RESUMO

OBJECTIVE: Analyze the effects of the functionalization of pre-functionalized GIC particles with chlorhexidine on the physicochemical properties and antimicrobial activity. MATERIALS AND METHODS: Four groups were prepared: (1) GIC (Bioglass R - Biodinamica) - control group; (2) GIC-CHX 1%: Group containing 1% pre-reacted CHX particles; (3) GIC-CHX 2.5%: Group containing 2.5% pre-reacted CHX particles; (4) GIC-CHX 5%: Group containing 5% pre-reacted CHX particles. Hourglass-shaped specimens (10 mm × 2 mm x 1 mm) were fabricated for mechanical tests including cohesive strength (n = 12), modulus of elasticity (n = 12) and microhardness (n = 10). Discs (10 mm × 2 mm) were prepared for the analysis of Ca+2, PO4- and F- ions release (n = 3), and roughness (n = 12). To evaluate the setting time, a Gilmore needle was used according to ISO 9917-1:2016. Disk-shaped specimens (5 × 1mm) were manufactured and subjected to bacterial activity (n = 9) (Streptococcus mutans ATCC 159). RESULTS: Modulus, roughness, setting time and ions release (Ca+2, PO4-, and F-) there were no statistically significant differences among the groups (p > 0.05). The setting time did not change with the incorporation of CHX. The GIC-CHX 2.5% and GIC-CHX 5% groups exhibited superior antibacterial activity compared to the control group and GIC-CHX 1% (p < 0.001). The GIC-CHX 5% group showed the highest microhardness values (p < 0.041), cohesive strength (p < 0.009) when compared to the control group. CONCLUSION: The pre-reacted CHX in GICs was able to confer antimicrobial activity, improve cohesive strength, microhardness, and did not impair ion release, setting time, and roughness.

Assuntos

RESUMO

BACKGROUND: To compare the clinical effectiveness of ion-releasing restorations (IRR) vs. composite resin (CR) in dental restorations. METHODS: A systematic search was carried out from articles published until January 2024, in the biomedical databases: PubMed, Cochrane Library, Scielo, Scopus, Web of Science and Google Scholar. Randomized clinical trials were included, with a follow-up time greater than or equal to 1 year, without time and language limits and which reported the clinical effect of IRR compared to CR in dental restorations. The RoB 2.0 tool was used to assess the risk of bias of the included studies and the GRADEPro GDT tool was used to assess the quality of evidence and the strength of recommendation of the results. RESULTS: The search yielded a total of 1109 articles. After excluding those that did not meet the selection criteria, 29 articles remained for the quantitative synthesis. The analysis found no statistically significant difference when comparing the dental restorations with IRRs or CRs. CONCLUSION: The literature reviewed suggests that there are no differences between the IRRs and CRs in dental restorations.

RESUMO

BACKGROUND: The survival of ART restorations can be influenced by the choice of the restorative material. The aim of this randomized non-inferiority controlled trial was to compare the 2-year survival rate and cost analysis of two encapsulated glass ionomer cements (GIC) as occlusoproximal restorative materials in primary molars. METHODS: Children from public schools in Tietê (Brazil), aged 4-8 years with occlusoproximal dentine carious lesions in primary molars were selected and randomly assigned to receive either Equia Forte (EF) or Riva Self Cure (RSC) as restorative materials. Treatment was carried out by two trained final-year dental students in schools following ART premises. Restorations were assessed by a trained and calibrated examiner after 2, 6, 12, 18, and 24 months. The primary outcome was restoration survival after 2 years, analyzed using Kaplan-Meier survival and Cox regression analysis (α = 5%). Professional and materials costs for each group were collected in Brazilian Reais (R$) and converted into US dollars (US$) and analyzed using Monte-Carlo simulation. RESULTS: A total of 152 children (76 per group) were included in the study, and 121 (79%) were evaluated after 2 years. The overall 2-year restoration survival rate was 39% (EF = 45%; RSC = 32%) with no difference between the groups. The baseline and 2-year total cost of restorations using RSC was lower when compared to EF (incremental cost: US$ 6.18). CONCLUSION: After two years of follow-up, Riva Self Cure shows comparable restoration survival rates to Equia Forte, being more cost-effective in the Brazilian perspective. TRIAL REGISTRATION: This randomized clinical trial was registered on ClinicalTrials.Gov - NCT02730000.

