RESUMO
Abstract This study evaluated the effect of toothbrushing on enamel-cementing material-ceramic bonded interfaces, using different cementing materials. Materials and Methods: Thirty enamel and thirty ceramic blocks were bonded with cementing materials to produce the samples that were bonded with three types of cementing materials: 1- RelyX Ultimate resin cement (REXU), 2- RelyX Unicem 2 self-adhesive resin cement (REU2) and 3- heated Z100 restorative composite (60°C). Bonded interfaces of the samples were toothbrushed and the surfaces of the 3 cementing materials were evaluated for roughness (RG, in µm), roughness profile (RP, in µm), and volume loss (VL, in µm3) (baseline and after 20,000 and 60,000 toothbrushing cycles). Data were evaluated by Generalized Linear Analysis (two factors: "material" and "toothbrushing cycle") and Bonferroni test (α=0.05). Results: REXU and Z100 exhibited lower RG than that presented by REU2, except after 60,000 toothbrushing cycles when only Z100 differed from REU2. The increase in toothbrushing cycles increased the RG and RP for all materials. REU2 also showed higher RP than those showed by REXU and Z100 when it was analyzed regarding the enamel. The VL of Z100 was the lowest with 20,000 toothbrushing cycles, regarding the enamel and ceramic. For 60,000 cycles, REXU showed the lowest VL regarding the ceramic, and REU2 had the highest VL regarding the enamel and ceramic. Conclusion: In general, REXU and Z100 showed the best results regarding the evaluations performed and the REU2 exhibited the highest RG, RP, and VL.
Resumo Este estudo avaliou o efeito da escovação nas interfaces de união esmalte-material cimentante-cerâmica, utilizando diferentes materiais cimentantes. Materiais e Métodos: Trinta esmaltes e trinta blocos cerâmicos foram unidos com materiais de cimentação para produzir as amostras que foram unidas com três tipos de materiais de cimentação: 1- cimento resinoso RelyX Ultimate (REXU), 2- cimento resinoso autoadesivo RelyX Unicem 2 (REU2) e 3-compósito restaurador aquecido Z100 (60°C). As interfaces coladas das amostras foram escovadas e as superfícies dos 3 materiais cimentantes foram avaliadas quanto à rugosidade (RG, em µm), perfil de rugosidade (RP, em µm) e perda de volume (VL, em µm3) (baseline e após 20.000 e 60.000 ciclos de escovação). Os dados foram avaliados por Análise Linear Generalizada (dois fatores: "material" e "ciclo de escovação") e teste de Bonferroni (α=0,05). Resultados: REXU e Z100 apresentaram menor RG do que REU2, exceto após 60.000 ciclos de escovação, quando Z100 diferiu apenas de REU2. O aumento dos ciclos de escovação aumentou o RG e RP para todos os materiais. O REU2 também apresentou PR maior que o REXU e Z100, quando analisado em relação ao esmalte. O VL de Z100 foi o menor com 20.000 ciclos de escovação em relação ao esmalte e cerâmica. Para 60.000 ciclos, o REXU apresentou o menor VL em relação à cerâmica e o REU2 o maior VL em relação ao esmalte e à cerâmica. Conclusão: De maneira geral, REXU e Z100 apresentaram os melhores resultados nas avaliações realizadas e o REU2 apresentou os maiores RG, RP e VL..
RESUMO
INTRODUCTION: Adjustments with diamond burs on the ceramic surface can affect its roughness and decrease flexural strength. This study evaluated the effect of polishing or glazing on the surface roughness and biaxial flexural strength of a zirconia-reinforced lithium silicate glass-ceramic upon adjustment with diamond burs. METHODS: Seventy disks were prepared according to ISO 6872 and divided into seven groups (n = 10) according to different adjustments and finishing processes. Surface roughness was measured prior to biaxial flexural strength testing. The topography was analyzed using an atomic force microscope , fracture markings were identified using a stereomicroscope and representative specimens were analyzed using scanning electron microscopy. RESULTS: The use of diamond burs significantly increased the surface roughness and decreased the strength of the evaluated ceramic (p⟨0.05). Polishing reduced the ceramic's roughness but resulted in flexural strength similar to that of the groups with wear (p⟩0.05). The glaze-treated specimens showed flexural strength statistically similar to the control group (p>0.05) but higher roughness, similar to those with wear. CONCLUSIONS: Polishing reduced the surface roughness but did not affect the biaxial flexural strength of the ZLS ceramic. At the same time, the application of glaze after wear increased the strength.
Assuntos
Cerâmica , Polimento Dentário , Teste de Materiais , Propriedades de Superfície , Polimento Dentário/métodos , Zircônio , Diamante , Porcelana DentáriaRESUMO
Reabilitações estéticas e funcionais são tratamentos realizados com bastante frequência na clínica diária do Cirurgião Dentista. Para tais intervenções existem diversos materiais citados na literatura, dentre eles, amálgama, ligas metálicas, resinas compostas e cerâmicas odontológicas. As cerâmicas apresentam inúmeras vantagens que integram estética e resistência, além de adesão aos tecidos dentários, todavia é alvo de uma vasta discussão a respeito de sua resistência mecânica quando se trata de trabalhos minimamente invasivos. A utilização das restaurações cerâmicas em dentes anteriores, submetidos a estresse mecânico reduzido, quando em condições oclusais satisfatórias, é vastamente citada na literatura, inclusive em espessuras extremamente conservadoras. Entretanto, quando se trata de dentes posteriores, onde as cargas oclusais são aumentadas, a espessura torna-se fator preponderante na utilização de tais materiais. Para esclarecer tais dúvidas, o presente estudo tem como objetivo realizar uma revisão da literatura a respeito da influência da espessura das cerâmicas a base de dissilicato de lítio em dentes posteriores na resistência a fratura de tais restaurações. Foi realizado levantamento bibliográfico de artigos publicados nas bases de dados PubMed, Lilacs, Medline, Scielo e Portal de Periódicos CAPES nos últimos 10 anos e, após a leitura dos resumos, selecionados os artigos presentes nesse trabalho. Conclui-se que cerâmicas a base de dissilicato de lítio de espessuras reduzidas devem ser utilizadas em dentes posteriores com cautela, haja vista a importância do equilíbrio oclusal e dos possíveis hábitos parafuncionais muito frequentes nos nossos pacientes.
