RESUMO
OBJECTIVES: To assess the discoloration of teeth treated with the different phases of calcium aluminate cement (CAC), in comparison with the conventional CAC and mineral trioxide aggregate (MTA). MATERIALS AND METHODS: Fifty bovine incisors were prepared and filled. Two millimeters of the filling was removed to fabricate a cervical plug with the following cements (n=10): CA(CaO.Al2 O3 ); CA2 (CaO.2Al2 O3 ); C12 A7 (12CaO.7Al2 O3 ); CAC and MTA. The initial color measurement was performed and after 7, 15, 30, 45, 90, 180, and 365 days new color measurements were performed to determine the color (ΔE00 ), lightness (ΔL'), chroma (ΔC'), hue differences (ΔH'), and the whiteness index (WID ). RESULTS: ΔE00 was significant for groups (p = 0.036) and periods (p < 0.05). The greater ΔE00 was observed after 365 days for CAC (12.8). C12 A7 (7.2) had the smallest ΔE00 . ΔL' and ΔC' were significant for groups and periods (p < 0.05). ΔH' was significant for periods (p < 0.05). After 365 days, significant reduction in lightness was observed for all groups. For CA, CA2 , CAC, and MTA groups, the WID values decreased over time (p < 0.05). CONCLUSIONS: The tested cements changed the color behavior of the samples, resulting in greater teeth darkening over time. CLINICAL SIGNIFICANCE: There is no long-term study assessing the discoloration induced by the different phases of CAC.