Assuntos

RESUMO

OBJECTIVE: The study aims to evaluate the effect of a glass ionomer cement (GIC; Fuji 9 Gold Label, GC) with added calcium orthophosphate particles and a calcium silicate cement (CSC; Biodentine, Septodont) regarding ion release, degradation in water, mineral content, and mechanical properties of demineralized dentin samples. METHODS: GIC, GIC + 5% DCPD (dicalcium phosphate dihydrate), GIC + 15% DCPD, GIC + 5% ß-TCP (tricalcium phosphate), GIC + 15% ß-TCP (by mass), and CSC were evaluated for Ca2+/Sr2+/F- release in water for 56 days. Cement mass loss was evaluated after 7-day immersion in water. Partially demineralized dentin disks were kept in contact with materials while immersed in simulated body fluid (SBF) at 37 °C for 56 days. The "mineral-to-matrix ratio" (MMR) was determined by ATR-FTIR spectroscopy. Dentin hardness and elastic modulus were obtained by nanoindentation. Samples were observed under scanning and transmission electron microscopy. Data were analyzed by ANOVA/Tukey test (α = 0.05). RESULTS: Ca2+ release from CSC and GIC (µg/cm2) were 4737.0 ± 735.9 and 13.6 ± 1.6, respectively. In relation to the unmodified GIC, the addition of DCPD or ß-TCP increased ion release (p < 0.001). Only the dentin disks in contact with CSC presented higher MMR (p < 0.05) and mechanical properties than those restored with a resin composite used as control (p < 0.05). Mass loss was similar for GIC and CSC; however, the addition of DCPD or ß-TCP increased GIC degradation (p < 0.05). CONCLUSION: Despite the increase in ion release, the additional Ca2+ sources did not impart remineralizing capability to GIC. Both unmodified GIC and CSC showed similar degradation in water. CLINICAL RELEVANCE: CSC was able to promote dentin remineralization.

Assuntos

RESUMO

OBJECTIVE: to evaluate the effect a glass ionomer cement (GIC) containing hydroxyapatite (HAp) or calcium silicate (CaSi) particles on mineral content and mechanical properties of demineralized dentin. Ion release and compressive strength (CS) of the cements were also evaluated. METHODS: GIC (Fuji 9 Gold Label, GC), GIC+ 5%HAp and GIC+ 5%CaSi (by mass) were evaluated. Ion release was determined by induced coupled plasma optical emission spectroscopy (Ca2+/Sr2+) or ion-specific electrode (F-) (n = 3). A composite (Filtek Z250, 3 M ESPE) was used as control in remineralization tests. Demineralized dentin discs were kept in contact with materials in simulated body fluid (SBF) at 37 °C for eight weeks. Mineral:matrix ratio (MMR) was determined by ATR-FTIR spectroscopy (n = 5). Dentin hardness (H) and elastic modulus (E) were determined by nanoindentation (n = 10). CS was tested after 24 h and 7d in deionized water (n = 12). Data were analyzed by ANOVA/Tukey test (α = 0.05). RESULTS: Ca2+ and Sr2+ release was higher for the modified materials (p < 0.05). Only GIC+ 5%HAp showed higher F- release than the control (p < 0.05). All groups showed statistically significant increases in MMR, with no differences among them after 8 weeks (p > 0.05). No differences in dentin H or E were observed among groups (p > 0.05). HAp-modified GIC showed increased initial CS, while adding CaSi had the opposite effect (p < 0.05). After 7 days, GIC+ 5%CaSi presented lower CS in relation to control and GIC+ 5%HAp (p < 0.05). SIGNIFICANCE: GIC modification with HAp or CaSi affected CS and increased ion release; however, none of the groups showed evidence of dentin remineralization in comparison to the negative control.

Assuntos

RESUMO

Abstract This study analyzed the physical-chemical properties of bioactive ionomer materials. Cention N bioactive materials were evaluated chemically activated (CN) and light-cured (CN-LC), Equia Forte Fill (EQUI); conventional resin composite Filtek Z350 XT (Z350); resin glass ionomer cement Riva light Cure (RIVA) and flowable resin composite Filtek Bulk Fill Flow (BULK-F) were evaluated. Sixty specimens (n=10) were prepared for sorption (SR), solubility (SL), flexural strength (FS), shrinkage stress (SS), conversion degree (CD), microhardness (MI), and surface roughness (SR) tests. Non-cured and light-cured materials were assessed on FTIR. 30 human molar teeth were used in the bond strength test (BS). Data were subjected to ANOVA and post-hoc Tukey's test (5% of significance). EQUI showed more sorption in SR and no statistical difference from RIVA and CN-LC. CN group showed more solubility and EQUI presented less (p<0.05). BULK-F showed higher FS (MPa), without differences from CN and Z350, whereas EQUI presented the lowest FS not differing from RIVA. BULK-F and CN-LC showed more shrinkage stress differing from EQUI. CN-LC and CN showed higher CD differing from the other which showed no differences (p>0.05) between them. EQUI showed the highest hardness (p<0.05) in MI. There were no differences (p>0.05) in SR (µm). Z350 and BULK-F presented higher BS, whereas CN-LC showed the lowest, although not differing from EQUI and RIVA. Equia Forte's solubility and microhardness make it a good alternative as a restorative material. Cention N degree of conversion and flexural strength making it an esthetic option to amalgam.