Aesthetic and functional rehabilitations are treatments performed quite frequently in the daily clinic of the Dental Surgeon. For such interventions there are several materials cited in the literature, among them, amalgam, metal alloys, composite resins and dental ceramics. Ceramics have numerous advantages that integrate aesthetics and resistance, in addition to adhesion to dental tissues, however, it is the subject of a vast discussion regarding their mechanical resistance when it comes to minimally invasive works. The use of ceramic restorations in anterior teeth, submitted to reduced mechanical stress, when in satisfactory occlusal conditions, is widely cited in the literature, including in extremely conservative thicknesses. However, when it comes to posterior teeth, where occlusal loads are increased, thickness becomes a preponderant factor in the use of such materials. To clarify these doubts, the present study aims to review the literature regarding the influence of the thickness of lithium disilicate ceramics in posterior teeth on the fracture resistance of such restorations. A bibliographic survey of articles published in PubMed, Lilacs, Medline, Scielo and Portal de Periódicos CAPES in the last 10 years was carried out and, after reading the abstracts, the articles present in this work were selected. It is concluded that reduced thickness lithium disilicate ceramics should be used in posterior teeth with caution, given the importance of occlusal balance and possible parafunctional habits that are very common in our patients.
Assuntos
Cerâmica , Porcelana Dentária , Resistência à Flexão , Reabilitação BucalRESUMO
To evaluate the stress behavior of ceramic fragment restoration, varying the thickness of the cement layer and intraoral temperature variation. A solid model of a upper lateral incisor was obtained and a defect at enamel distal/incisal edge was restored with a ceramic fragment. Based on this initial model, 4 different models (M) were built: M1 - absence of cement layer (CL) (0 µm of thickness); M2 - CL with an uniform thickness of 50 µm; M3 - CL with 50 µm at the margin of ceramics and 100 µm in the inner area far from margins; M4 - CL with 50 µm at the margin of ceramics and 200 µm in the inner area far from margins. The environment temperature changed from 5 °C to 50 °C in 4 increments. The finite element analysis was performed. Increase the cement layer thickness generated higher stress levels on ceramic surface in all temperatures, as well as on cement interface. In general hot temperature was the worst scenario for ceramic fragments integrity, since tensile and compressive stress were more intense. The maximum principal stress on ceramic fragment was found 90 MPa for M4 at 50 °C, followed for M3 (87 Mpa). For CL, the peak of stress was found for M3 at 5 °C (47 MPa). Is it possible to conclude that thick resin cement layer contribute to higher stress concentration on ceramic fragment, and extremely hot temperatures increase the risk of structural failure, since both ceramic and \cl are exposed to higher compressive and tensile stresses.
Assuntos
Porcelana Dentária/química , Análise do Estresse Dentário , Fenômenos Mecânicos , Cimentos de Resina/química , Temperatura , Módulo de Elasticidade , Análise de Elementos Finitos , Humanos , Incisivo/anatomia & histologia , Estresse Mecânico , Propriedades de SuperfícieRESUMO
PURPOSE: To evaluate the influence of particle and air-abrasion on the surface characterization and shear bond strength (SBS) of a Y-TZP ceramic with a resin cement. MATERIALS AND METHODS: Y-TZP specimens were air-abraded with 50 µm alumina particles; 120 µm alumina particles; 30 µm silica-coated alumina particles (Rocatec Soft); 110 µm silica-coated alumina particles (Rocatec Plus). Air-abrasion was performed before (BS); after (AS); before and after (BAS) zirconia sintering. Surface characterization included roughness (n = 10), wettability (n = 10), morphology (n = 2), and elemental composition (n = 2). For SBS (n = 11), composite resin discs were bonded to the air-abraded and silane-treated zirconia surface, with the resin cement RelyX ARC. Failure mode was determined. Roughness, wettability, and SBS data were analyzed by two-way ANOVA with pairwise interaction and Tukey's test (α = 0.05). RESULTS: Air-abrasion performed with coarser particles at BS and BAS moments provided the highest roughness values, while the lowest roughness values were observed with particles combined with AS moment (p < 0.01). Rocatec Plus provided lower contact angle than the 120 µm alumina particles (p = 0.013), and BAS exhibited lower contact angle than BS (p = 0.002). The combinations 120 µm/BS and the silica-coated alumina particles/AS and /BAS showed the highest SBS (p < 0.05). The combination of each particle/BAS was statistically similar to the same particle/AS. Failure mode was 100% adhesive for all groups. The interaction particle size/air-abrasion moment determined the morphological pattern. Silicon was observed only in the Rocatec groups. CONCLUSIONS: Roughness was influenced by the particle size and was higher when the zirconia was air-abraded in its green stage. The particle composition played an important role in the wettability and both studied air-abrasion moments provided similar wettability than the one in which air-abrasion is usually performed. The highest SBS values were observed in the three moments, by using certain particles for each moment.
