVA a um critério eteste de Tukey. Quanto aos valores de rugosidade superficial, o grupo PRE (299,91Mpa) e POS (291,23 Mpa) não apresentaram diferença estatística significante e ogrupo JAT (925,21 Mpa) mostrou maiores valores de rugosidade superficial quandocomparado ao PRE e POS. Para o teste de microcisalhamento não foramobservadas diferenças estatisticamente significantes entre os grupos. Por meio dosresultados obtidos foi possível observar que o tratamento ultrassonico é capaz dealterar a superfície da Y-TZP...

The objective of this study was to evaluate the effect of ultrasonic treatment assurface treatment of Y-TZP before and after the final sintering, through measurementof surface roughness and bond strength by microshear test. Therefore, Y-TZP discswere made and distributed in 4 groups (n = 7), as surface treatment: 1-PRE: Presinteringsonication; 2-POS: Post-sintering sonication; 3-JAT: air abrasion withaluminum oxide particles 50μm; 4-CON: no treatment. The specimens were polishedand standardized and subsequently submitted to the treatments according to eachgroup. The POS, JAT and CON groups been previously sintered to treatment and thePRE group after sonication. The PRE and POS groups were submitted to UltrasonicProcessor treatment (Sonics VCX-750) at 30% power for 15 minutes. The JAT groupreceived air abrasion with aluminum particles 50μm at distance of 15 cm, while groupreceived no treatment. The measurement of surface roughness was made inConfocal Microscope (MC), then resin cement cylinders were prepared andpolymerized in Y-TZP surface to be subjected to mechanical testing microshearperformed on universal testing machine (INSTRON). The values of surfaceroughness and bond strength were subjected to ANOVA and Tukey testAbout thevalues of surface roughness, the PRE group (299.91 MPa) and POS (291.23 MPa)showed no statistically significant difference and the JAT group (925.21 MPa)showed higher surface roughness values when compared to PRE and POS. Formicroshear test statistically significant differences were observed between thegroups. Through the results it was observed that the ultrasonic treatment is able tochange the surface of the Y-TZP and influence the bond strength to resin cement.

Assuntos

RESUMO

Introdução e objetivo:: Os sistemas adesivos autocondicionantes têm sido largamente utilizados por dentistas e pesquisadores nos procedimentos adesivos de restaurações dentárias. O objetivo deste estudo foi avaliar a resistência de união ao microcisalhamento de sistemas adesivos autocondicionantes em dentina profunda. Material e métodos: Prepararam-se 50 terceiros molares humanos até obtenção de superfícies planas de dentina profunda (2 mm abaixo do limite amelodentinário do sulco central), abrasionadas com lixa de carbeto de silício n.º 600. As amostras foram aleatoriamente divididas em cinco grupos (n = 10), de acordo com os grupos experimentais: 1) adesivo convencional Syntac (controle), 2) adesivo autocondicionante One-Up Bond F Plus (um passo), 3) Hybrid Bond (um passo), 4) AdheSE (dois passos) – unidos ao compósito Tetric Ceram – e 5) Silorane System Adhesive (dois passos), unido ao compósito de baixa contração FiltekSilorane. Os materiais foram aplicados segundo orientações dos fabricantes e com uma matriz Tygon. Os corpos-de-prova foram armazenados em água destilada a 37±2ºC por uma semana. Determinou-se a resistência de união por meio da máquina universal de ensaios Zwick, a uma velocidade de 0,5 mm/minuto. Resultados: Os resultados obtidos em MPa (DP) foram analisados estatisticamente (Anova e teste de Tukey – p < 0,05) e apresentaram os seguintes dados: 2) 25,5 (4,4); 1) 24,9 (5,3); 3) 22,4 (8,1); 4) 21,5 (4,4) e 5) 18,1 (7,2). O teste de Tukey mostrou variações significativas entre os grupos 2 e 5, que não evidenciaram diferenças com os demais grupos testados. Conclusão: O adesivo Silorane e o compósito Filtek Silorane tiveram resistência de união similar à dos demais materiais, porém menor que o One-Up Bond F Plus, quando este foi utilizado com o Tetric Ceram. Os resultados sugerem que, em termos de resistência de união, os adesivos autocondicionantes podem ser uma boa alternativa nos procedimentos restauradores adesivos em dentina profunda.

Introduction and objecttiivee:: The self-etching adhesive systems have been widely used by dentists and researchers in the procedures of adhesive dental restorations. The purpose of this study was to evaluate the microshear bond strength of self-etching adhesive systems to deep dentin.Material and methods: Fifty freshly extracted human third molars were prepared using a diamond saw until obtaining flat surfaces of deep dentin (2 mm below the DEJ of central sulcus), wet-abraded with 600-grit SiC paper. The samples were randomly divided into five groups (n = 10) according to the experimental groups: 1) conventional adhesive Syntac (control), 2) one-step self-etching adhesive One-Up Bond F Plus, 3) onestep self-etching adhesive Hybrid Bond, 4) two-step self-etching adhesive AdheSE – bonded to Tetric Ceram resin composite; and the 5) two-step self-etching adhesive Silorane System Adhesive bonded to low shrinkage resin composite Filtek Silorane. The adhesives and the resin composite were applied according to the manufacturers’ instructions, and using a Tygon tubing mold. The samples were stored in distilled water at 37±2ºC for one week. Microshear bond strengths were determined using a Zwick universal testing machine at a crosshead speed of 0.5 mm/minute. Results: The results obtained in MPa (SD) were statistically analyzed (Anova and Tukey test, p < 0.05), and showed the following results: 2) 25,5 (4,4); 1) 24,9 (5,3); 3) 22,4 (8,1); 4) 21,5 (4,4) and 5) 18,1 (7,2). There was statistically significant variation between groups 2 and 5; which did not show difference to the other groups tested. Conclusion: The Silorane System Adhesive and the low shrinkage resin composite Filtek Silorane showed similar bond strength to Syntac, Hybrid Bond and AdheSE – bonded to Tetric Ceram resin composite; however, being lower than One-Up Bond F Plus bonded to Tetric Ceram. Regarding the bond strength, the results suggest that self-etching adhesive systems can...