Resumo Este estudo analisou as propriedades físico-químicas dos materiais de ionômero bioativo. Os materiais bioativos Cention N quimicamente ativados (CN) e fotopolimerizados (CN-LC), Equia Forte Fill (EQUI); resina composta convencional Filtek Z350 XT (Z350); resina de ionômero de vidro Riva light Cure (RIVA) e resina composta fluida Filtek Bulk Fill Flow (BULK-F) foram avaliados. Sessenta espécimes (n=10) foram preparados para testes de sorção (SR), solubilidade (SL), resistência à flexão (FS), tensão de contração (SS), grau de conversão (CD), microdureza (MI) e rugosidade da superfície (SR). Os materiais não curados e curados com luz foram avaliados por FTIR. 30 dentes molares humanos foram usados no teste de resistência de união (BS). Os dados foram submetidos a ANOVA e teste de post-hoc Tukey (5% de significância). O EQUI apresentou maior sorção no SR e não mostrou diferença estatística em relação aos grupos RIVA e CN-LC. O grupo CN apresentou maior solubilidade e o EQUI apresentou menor (p<0,05). O BULK-F apresentou maior FS (MPa), sem diferir do CN e do Z350, enquanto o EQUI apresentou o menor FS, não diferindo do RIVA. O BULK-F e o CN-LC apresentaram maior estresse de contração, diferindo do EQUI. O CN-LC e o CN apresentaram maior CD (%), diferindo dos demais, que não apresentaram diferenças (p>0,05) entre si. A EQUI apresentou a maior dureza (p<0,05) no MI. Não houve diferenças (p>0,05) na SR (µm). Z350 and BULK-F apresentaram BS, enquanto a CN-LC apresentou a menor, embora não diferindo da EQUI e da RIVA. A solubilidade e a microdureza do Equia Forte o tornam uma boa alternativa como material restaurador. O grau de conversão e a resistência à flexão do Cention N o tornam uma opção estética ao amálgama.

RESUMO

Aim: This study evaluated the short-term clinical and microbiological performance of resin-modified glass ionomer cement (RM-GIC) cement containing chlorhexidine (CHX) for atraumatic restorative treatment (ART) in primary teeth. Materials and methods: The clinical trial was conducted in 36 children that received ART in primary molars either with GIC (group I, n = 18) or GIC containing 1.25% CHX (group II, n = 18). The survival rate of restorations was checked 7 days, 3, and 6 months after their application when saliva and biofilm were collected for microbiological assessment of mutans streptococci (MS) counts. Data were analyzed using the Kruskal-Wallis/Mann-Whitney U tests for clinical analysis and microbiological evaluations (p < 0.05). Results: The survival rate of restorations was similar comparing groups I with II. Microbiological analysis showed a significant reduction in MS levels 7 days after the treatment in both saliva and biofilm of children treated with RM-GIC containing CHX (group II); however, MS counts at 3 and 6 months did not differ from the initial counts. Conclusion: A total of 1.25% CHX improved the microbiological properties of GIC in the short term without impairing the clinical performance of ART restorations. Clinical significance: Glass ionomer cement (GIC) containing CHX could be an alternative in ART procedures with the objective of promoting an additional antimicrobial effect, which is interesting for children with high counts of MS during the initial phase of adaptation to dental treatment. How to cite this article: da Silva ME, de Sena MD, Colombo NH, et al. Short-term Clinical and Microbiological Performance of Resin-modified Glass Ionomer Cement Containing Chlorhexidine for Atraumatic Restorative Treatment. Int J Clin Pediatr Dent 2023;16(S-1):S27-S32.

RESUMO

PURPOSE: Sealants are an effective method of prevention and treatment for early caries lesions. This study analyzed the 1-year clinical performance of resin-based and ionomeric sealants applied to permanent teeth under different humidity conditions. METHODS: The investigation was a triple-blind randomized clinical trial (RCT) with a four arms split-mouth design, divided according to the sealant protocol: (1) Resin-based sealant applied with rubber dam isolation, (2) Resin-based sealant applied with cotton rolls isolation, (3) Ionomeric sealant applied with rubber dam isolation and (4) Ionomeric sealant applied with cotton rolls isolation. Fifty-eight patients started the study (232 teeth), and 47 (188 teeth) remained until the 1-year recall. The modified USPHS criteria were used in the analyzes to investigate surface texture, retention and the presence of secondary caries lesions around the sealants; in the following periods: baseline, after 3, 6, 9, and 12 months by two calibrated examiners. Data were analyzed by the Mann-Whitney and Friedman tests. RESULTS: There was no difference between the types of sealants (p > 0.05). The type of humidity control influenced the superficial texture (p = 0.0012) and the retention of sealants (p = 0.0023). The sealant displacement was greater under cotton rolls isolation. Only one active caries lesion in enamel was found in the 9th month. CONCLUSION: It may be concluded that sealants effectively prevented caries, even when they were partially or totally lost, regardless of the material. The rubber dam isolation with a rubber dam promoted lower surface roughness and improved the retention rates. International Clinical Trials Registry Platform: #1111-1215-2832 (07/26/2018).