Assuntos
Abrasão Dental por Ar/métodos , Cimentos de Resina/química , Resistência ao Cisalhamento , Ítrio/química , Zircônio/química , Óxido de Alumínio/química , Análise de Variância , Bis-Fenol A-Glicidil Metacrilato , Resinas Compostas/química , Colagem Dentária , Cimentos Dentários , Materiais Dentários/química , Falha de Restauração Dentária , Análise do Estresse Dentário , Humanos , Teste de Materiais , Microscopia Eletrônica de Varredura , Tamanho da Partícula , Polietilenoglicóis , Ácidos Polimetacrílicos , Dióxido de Silício/química , Propriedades de Superfície , MolhabilidadeRESUMO
Objective: Despite the increase of all-ceramic prosthesis in dental practice there is no evidence of the possibility of welding these structures if necessary. The objective of this study was to use CO2 laser (λ = 10.6 µm) as a welding agent to fuse dental polycrystalline alumina ceramic. Methods: Ceramic blocks of pre-sintered alumina were sectioned into 20 bars (10.0 x 1.5 x 1.5 mm) and sintered to the final cross section dimension of 1.2 x 1.2mm. The bars were adapted to an LHPG (Laser Heated Pedestal Growth) system device where the bars could be fixed in pairs and have their ends irradiated with CO2 laser to fusion. The ring-shaped laser beam (300 µm thickness) was directed with the aid of mirrors to reach samples' ends. The laser was continuously applied (40 W nominal power, 5 seconds). After welding, the samples were analyzed in stereomicroscope and SEM. A diffraction analysis was carried out with one sample. Results: CO2 laser was able to fuse the ceramic bars, but some of them showed some shape distortion in the fusion zone. The aspect of the fused alumina differed in color and translucency from the original sintered material. SEM evidenced the presence of porosity and voids in the center of the fusion zone. X-ray diffraction pointed to a reduction in crystallite size by two to four times in the welded region of samples. Conclusions: This study points to CO2 laser as a possible welding agent to polycrystalline alumina dental ceramic. Porosity observed in the molten zone gives cause for concern regarding weld resistance. (AU)
Objetivo: Apesar do aumento no número de próteses totalmente cerâmicas na prática clínica, não há evidência da possibilidade de se soldar essas estruturas se necessário. Este estudo testou o laser de CO2 (λ=10.6 µm) como um agente de solda para estruturas cerâmicas de alumina policristalina. Métodos: Blocos cerâmicos de alumina pré-sinterizada foram seccionados na forma de barras (10,0 x 1,5 x 1,5 mm) e sinterizados na dimensão final de 1,2 x 1,2 mm. As barras foram adaptadas a um sistema de crescimento de fibras cerâmicas (LHPG Laser Heated Pedestal Growth) onde as barras foram fixadas em pares e tiveram suas extremidades irradiadas com laser de CO2 até a sua fusão. O feixe de laser foi direcionado com a ajuda de espelhos para atingir as extremidades das barras. O laser foi aplicado de forma contínua (40 W de potência nominal, 5 segundos). Depois da solda, os espécimes foram analisados em estereomicroscopia e MEV. Teste de difração foi conduzido com um espécime. Resutados: O laser de CO2 foi capaz de fundir as barras cerâmicas, mas algumas delas mostraram uma distorção da forma na zona de fusão. O aspecto da alumina soldada diferiu em cor e translucidez do material original. O MEV evidenciou a presença de porosidade no centro da zona de fusão. A difração por raio-x apontou para uma redução no tamanho dos cristalitos de duas a quatro vezes na região da solda. Conclusões: Esse estudo mostrou ser possível usar o laser de CO2 como um agente de solda para uma cerâmica policristalina de alumina. A porosidade observada na zona de fusão traz preocupação quanto à resistência da solda. (AU)
Assuntos
Materiais Dentários , Lasers de Gás , Óxido de AlumínioRESUMO
O desenvolvimento das cerâmicas odontológicas só foi possível devido à introdução de novos recursos tecnológicos, que aliado a demanda por estética gerou novos conceitos quanto ao uso e aplicação desses materiais. Nos deparamos com diversos tipos de cerâmicas e métodos de obtenção que entregam resultados diferentes em relação à resistência e a translucidez. Nesse contexto, é preciso conhecer cada sistema cerâmico disponível desde suas principais características até suas limitações, para saber indicá-lo de modo correto em cada situação clínica específica. O objetivo desse trabalho é auxiliar o cirurgião-dentista na escolha de um material totalmente cerâmico, entre as cerâmicas: feldspáticas, dissilicato de lítio e zircônia para restaurações em coroas totais sobre dente. Concluiu-se que, as cerâmicas são diferentes entre si, as feldspáticas são mais usadas para casos estéticos, principalmente na técnica estratificada, o dissilicato de lítio reúne estética e resistência e a zircônia se apresenta como um material promissor por apresentar as melhores propriedades mecânicas.
The development of dental ceramics was only possible due to the introduction of new technological resources, that accompanied by the increasing demand for aesthetics generated new concepts about the use and applications of those materials. These circumstances resulted in the need of various types of ceramics and therefore production methods, which aims to deliver different results in terms of strength and translucency. In this context, it is crucial to understand each available ceramic's system characteristics and limitations, so as to properly select the right material for given clinical application. The objective of this work is to assist the dental surgeon in the choice of an allceramic material for restorations in full-coverage crowns, among three of them: feldspathic porcelain, lithium disilicate and dental zirconia. In this work was concluded that the ceramics are not identical and that feldspathic porcelains are often more used for aesthetic cases, especially in the stratified technique, the lithium disilicate combines aesthetics and strength and, finally, the dental zirconia presents itself as a promising material due to its superior mechanical properties.
Assuntos
Cerâmica , Ligas Metalo-Cerâmicas , Prótese Dentária , Coroas , Ligas Dentárias , Restauração Dentária PermanenteRESUMO
AIM: This study aims to evaluate the microshear bond strength of zirconia-based ceramics with different resin cement systems and surface treatments. MATERIALS AND METHODS: Forty blocks of zirconia-based ceramic were prepared and embedded in polyvinyl chloride (PVC) tubes with acrylic resin. After polishing, the samples were washed in an ultrasonic bath and dried in an oven for 10 min. Half of the samples were subjected to sandblasting with aluminum oxide. Blocks were divided into four groups (n = 10) in which two resin cements were used as follows: (1) RelyX™ U100 with surface-polished zirconia; (2) RelyX™ U100 with surface-blasted zirconia; (3) Multilink with surface-polished zirconia; and 4) Multilink with surface-blasted zirconia. After performing these surface treatments, translucent tubes (n = 30 per group) were placed on the zirconia specimens, and resin cement was injected into them and light cured. The PVC tubes were adapted in a universal testing machine; a stiletto blade, which was bolted to the machine, was positioned on the cementation interface. The microshear test was performed at a speed of 0.5 mm/min. Failure mode was analyzed in an optical microscope and classified as adhesive, cohesive, or mixed. RESULTS: The null hypothesis of this study was rejected because there was a difference found between the resin cement and the surface treatment. There was a statistical difference (P < 0.005) in RelyX™ U100 with surface-blasted zirconia, in relation to the other three groups. For Multilink groups, there was no statistical difference between them. CONCLUSION: Self-adhesive resin cement showed a more significant tendency toward bond strength in the ceramic-based zirconium oxide grit-blasted surfaces.
RESUMO
Os avanços na tecnologia dos materiais odontológicos têm permitido o desenvolvimento de técnicas mais conservadoras e aumentaram as chances de obter resultados estéticos mais previsíveis. Considerando as particularidades de cada técnica, a cerâmica tem sido usada devido à sua biocompatibilidade, longevidade e semelhança com a aparência natural do dente. O objetivo deste trabalho foi utilizar uma técnica minimamente invasiva previsível tanto esteticamente quanto funcionalmente para a confecção de dez laminados cerâmicos. Foi possível concluir que a proposta deste trabalho cumpriu com os requisitos para que uma reabilitação seja adequada nos quesitos de estética, função e estabilidade em longo prazo.
Technology advances in dental materials has allowed the development of more conservative techniques and increased the chances of more predictable aesthetics results. Considering the particularities of each technique, ceramics have been used due to its biocompatibility, longevity and likeness with the tooth natural appearance. The aim of this study was to use a predictable minimally invasive technique both aesthetically and functionally to fabricate 10 ceramic laminate veneers. It was concluded that the proposed technique in this work met the requirements for an esthetic, functional, and stable long-term rehabilitation.
Assuntos
Humanos , Feminino , Adulto , Cimentação , Porcelana Dentária , Planejamento de Prótese Dentária , Estética Dentária , Facetas DentáriasRESUMO
PURPOSE: To determine the elastic properties of five ceramic systems with different compositions (lithium disilicate vs. feldspathic ceramics) and processing methods and compare the stress distribution in premolars in the interface with inlays made with these systems loaded with the maximum normal bite force (665 N) using 3D finite element analysis (FEA). MATERIALS AND METHODS: The elastic properties of five ceramic restoration materials (IPS e.max Press, IPS e.max CAD, Vita PM9, Vita Mark II, Vita VM7) were obtained using the ultrasonic pulse-echo method. Three-dimensional FEA simplified models of maxillary premolars restored with these ceramic materials were created. The models were loaded with a load at the two nodes on the occlusal surface in the middle of the tooth, 2 mm from the outside of the tooth, simulating a loading ball with a radius of 6 mm. RESULTS: The means values of density (g/cm³), Young's modulus (GPa), and Poison's ratio was 2.6 ± 0.3, 82.3 ± 18.3, and 0.22 ± 0.01 for IPS e.max Press; 2.3 ± 0.1, 83.5 ± 15.0, and 0.21 ± 0.01 for IPS e.max CAD; 2.5 ± 0.1, 44.4 ± 11.5, and 0.26 ± 0.08 for PM9; 2.4 ± 0.1, 70.6 ± 4.9, and 0.22 ± 0.01 for Vitamark II; 2.4 ± 0.1, 63.3 ± 3.9, and 0.23 ± 0.01 for VM7, respectively. The 3D FEA showed the tensile stress at the interface between the tooth and the inlay was dependent on the elastic properties of the materials, since the Vita PM9 and IPS e.max CAD ceramics presented the lowest and the highest stress concentration in the interface, respectively. CONCLUSIONS: The elastic properties of ceramic materials were influenced by composition and processing methods, and these differences influenced the stress concentration at the bonding interface between tooth and restoration. The lower the elastic modulus of inlays, the lower is the stress concentration at the bonding interfaces.
Assuntos
Colagem Dentária , Porcelana Dentária/uso terapêutico , Restaurações Intracoronárias , Restauração Dentária Permanente/métodos , Análise do Estresse Dentário , Elasticidade , Análise de Elementos Finitos , Humanos , Imageamento TridimensionalRESUMO
The aim of the present study was to evaluate the influence of intra-oral aging on the tetragonal-to-monoclinic (tâm) phase transformation of two Y-TZP dental ceramics - Lava Frame (Frame) and Lava Plus (Plus) - and determine the impact of this response on their microstructures and mechanical properties: flexural strength, Young's modulus, microhardness and fracture toughness. Standardized ceramic specimens were analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM) and atomic force microscopy (AFM). After the baseline analysis, the specimens were attached to personalized intra-oral resin appliances and exposed to the oral cavity of 20 subjects for 60 days and then analyzed again. Specimens produced for mechanical properties evaluation were also analyzed before and after the 60-day intra-oral aging. The data were analyzed using two-way ANOVA and Tukey HSD's post hoc test (α=0.05). Weibull analysis was used to evaluate the strength reliability. Both Y-TZP ceramics suffered tâm phase transformation after 60-day intra-oral aging (Plus=4.7%/Frame=7.7%). SEM and AFM analyses showed dislodgement of ZrO2 grains and a significant increase in roughness after intra-oral aging for both ceramics. Both Y-TZP ceramics suffered a decrease on flexural strength, Young's modulus and fracture toughness after intra-oral aging (p<0.05). Only Plus presented a decrease of microhardness after intra-oral aging (p<0.05). Intra-oral aging for 60 days produced tâm phase transformation, changed the microstructure and decreased the mechanical properties of two Y-TZP dental ceramics.