Assuntos

RESUMO

Abstract Wetting the dentin is critical to atraumatic restorative treatment. The conventional insertion can be challenging when using high-viscosity glass-ionomer cement. This study evaluated the formation of gaps and voids after three insertion methods using micro-CT. Teeth underwent removal of occlusal and proximal caries through the atraumatic restorative treatment technique. Then, they were fixed in an artificial dental arch to simulate the clinical condition and were restored using three insertion methods: conventional, Centrix injection, and double-filling. Previous dentin conditioning procedures, steel matrix and wooden wedge application, and post-insertion procedures (digital compression and surface protection) were the same. The material was inserted using a manual instrument in the conventional technique and was inserted with a syringe in the Centrix injection group. In the double-filling technique, the tooth received a first layer of a flowable ionomer (through modifying the powder/liquid ratio), and a second layer (with standard ratio) was applied before the final set of the first one. A micro-CT unit scanned each tooth before and after restoration. Each cavity was defined as the volume of interest, and the volumes of gaps and voids were calculated. Data were analyzed using one-way ANOVA and Tukey posthoc test (p < .05). Double-filling had improved filling volume with lower values for gap volume, followed by Centrix injection. The conventional technique had the highest gap volume. No statistically significant difference was observed for void volume. Double-filling demonstrated fewer gaps, followed by Centrix injection, which is critical to obtain better adhesive, remineralizing, and antibacterial activities.

Resumo O molhamento da dentina parcialmente desmineralizada no fundo da cavidade dentária é fundamental para o sucesso do tratamento restaurador atraumático. No entanto, o método de inserção convencional pode ser desafiador ao usar cimento de ionômero de vidro de alta viscosidade. Este estudo avaliou a formação de gaps e vazios internos após três métodos de inserção de cimento de ionômero de vidro de alta viscosidade usando micro-CT. Dez terceiros molares foram submetidos à remoção de cárie oclusal através da técnica de tratamento restaurador atraumático e complementação proximal (com ou sem lesão pré-existente). Em seguida, foram fixados em uma arcada dentária artificial para simular a condição clínica. Os dentes foram restaurados usando a técnica de tratamento restaurador atraumático com três métodos de inserção: convencional, injeção Centrix e dupla inserção. Os procedimentos anteriores de condicionamento dentinário, inserção de matriz de aço, aplicação de cunha de madeira e procedimentos pós-inserção do material (como compressão digital e proteção de superfície) foram os mesmos para os três grupos testados. O material foi inserido com instrumento manual na técnica convencional, seguindo a metodologia clássica do tratamento restaurador atraumático. O material foi inserido com um dispositivo desenvolvido especificamente para esse fim na técnica de inserção com seringa tipo Centrix. Na técnica de dupla obturação, o dente recebeu uma primeira camada do cimento de ionômero de vidro mais fluido (obtido através da modificação da relação pó/líquido), e uma segunda camada (com relação pó/líquido padrão) foi aplicada antes da presa final da primeira. Um micro-CT escaneou cada dente antes e depois da restauração. Cada cavidade foi definida como o volume de interesse, e os volumes de gaps e vazios foram calculados. Os dados foram analisados por ANOVA one-way e teste post-hoc de Tukey com nível de significância de 5%. A dupla inserção melhorou significativamente o volume de preenchimento com valores percentuais mais baixos para o volume do gap, seguido pela injeção com seringa tipo Centrix. A técnica convencional apresentou o maior percentual de volume de gap. Nenhuma diferença estatisticamente significativa foi observada para o volume de vazios internos. O grupo de dupla inserção demonstrou menor formação de gaps, seguido pelo grupo de injeção com seringa tipo Centrix, que é fundamental para obter melhores atividades adesivas, remineralizantes e antibacterianas.

RESUMO

PURPOSE: This study evaluates the effects of different toothpastes on the nanohardness and chemical compositions of restorative materials and dental surfaces. METHODS: Bovine enamel (n = 72) and dentin (n = 72) blocks were obtained and restored using RMGIC (n = 36) or CR (n = 36) to create the following surfaces: dentin adjacent to RMGIC (DRMGIC), enamel adjacent to RMGIC (ERMGIC), dentin adjacent to CR (DCR), and enamel adjacent to CR (ECR). After restoration, one hemiface of each specimen was coated with an acid-resistant varnish to facilitate the creation of control (C) and eroded (E) sides; the latter were achieved by erosion-abrasion cycles as follows: erosion with 1% citric acid: 5 days, four times for 2 min each day; 1% citric acid/abrasion, two times for 15 s, followed by immersion in a toothpaste slurry for 2 min. Toothpastes without fluoride (WF; n = 12), with sodium fluoride (NaF; n = 12), and with stannous fluoride (SnF2; n = 12) were used for RMGIC or CR. The specimens were analyzed for nanohardness (H), and chemical composition using energy-dispersive X-ray spectroscopy and Raman microscopy. The data were statistically analyzed using two-way repeated measures ANOVA and Tukey's test (α = 0.05). RESULTS: Lower H values were obtained with NaF for DRMGIC-C, with a statistically significant difference from the H value obtained with WF (p < 0.05). The calcium and phosphorus concentrations in DCR-E were significantly lower with WF than with the other types of toothpaste (p < 0.05). Fluoride-containing toothpastes are capable of preserving the main chemical components of the dentin adjacent to the restorative materials under erosive-abrasive conditions.