Assuntos
Cerâmica/análise , Materiais Dentários/análise , Ítrio/análise , Zircônio/análise , Divisão Celular , Humanos , Teste de Materiais , Maleabilidade , Reprodutibilidade dos Testes , Estresse Mecânico , Propriedades de Superfície , Fatores de TempoRESUMO
Abstract This study evaluated the effect of air-abrasion on t®m phase transformation, roughness, topography and the elemental composition of three Y-TZP (Yttria-stabilized tetragonal zirconia polycrystal) dental ceramics: two conventional (Lava Frame and IPS ZirCad) and one with high-translucency (Lava Plus). Plates obtained from sintered blocks of each ceramic were divided into four groups: AS (as-sintered); 30 (air-abrasion with 30 mm Si-coated Al2O3 particles); 50 (air-abrasion with 50 mm Al2O3 particles) and 150 (air-abrasion with 150 mm Al2O3 particles). After the treatments, the plates were submitted to X-ray diffractometry; 3-D profilometry and SEM/EDS. The AS surfaces were composed of Zr and t phases. All treatments produced t®m phase transformation in the ceramics. The diameter of air-abrasion particles influenced the roughness (150>50>30>AS) and the topography. SEM analysis showed that the three treatments produced groove-shaped microretentions on the ceramic surfaces, which increased with the diameter of air-abrasion particles. EDS showed a decrease in Zr content along with the emergence of O and Al elements after air-abrasion. Presence of Si was also detected on the plates air-abraded with 30 mm Si-coated Al2O3 particles. It was concluded that irrespective of the type and diameter of the particles, air-abrasion produced t®m phase transformation, increased the roughness and changed the elemental composition of the three Y-TZP dental ceramics. Lava Plus also behaved similarly to the conventional Y-TZP ceramics, indicating that this high translucency ceramic could be more suitable to build monolithic ceramic restorations in the aesthetic restorative dentistry field.
Resumo Este estudo avaliou o efeito da abrasão a ar na transformação de fase t®m, na rugosidade, topografia e composição elementar de três cerâmicas Y-TZP (Zircônia tetragonal policristalina estabilizada por ítrio): duas convencionais (Lava Frame e ZirCad) e uma de alta translucidez (Lava Plus). Placas obtidas de blocos sinterizados de cada cerâmica foram divididos em quatro grupos: AS (pré-sinterizado); 30 (jateamento com partículas de Al2O3 de 30 mm cobertas com Si); 50 (jateamento com partículas de Al2O3 de 50 mm) e 150 (jateamento com partículas de Al2O3 de 150 mm). Após os tratamentos, as placas foram submetidas à difratometria de Rx, perfilometria 3-D e microscopia eletrônica de varredura com espectroscopia de energia dispersiva de Rx (SEM/EDS). As superfícies pré-sinterizadas apresentaram predominantemente Zr e fase tetragonal. Todos os tratamentos superficiais produziram transformação t®m nas cerâmicas avaliadas. A topografia e a rugosidade foram influenciadas pelo diâmetro das partículas abrasivas (150>50>30>AS). A análise através de SEM mostrou que os três tratamentos produziram fendas retentivas nas superfícies das cerâmicas, por influência do tamanho das partículas. A análise através de EDS mostrou uma diminuição da concentração de Zr, paralela ao surgimento de O e Al, após o jateamento. No grupo tratado com partículas de Al2O3 de 30 mm cobertas com Si foi também observado um aumento de Si após o jateamento. Concluiu-se que, independente do tipo e do diâmetro das partículas, o jateamento produziu transformação t®m, aumentou a rugosidade e alterou a composição elementar das cerâmicas avaliadas. A Lava Plus apresentou comportamento semelhante às cerâmicas convencionais, indicando que esta cerâmica de alta translucidez pode ser mais adequada à confecção de restaurações monolíticas no campo da odontologia estética restauradora.
Assuntos
Cerâmica , Materiais Dentários , Espectrometria por Raios X , Difração de Raios X , Teste de Materiais , Microscopia Eletrônica de Varredura , ArRESUMO
O aumento no número de pacientes adultos tem trazido desafios para os ortodontistas que, eventualmente, se deparam com a necessidade de colar bráquetes em superfície de porcelana. O objetivo do presente estudo foi avaliar a resistência de adesão e o índice de remanescente adesivo de bráquetes colados em superfície de porcelana e determinar quais os protocolos apresentam melhor resistência de união para o uso clínico. Foram produzidos 40 corpos de prova, reproduzindo a superfície vestibular de um incisivo central superior e, posteriormente, divididos em 4 grupos, aplicando os seguintes protocolos: Grupo I: Asperização da superfície com broca, ácido fluorídrico a 10%, silano e resina; Grupo II: Asperização com broca, aplicação de ácido fluorídrico a 10%, adesivo e resina; Grupo III: Aplicação de ácido fluorídrico a 10%, silano e resina e Grupo IV: Asperização com broca, aplicação de ácido fosfórico a 37%, silano e resina. Os corpos de prova foram submetidos ao teste de cisalhamento em uma máquina de ensaio universal. Após a descolagem dos acessórios, o índice de remanescente adesivo (IRA) foi determinado utilizando uma lupa estereoscópica e a superfície dos corpos de prova foi avaliada no MEV. De acordo com os resultados obtidos, verificou-se que não houve diferença estatisticamente significante entre os protocolos testados para colagem em porcelana. Com relação ao índice de remanescente adesivo, também não houve diferença estatisticamente significante. Concluiu-se que todos os protocolos apresentaram resistência de união ao cisalhamento compatível para uso clínico...
The widespread increase in the number of adult patients has posed daunting challenges for orthodontists, who are occasionally faced with the need to bond brackets to porcelain surfaces. The aim of this study was to evaluate the shear bond strength and adhesive remnant index of brackets bonded to porcelain surfaces, and determine what protocols offer a better bond strength in clinical practice. Forty specimens were fabricated reproducing the labial surface of a maxillary central incisor and then divided into 4 groups by applying the following protocols: Group I: Surface roughening with a drill, hydrofluoric acid at 10%, silane and resin; Group II: Surface roughening with a drill, application of hydrofluoric acid at 10%, orthodontic adhesive and resin; Group III: Application of hydrofluoric acid at 10%, silane and resin; and Group IV: Surface roughening with a drill, application of phosphoric acid at 37%, silane and resin. The samples were subjected to shear bond strength tests with a universal testing machine. After bracket removal, the adhesive remnant index (ARI) was determined using a stereoscopic microscope, and the surface of the specimens was evaluated with SEM. The results disclosed no statistically significant difference between the protocols tested for bonding to porcelain. There was no statistically significant difference in the adhesive remnant index. It was concluded that all protocols presented adequate shear bond strength for clinical use...
Assuntos
Humanos , Colagem Dentária , Porcelana Dentária , Braquetes OrtodônticosRESUMO
O presente estudo, in vitro, teve como objetivo a análise qualitativa do bordo de restaurações cerâmicas, à base de dissilicato de lítio cimentadas sobre dentes bovinos, simulando as coberturas parciais laminadas ultra finas conhecidas como Fragmentos Cerâmicos . Variou-se a presença ou não de preparo dentário, confeccionado com ponta diamantada esférica e dois protocolos distintos para o acabamento e o polimento, sendo eles: Protocolo 1, acabamento com ponta diamantada e borracha abrasiva e polimento com borrachas abrasivas, e o Protocolo 2, acabamento e polimento com borrachas abrasivas. Foram realizadas imagens geradas por microscopia eletrônica de varredura, e organizadas em pranchas para serem analisadas por escores pelos avaliadores, considerando os seguintes parâmetros: presença de trincas, regularidade dos bordos, superfície e adaptação das restaurações. Os dados obtidos a partir das análises qualitativas das imagens foram tratados estatisticamente pelo teste de Kruskal-Wallis com nível de significância de 5%. Os dados obtidos da medida de tempo (segundos) necessária para avaliação dos dois protocolos de acabamento e polimento foram analisados estatisticamente pelo teste t de Student com nível de significância de 5%. Após análise dos resultados, foi possível concluir que não houve influência do preparo do esmalte (P>0,05), não apresentando diferença estatisticamente significantiva. Assim como não houve diferença estatisticamente significativa entre os dois protocolos de acabamento e polimento quanto aos parâmetros avaliados (P>0,05). No entanto, é possível afirmar que houve diferença estatisticamente significativa entre o tempo necessário para realização dos dois protocolos (P<0,05), sendo que o protocolo 2 apresentou menor tempo clínico(AU)
The present in vitro study aimed the qualitative analysis of marginal ceramic restorations based on lithium disilicate cemented over bovine teeth, mimicking the partial ultra thin laminated coverage restorations known as Sectional Veneers. We varied the presence or absence of tooth preparation, made with a cilindric diamond bur and two distinct protocols for finishing and polishing, as follows: Protocol 1, finish with a diamond bur and abrasive rubber and polishing with abrasive rubbers, and Protocol 2 , finishing and polishing with abrasive rubbers. Images generated by scanning electron microscopy were performed, and arranged in boards to be analyzed by the evaluators by scores under the following parameters: presence of cracks, marginal regularity, surface and marginal adaptation of the restoration. The data obtained from the qualitative analyzes of the images were statistically analyzed using the Kruskal-Wallis test with a significance level of 5%. The data obtained from the measurement of time (seconds) required for the evaluation of two protocols for finishing and polishing were statistically analyzed by Student's t test with significance level of 5%. After analyzing the results, it was concluded that there was no influence of the preparation of the enamel (P>0,05). There was not a statistically signifcant difference. As there was no statistically significant difference between the two finishing and polishing protocols according to the parameters evaluated (P>0,05). However, it is clear that there was a statistically significant difference between the time required for performance of the two protocols (P<0,05). We concluded that protocol 2 showed less clinical time(AU)
Assuntos
Animais , Bovinos , Cerâmica , Esmalte Dentário , Polimento Dentário , Restauração Dentária Permanente , Lítio , Fatores de Tempo , Técnicas In Vitro , Microscopia Eletrônica de VarreduraRESUMO
Ceramics have been widely used for esthetic and functional improvements. The resin cement is the material of choice for bonding ceramics to dental substrate and it can also dictate the final esthetic appearance and strength of the restoration. The correct use of the wide spectrum of resin luting agents available depends on the dental tooth substrate. This article presents three-year clinical results of a 41 years old female patient B.H.C complaining about her unattractive smile. Two all-ceramic crowns and two laminates veneers were placed in the maxillary incisors and cemented with a self-adhesive resin luting cement and conventional resin luting cement, respectively. After a three-year follow-up, the restorations and cement/teeth interface were clinically perfect with no chipping, fractures or discoloration. Proper use of different resin luting cements shows clinical appropriate behavior after a three-year follow-up. Self-adhesive resin luting cement may be used for cementing all-ceramic crowns with high predictability of success, mainly if there is a large dentin surface available for bonding and no enamel at the finish line. Otherwise, conventional resin luting agent should be used for achieving an adequate bonding strength to enamel.