RESUMO

OBJECTIVES: Answer the PICO question: Do class I and II posterior restorations in permanent teeth placed with high-viscosity glass-ionomer cement (HV-GIC) fail more than composite resin (CR) restorations? DATA: The study was registered in the PROSPERO database (CRD42020138290). Randomized and controlled clinical trials, comparing the performance of HV-GIC and CR in load bearing cavities of posterior permanent teeth were included. Cochrane risk of bias tool and GRADE were used to assess the quality and certainty of the evidence. Meta-analyses were performed for clinical outcomes on USPHS and FDI criteria for 12-, 24- and 36-months follow-ups. SOURCES: PubMed, Scopus and Web of Science were last searched on April 2, 2022, without language or date restrictions. Reference lists of primary studies and their related article link in PubMed were manually searched. STUDY SELECTION: Ten studies were included, while data from 8 were used for the meta-analyses. A total of 849 HV-GIC and 800 CR restorations were followed. The primary outcome was the fracture/retention of the restoration, with a comparable performance for both materials on all follow-ups. The 36 months follow-up for class I restorations (longest) showed risk difference of -0,00 (95%CI -0,03 to 0,03; p = 0,98) and no heterogeneity (p = 0,98, I2=0%). The certainty of the evidence is moderate, as all included studies were at an uncertain risk of bias. CONCLUSIONS: HV-GIC and CR presented comparable clinical performance in posterior permanent teeth up to 36 months. HV-GIV wear in class I restorations followed by 24 months was the only poorer result compared to CR. CLINICAL SIGNIFICANCE: Conservative load bearing cavities in permanent posterior teeth can be restored with HV-GIC with comparable clinical performance to CR expected at least up to 3 years. HV-GIC is a valuable direct restorative option for posterior teeth in high caries risk patients, in which CR is frequently associated with failure.

Assuntos

RESUMO

This study investigated the influence of incorporating Biosilicate® on the physico-mechanical and biological properties of glass ionomer cement (GIC). This bioactive glass ceramic (23.75% Na2O, 23.75% CaO, 48.5% SiO2, and 4% P2O5) was incorporated by weight (5%, 10%, or 15%) into commercially available GICs (Maxxion R and Fuji IX GP). Surface characterization was made by SEM (n = 3), EDS (n = 3), and FTIR (n = 1). The setting and working (S/W time) times (n = 3) and compressive strength (CS) were analyzed (n = 10) according to ISO 9917-1:2007. The ion release (n = 6) was determined and quantified by ICP OES and by UV-Vis for Ca, Na, Al, Si, P, and F. To verify cell cytotoxicity, stem cells from the apical papilla (SCAP) were exposed to eluates (n = 3, at a ratio of 1.8 cm2/mL) and analyzed 24 h post-exposure. Antimicrobial activity against Streptococcus mutans (ATCC 25175, NCTC 10449) was analyzed by direct contact for 2 h (n = 5). The data were submitted for normality and lognormality testing. One-way ANOVA and Tukey's test were applied for the working and setting time, compressive strength, and ion release data. Data from cytotoxicity and antimicrobial activity were submitted for Kruskal-Wallis' testing and Dunn's post hoc test (α = 0.05). Among all experimental groups, only those with 5% (wt) of Biosilicate® showed better surface quality. Only M5% showed a comparable W/S time to the original material (p = 0.7254 and p = 0.5912). CS was maintained for all Maxxion R groups (p > 0.0001) and declined for Fuji IX experimental groups (p < 0.0001). The Na, Si, P, and F ions released were significantly increased for all Maxxion R and Fuji IX groups (p < 0.0001). Cytotoxicity was increased only for Maxxion R with 5% and 10% of Biosilicate®. A higher inhibition of S. mutans growth was observed for Maxxion R with 5% of Biosilicate® (less than 100 CFU/mL), followed by Maxxion R with 10% of Biosilicate® (p = 0.0053) and Maxxion R without the glass ceramic (p = 0.0093). Maxxion R and Fuji IX presented different behaviors regarding Biosilicate® incorporation. The impacts on physico-mechanical and biological properties were different depending on the GIC, but therapeutic ion release was increased for both materials.

RESUMO

Este trabalho teve como objetivo demonstrar a importância do Tratamento Restaurador Atraumático (ART) na Odontologia, assim como compreender sua contextualização histórica, descrever suas vantagens e desvantagens, conhecer suas indicações e limitações e seu protocolo. Foram selecionados artigos científicos publicados em português e inglês, disponíveis nas bases de dados MEDLINE, SciELO e Google Acadêmico, tendo sido incluídos artigos dos últimos dez anos, utilizando os descritores: "Tratamento Dentário Restaurador sem Trauma", "Cárie dentária", "Cimento de Ionômero de Vidro" e "Avaliação da Promoção de Saúde". O tratamento restaurador Atraumático (ART), consiste na empregabilidade de uma técnica que tem como finalidade combater a doença cárie e promover saúde. Resume-se em uma abordagem de gerenciamento para lesões de cárie com mínimos preparos, sendo utilizados apenas instrumentos manuais para remoção da dentina infectada, a exemplo a colher de dentina, sendo finalizada posteriormente com cimento de ionômero de vidro para selar a cavidade. As principais vantagens estão relacionadas a sua aplicação, sendo pregada como uma técnica de fácil execução, procedimento rápido, apresenta baixo custo, devido à necessidade mínima de materiais que são utilizados, dispensa a utilização da energia elétrica, pode ser feita em diversos ambientes. Diante da literatura compreende-se que ART é uma técnica de grande importância para o gerenciamento e declínio da doença cárie em diversos âmbitos odontológico, capaz de proporcionar grandes vantagens positiva para abordagem odontológica, tornando o atendimento menos estressante, mais colaborativo e rápido.

This study aimed to demonstrate the importance of Atraumatic Restorative Treatment (ART) in Dentistry, as well as to understand its historical context, describe its advantages and disadvantages, know its indications and limitations and its protocol. Scientific articles published in Portuguese and English, available in the MEDLINE, SciELO and Google Scholar databases were selected, including articles from the last ten years, using the descriptors: "Restorative Dental Treatment without Trauma", "Dental Caries", "Glass Ionomer Cement" and "Evaluation of Health Promotion". The Atraumatic Restorative Treatment (ART) consists of the employability of a technique that aims to combat caries and promote health. It is summarized in a management approach for caries lesions with minimal preparations, using only manual instruments to remove the infected dentin, such as the dentin spoon, being finished later with glass ionomer cement to seal the cavity. The main advantages are related to its application, being preached as a technique of easy execution, quick procedure, low cost, due to the minimum need for materials that are used, it does not require the use of electricity, it can be performed in different environments. In view of the literature, it is understood that ART is a technique of great importance for the management and decline of caries in various dental areas, capable of providing great positive advantages for the dental approach, making care less stressful, more collaborative and faster.

Assuntos

RESUMO

This study characterized TiO2 nanotube (TiO2-nt) ultrastructure and morphology, and the physicochemical impact on high-viscosity conventional glass-ionomer cement (GIC). TiO2-nt was synthesized by the alkaline method (n = 3), assessed by scanning (SEM) and transmission electron microscope (TEM), and was added (3%, 5%, 7%-in weight) to KM (Ketac Molar EasyMix™). Analyses included: SEM; Energy-dispersive spectroscopy (EDS); Raman spectroscopy (RAMAN); Setting time with Gillmore needles (ST); Color (Co); Radiopacity (XR); Water sorption (WS); and solubility (SO). Quantitative data were submitted to ANOVA and Tukey's tests (chr = 0.05). External and internal TiO2-nt diameters were 11 ± 2 nm and 6 ± 0 nm, respectively. Data analyses showed: (i) TiO2-nt present into KM matrix, with a concentration-dependent increase of Ti levels into KM, (ii) physical interaction between KM and TiO2-nt, (iii) longer initial ST for the 7% group compared to KM and 3% groups (p ≤ 0.01), (iv) decreased luminosity and yellowness for the 5% and 7% groups, (v) 36% greater radiopacity for the 5% group compared to enamel, dentin, and KM, and (vi) lower SO values for the 5% group, with no significant differences on WS across the groups. TiO2-nt displayed physical interaction with KM matrix, and also modified SO, XR and Co, without affecting ST. This study provides information on the potential impact of TiO2-nt on GIC performance. TiO2-nt may be proposed to boost confidence among dental surgeons in terms of GIC's handling characteristics, success rate and differential diagnostic.

Assuntos

RESUMO

Abstract This study evaluated the effect of aging and cementation of fiber posts using glass ionomer and resin cements on push-out bond strength, failure mode, and resin tag formation. One hundred and twenty bovine incisors were used. After post-space preparation, the specimens were randomly allocated into 12 groups (n = 10) according to the cementation system used: GC - GC Gold Label Luting & Lining); RL - RelyX Luting 2; MC - MaxCem Elite; RU - RelyX U200 and the aging periods (24 hours, 6 months, and 12 months). Slices from the cervical, middle, and apical thirds were obtained and analyzed by push-out bond strength test and confocal laser scanning microscopy. One-way ANOVA and Tukey's post-hoc test was used at a significance level of 5%. For the push-out bond strength test, no differences among GC, RU, and MC in the cervical and middle thirds were observed, regardless of the period of storage (P > 0.05). In the apical third, GC and RU showed similar bond strength but higher than other groups (P > 0.05). After 12 months, GC showed the highest bond strength (P < 0.05). Bond strength to post-space dentin decreased over time, regardless of the cementation system used. Cohesive failure was the most frequent, regardless of the period of storage, cementation system, and post-space third. Tag formation was similar among all groups. After 12 months, GC showed the highest bond strength values.