RESUMO
This study investigated the influence of ceramic compositions on Knoop Hardness Number (KHN) immediately and 24 h after polymerization and the effect of activation modes on the KHN of a resin cement. Ten Panavia F 2.0 resin cement discs were activated either directly using curing light, or chemically without light, or through 1.2-thick ceramic discs. The following ceramics were evaluated: Duceram, Cergogold, IPS Empress, IPS Empress 2, Procera, Cercon, In Ceram Alumina and In Ceram Zirconia. The KHN was obtained immediately and after 24-h testing time. Two-way ANOVA and Tukey's test were performed for statistical analysis (p<0.05). Direct activation showed higher KHN than activation through ceramics and chemical activation for both immediate and 24-h post activation. The KHN for 24-h post activation time was higher than that of the immediate post activation time except for the direct activation mode. The glass and di-silicate based ceramics showed higher KHN than alumina- and zirconia-based ceramics, immediately and after 24-h. The reinforced and opaque ceramics had the lowest KHN. The ceramic composition resulted in light attenuation, lower polymerization and lower KHN, and the 24-h testing time promoted an improvement of KHN except for direct activation mode.
Este estudo investigou a influência de composições de cerâmica no número de dureza Knoop (KHN), imediatamente e 24 h após a polimerização; e o efeito de modos de ativação na KHN de um cimento resinoso. Dez discos de cimento resinoso Panavia F 2.0 foram ativados diretamente usando uma fonte de luz, ou quimicamente sem luz, ou através de discos de cerâmica com espessura de 1,2 mm. As cerâmicas avaliadas foram Duceram, Cergogold, IPS Empress, IPS Empress 2, Procera, Cercon, In Ceram Alumina e In Ceram Zirconia. O KHN foi obtido nos tempos imediatamente e após 24 h. Os testes ANOVA two-way e Tukey foram realizados para a análise estatística (p<0,05). A ativação direta apresentou maiores KHN que a ativação através das cerâmicas e ativação química, para ambos os tempos testados imediatamente e após 24 h. O KHN para o tempo de ativação testado após 24 h foi superior que o tempo imediatamente, exceto para o modo de ativação direto. As cerâmicas à base de vidro e di-silicato apresentaram KHN superiores que as cerâmicas à base de alumina e zircônia, imediatamente e após 24 h. As cerâmicas mais reforçadas e opacas resultaram um dos menores KHN. A composição da cerâmica resulta em atenuação de luz, menor polimerização e menor KHN; e o tempo de 24 h testado promove uma melhora no KHN, exceto para o modo de ativação direto.
Assuntos
Humanos , Porcelana Dentária/química , Dureza , Cura Luminosa de Adesivos Dentários , Cimentos de Resina/química , Autocura de Resinas Dentárias , Análise de Variância , Porcelana Dentária/efeitos da radiação , Testes de Dureza , Teste de Materiais , Cimentos de Resina/efeitos da radiação , Estatísticas não ParamétricasRESUMO
O objetivo deste estudo foi investigar o efeito do processamento por injeção (método da cera perdida) na resistência à flexão, em três pontos, de porcelanas feldspáticas convencionalmente obtidas por sinterização. Foram avaliadas as porcelanas Ceramco-2, Duceragold, Duceram-Plus, Excelsior, Omega-900, Symbio, Vitadur-Alpha e VMK-95. Como controle, foi também utilizada a porcelana Cergogold, fornecida na forma de pastilhas pré-sinterizadas e processada exclusivamente por injeção. Corpos de prova em forma de barra (n = 10), com dimensões de 25 × 5 × 2 mm (ISO-6872), foram confeccionados em matrizes metálicas e processados, por sinterização ou injeção, nas temperaturas de cocção indicadas pelos fabricantes. Os ensaios foram realizados em equipamento MTS-810 (Material Test System, EUA), com célula de carga de 10 kN e velocidade de 0,5 mm.min-1. Os resultados, submetidos à análise de variância (p menor ou igual a 0,05), mostraram que o processamento por injeção foi capaz de proporcionar maior resistência à fexão para as porcelanas Duceram-Plus, Excelsior, Omega-900, Symbio e VMK-95 (p < 0,001). Nessa mesma condição experimental, a porcelana Cergogold mostrou-se estatisticamente superior apenas à porcelana Vitadur-Alpha, sendo inferior à porcelana Omega-900 e semelhante às demais (p < 0,001). A resistência à fexão das porcelanas Ceramco-2, Duceragold e Vitadur-Alpha não foi influenciada pelo processo de obtenção (p < 0,001).
The aim of this study was to evaluate the effect of injection process, on the three-point flexural strength on feldspathic ceramic, fabricated by sintering technique. The ceramics evaluated were Duceragold, Duceram Plus, Excelsior, Omega 900, Symbio,Vitadur Alpha, VMK 95 and Ceramco 2. Cergogold, that the processing technique is based on a conventional injection moulding, was used for control. The bar-shaped specimens (n = 10) with the size of 25 × 5 × 2 mm (ISO-6872) were fabricated in a metal mould and processed by injection or sinterized, according to manufacturing specifcations. The fexural test was performed in a MTS 810 testing machine (Material Test System, USA), with a 10 kN load cell and a crosshead speed of 0.05 mm.min-1. The data (MPa) were subjected to analysis of variance (p less than or equal to 0.05), and showed that the injection processed enhance the flexural strength of Duceram-Plus, Excelsior, Omega-900, Symbio and VMK-95 (p < 0.001). In this experimental condition, the ceramic Cergogold showed high value than Vitadur-Alpha, was inferior to the ceramic Omega-900, but there were no signifcant difference with the others (p < 0.001). The flexural strength was not influenced by the processing method for the ceramics Ceramco-2, Duceragold and Vitadur-Alpha.
Assuntos
Cerâmica , Resistência à Flexão , Injeções , Adaptação Marginal Dentária , Porcelana Dentária , Teste de MateriaisRESUMO
The aim of this study was to evaluate the Knoop hardness after 15 min and 24 h of different shades of a dual-cured resin-based cement after indirect photoactivation (ceramic restoration) with 2 light-curing units (LCUs). The resin cement Variolink II (Ivoclar Vivadent) shade XL, A2, A3 and opaque were mixed with the catalyst paste and inserted into a black Teflon mold (5 mm diameter x 1 mm high). A transparent strip was placed over the mold and a ceramic disc (Duceram Plus, shade A3) was positioned over the resin cement. Light-activation was performed through the ceramic for 40 s using quartz-tungsten-halogen (QTH) (XL 2500; 3M ESPE) or light-emitting diode (LED) (Ultrablue Is, DMC) LCUs with power density of 615 and 610 mW/cm2, respectively. The Koop hardness was measured using a microhardness tester HMV 2 (Shimadzu) after 15 min or 24 h. Four indentations were made in each specimen. Data were subjected to ANOVA and Tukey's test (a=0.05). The QTH LCU provided significantly higher (p<0.05) KHN values than the LED LCU. When the post-cure times were compared for the same shade, QTH and LED at 24 h provided significantly higher (p<0.05) KHN values than at 15 min. It may be concluded that the Knoop hardness was generally dependent on the LCU and post-cure time. The opaque shade of the resin cement showed lower Knoop hardness than the other shades for both LCUs and post-cure times.
Este estudo avaliou a dureza Knoop após 15 min e 24 h de diferentes cores do cimento resinoso dual após fotoativação indireta com 2 fontes de luz. O cimento resinoso Variolink II (Ivoclar Vivadent) nas cores XL, A2, A3 e opaco foram misturados com a pasta catalisadora e inseridos dentro de um molde de teflon preto com (5 mm de diâmetro x 1 mm de espessura). A tira de poliéster transparente foi inserida sobre o molde e um disco da cerâmica (Duceram Plus, cor A3) foi posicionada sobre o cimento resinoso. A fotoativação foi realizada sobre o disco de cerâmica por 40 s usando a lâmpada de luz halógena (XL 2500, 3M ESPE) ou luz emitida por diodo (LED) com intensidade de luz de 615 e 610 mW/cm2. A dureza Knoop foi medida usando o microdurômetro HMV 2 (Shimadzu) com carga de 50 g por 15 s, após 15 min e 24 h. Quatro indentações foram feitas em cada amostra. Os dados foram submetidos à Análise de Variância e ao teste de Tukey (a=5 por cento). A fonte de luz halógena promoveu valores de dureza significantemente maiores (p<0,05) que o LED. Quando os tempos pós-polimerização foram comparados para a mesma cor, a luz halógena e o LED promoveram valores de dureza significantemente maiores (p<0,05) em 24 h do que aos 15 min. Pode-se concluir que, de maneira geral, a dureza Knoop foi dependente da fonte de luz e do tempo pós-polimerização. A cor opaca do cimento resinoso mostrou menores valores de dureza Knoop que as outras cores para ambas as fontes de luz e tempos pós-polimerização.
Assuntos
Lâmpadas de Polimerização Dentária , Porcelana Dentária , Cura Luminosa de Adesivos Dentários , Cimentos de Resina , Análise de Variância , Análise do Estresse Dentário , Dureza , Teste de Materiais , Cimentos de Resina/química , Cimentos de Resina/efeitos da radiação , Estatísticas não Paramétricas , Fatores de TempoRESUMO
O objetivo deste trabalho foi avaliar, por meio de ensaios de resistência à flexão, em três pontos, e de dureza, o comportamento mecânico das porcelanas feldspáticas Duceram Plus, Excelsior, Duceragold, Symbio, VMK, Omega 900 e Vitadur Alpha, submetidas a dois métodos de processamento laboratorial: sinterização convencional (fabricantes) e por injeção a vácuo (experimental). Foram confeccionadas dez amostras de cada grupo experimental para o ensaio de resistência à flexão (em forma de barra, 25mm de comprimento, 5mm de largura, 2mm de espessura - ISO 6872). Os testes foram realizados em equipamento MTS 810 (Material Test System, EUA), com célula de carga de 10kN e velocidade de 0,5mm/minuto, gerenciado por programa Test Star II (IBM, EUA). Para o ensaio de dureza, na escala Vickers, cinco fragmentos de cada grupo foram incluídos em resina acrílica autopolimerizável, polidos e submetidos ao teste em durômetro Buheler (EUA), com carga de 300gf, por 30 segundos. As cerâmicas Duceram Plus, Excelsior, Omega 900, Symbio e VMK 95 apresentaram maior resistência à flexão quando processadas por injeção. Os materiais Ducera Gold e Vitadur Alpha não sofreram qualquer influência deste método de processamento. O processo de injeção a vácuo, experimental, não alterou a dureza dos materiais estudados
The aim of this study was to compare the flexural strength and hardness of seven feldspatic ceramics (Duceram Plus, Excelsior, Duceragold, Symbio, VMK, Omega 900 and Vitadur Alpha) processed by convencional fusing and heat-pressing. Ten especimens were made for flexural test (25mm length; 5mm width; 2mm thick - ISO 6872). The tests were realized in a MTS 810 machine (Material Test System - USA), with a 10kN load cell and crosshead-speed of 0.5mm/minute, managed by Test Star II software (IBM, USA). Five samples of each ceramic were included in autocured resin JET (Artigos odontológicos Clássico, Brazil), polished and submitted to Vickers hardness test in duromer Buheler (USA), with load of 300gf, for 30 seconds. Results showed that the ceramics Duceram Plus, Excelsior, Omega 900, Symbio and VMK 95 presented higher flexural stengths values when heat-pressed. Ducera Gold and Vitadur Alpha flexural stengths values weren´t affected by the processing method. Processing method (convencional fusing and heat-pressed) did not influenced the hardness of materials evaluated