Resumo Avaliar o efeito do envelhecimento e sistemas de cimentação usando ionômero de vidro e cimentos resinosos na resistência de união à dentina após a cimentação do pino de fibra. Cento e vinte incisivos bovinos foram utilizados. Após o preparo do pós-espaço, os corpos de prova foram distribuídos aleatoriamente em 12 grupos (n = 10) de acordo com o período de envelhecimento (24 horas, 6 meses e 12 meses) e o sistema de cimentação utilizado: GC - cimento de ionômero de vidro (GC Gold Label Cimentação e Revestimento); RL - RelyX Luting 2; MC - MaxCem Elite; RU - RelyX U200. Cortes dos terços cervical, médio e apical foram obtidos e analisados por teste de resistência de união push-out e microscopia confocal de varredura a laser. ANOVA one-way e teste de Tukey foi usado a um nível de significância de 5%. Para o teste de resistência de união, não foram observadas diferenças entre GC, RU e MC nos terços cervical e médio, independentemente do período de armazenamento (P > 0,05). No terço apical, GC e RU apresentaram resistência de união semelhante, porém superior aos demais grupos (P > 0,05). Após 12 meses, o GC apresentou a maior resistência de união (P < 0,05). A resistência de união à dentina no espaço para pino diminuiu ao longo do tempo, independentemente do sistema de cimentação utilizado. A formação de tags foi semelhante entre todos os grupos. Após 12 meses, o GC apresentou os maiores valores de resistência de união.

RESUMO

O objetivo deste estudo foi analisar a resistência de união de restaurações indiretas cimentadas em superfícies dentinárias desmineralizadas com simulação da remoção seletiva da dentina com e sem uso de material forrador. Foram utilizados 60 dentes bovinos com a superfície vestibular desgastada até dentina sadia e divididos em quatro grupos: dentina sadia (controle), dentina desmineralizada (des), dentina desmineralizada e selada com resina flow (des-flow) e dentina desmineralizada e coberta com cimento de inonômero de vidro (des-civ). Todos os espécimes receberam condicionamento com ácido fosfórico (37% Condac, FGM) previamente a hibridização com adesivo universal (Single Bond Universal; 3M). O grupo des-civ recebeu uma cobertura de cimento de ionômero de vidro previamente ao condicionamento e hibridização e o grupo des-flow recebeu um selamento com resina flow (Resina Filtek Z350 XT Supreme Flowable, 3M) após condicionamento e hibridização. Em sequência, foram cimentadas peças simulando restaurações indiretas em resina composta (Grandioso ­ VOCO) na região condicionada de cada amostra. O conjunto recebeu fotoativação por 60 segundos em cada face da peça cimentada. Após 48 horas da cimentação, os espécimes dos três primeiros grupos foram submetidos aos testes mecânicos de tração, com velocidade de 1 mm/min. E após 29 dias, o quarto grupo foi submetido ao mesmo teste. A análise do tipo de fratura foi realizada por estereomicroscopia e os dados foram convertidos em MPa. Os resultados apresentaram diferença estatística de acordo com o teste ANOVA a 1 fator (p=0,011). Para as comparações múltiplas, o teste de Tukey apontou que o grupo des-flow apresentou valores menores do que o grupo controle. Todas as outras comparações foram similares. Concluiu-se que o grupo des-flow, quando comparado ao grupo controle, apresentou uma adesão inferior e que os materiais forradores não diferiram entre si (AU)

The aim of this study was to analyze the bond strength of cemented indirect restorations on demineralized dentin surfaces by simulating selective dentin removal with and without the use of a liner material. Sixty bovine teeth were used with the buccal surface worn down to healthy dentin and divided into four groups: healthy dentin (control), demineralized dentin (des), demineralized dentin sealed with flow resin (desflow) and demineralized dentin covered with glass ionomer cement (des-civ). All specimens were etched with phosphoric acid (37% Condac, FGM) prior to hybridization with universal adhesive (Single Bond Universal; 3M). The des-civ group received a glass ionomer cement cover prior to etching and hybridization, and the desflow group received a flowable resin seal (Filtek Z350 XT Supreme Flowable Resin, 3M) after etching and hybridization. Subsequently, specimens simulating indirect composite resin restorations (Grandioso - VOCO) were cemented in the etched region of each sample. The set was photoactivated for 60 seconds on each side. 48 hours after cementation, the specimens from the first three groups were subjected to mechanical tensile testing at a speed of 1 mm/min. After 29 days, the fourth group was subjected to the same test. The analysis of the fracture type was performed by stereomicroscopy and the data were converted into MPa. The results showed statistical difference according to the one-way ANOVA (p=0.011). For multiple comparisons, the Tukey's test showed that the des-flow group presented lower values than the control group. All other comparisons were similar. It was concluded that the des-flow group, when compared to the control group, presented lower adhesion and that the liner materials did not differ among themselves.(AU)

Assuntos

RESUMO

Aim: To evaluate the potential of inducing mineral density changes of indirect pulp capping materials applied to demineralized dentin. Methods: A total of 50 cavities were prepared, 5 in each tooth, in extracted ten molars without caries, impacted or semi-embedded. The cavities were scanned by microcomputed tomography (µ-CT) after creating artificial caries by microcosm method (pre-treatment). Each cavity was subjected to one of 5 different experimental conditions: control (dental wax), conventional glass ionomer cement (Fuji IX GP Extra), resin-modified calcium silicate (TheraCal LC), resin-modified calcium hydroxide (Ultra-Blend Plus), MTA (MM-MTA) and the samples were kept under intrapulpal pressure using simulated body fluid for 45 days. Then, the second µ-CT scan was performed (post-treatment), and the change in dentin mineral density was calculated. Afterward, elemental mapping was performed on the dentinal surfaces adjacent to the pulp capping agents of 5 randomly selected samples using energy dispersive X-ray spectroscopy (EDS) apparatus attached to a scanning electron microscope (SEM). The Ca/P ratio by weight was calculated. Friedman test and Wilcoxon Signed Ranks test were used to analyze the data. Results: There was a significant increase in mineral density values of demineralized dentin after treatment for all material groups (p<0.05). Resin-modified calcium silicate had similar efficacy to MTA and conventional glass ionomer cement, but was superior to resin-modified calcium hydroxide in increasing the mineral density values of demineralized dentin. Conclusions: Demineralized dentin tissue that is still repairable can be effectively preserved using materials with remineralization capability

Assuntos

RESUMO

Treatment of dental caries in children still remains challenging due to lack of cooperation with conventional treatment modalities. Recently, the use of Silver Diamine Fluoride (SDF) has proved useful in addressing this challenge. Aim: This clinical trial aimed to evaluate the effectiveness of Silver Diamine Fluoride (SDF) in arresting caries in children in Lagos, Nigeria. Methods: This was a phase III balanced randomized controlled school based interventional study on 240 children. The study group was treated with SDF while GIC was used in the control group. Follow up visits in 2 weeks, 1 month, and 3 months were carried out to assess the treatment outcome. Inferential statistics with the use of Pearson Chi-square test and Independent Student t-test were used at 5% level of significance. Results: There was significant relationship between SDF and caries arrest in 2 weeks, 1 month and 3 months' assessment period (p = 0.001). The control group showed continuous decline (71.7%, 54.3% and 50.9%) in restorative success from 2 weeks to 3 months respectively. The mean ± SD and Confidence Interval (CI) of arrested caries in the SDF group were 113± 1.24 and 113.1 ­ 113.5 respectively. In the control group the mean ± SD and CI of restorative success were 69.3±11.8 and 67.2 ­ 71.4. The effect size was 5.24. Conclusion: The result of the study showed that SDF was effective in arresting caries in children without any harm and there was statistically significant difference in the use of 38% SDF in arresting caries in children

Assuntos

RESUMO

Abstract Introduction Chronic suppurative otitis media is one of the most common causes of reversible conductive hearing loss which can lead to necrosis of the ossicles. The incus, especially its long process, is the most common ossicle affected. Objectives The present study aims to assess the use of glass ionomer cement for the reconstruction of the long process of the incus. Methods The present study was conducted on 27 patients with chronic suppurative otitis media with central perforation with dry and quiescent ears with an eroded long process of the incus submitted to tympanoplasty. The audiological evaluations were done on all patients, including preoperative and postoperative evaluation of the airbone gap; the average pure tone threshold was done 6 months postoperatively. Results The average air pure tone threshold was 42.8 dB preoperatively and 22.5 dB postoperatively. The postoperative air pure tone thresholds were significantly smaller than the preoperative values (p < 0.01). The air-bone gap was 30.5 dB at 500 Hz, 31.6 dB at 1 KHz, and 24.1 dB at 2 kHz preoperatively, and 7.7 dB at 500 Hz, 7.2 dB at 1 KHz, and 7.1 dB at 2 kHz postoperatively at the end of 6 months of follow-up. There were significant hearing gains in the air-bone gap (p < 0.001). Conclusion Glass ionomer cement is a useful and effective material for bridging the defect of the long process of the incus.

RESUMO

Introduction Chronic suppurative otitis media is one of the most common causes of reversible conductive hearing loss which can lead to necrosis of the ossicles. The incus, especially its long process, is the most common ossicle affected. Objectives The present study aims to assess the use of glass ionomer cement for the reconstruction of the long process of the incus. Methods The present study was conducted on 27 patients with chronic suppurative otitis media with central perforation with dry and quiescent ears with an eroded long process of the incus submitted to tympanoplasty. The audiological evaluations were done on all patients, including preoperative and postoperative evaluation of the air-bone gap; the average pure tone threshold was done 6 months postoperatively. Results The average air pure tone threshold was 42.8 dB preoperatively and 22.5 dB postoperatively. The postoperative air pure tone thresholds were significantly smaller than the preoperative values ( p < 0.01). The air-bone gap was 30.5 dB at 500 Hz, 31.6 dB at 1 KHz, and 24.1 dB at 2 kHz preoperatively, and 7.7 dB at 500 Hz, 7.2 dB at 1 KHz, and 7.1 dB at 2 kHz postoperatively at the end of 6 months of follow-up. There were significant hearing gains in the air-bone gap ( p < 0.001). Conclusion Glass ionomer cement is a useful and effective material for bridging the defect of the long process of the incus.