RESUMO
A zinc hydroxide nitrate (ZHN), Zn5(OH)8(NO3)2.2H2O, and a layered double hydroxide (LDH), Zn/Al-NO3 were doped with 0.2 mol% of Cu2+ during alkaline chemical precipitation. Both compounds were intercalated with adipate ((-)OOC(CH2)4COO(-)), azelate ((-)OOC(CH2)7COO(-)), and benzoate (C6H5COO(-)) ions through ion exchange reactions. Solid state 13C nuclear magnetic resonance spectroscopy showed only one signal of carboxylic carbon for adipate and azelate intercalated into LDH, indicating that the carboxylic ends of both acids were equivalent, whereas the signal split when the intercalation was into the ZHN matrix. The electron paramagnetic resonance (EPR) spectrum of copper in octahedral cation sites of LDH layers showed a Hamiltonian parameter ratio g ||/A ||=170 cm and, after intercalation of adipate, the change was not significant: g ||/A ||=174 cm. This result indicates that the carboxylate ions did not coordinate with copper centers. Nonetheless, the intercalation of azelate increased the ratio to g ||/A ||=194 cm, similar to the spectra of ZHN modified with adipate, g ||/A ||=199 cm, and azelate, g ||/A ||=183 and 190 cm, which are associated with the coordination of copper by weak carboxylate anion ligands. Copper occupies octahedral or tetrahedral sites in ZHN layers, and the EPR spectra indicate that the dicarboxylate anions reacted preferentially with octahedral sites, whereas benzoate reacted with both sites.
RESUMO
The intercalation of ions derived from succinic, glutaric, and adipic acid into layered zinc hydroxide nitrate by ionic exchange reaction is reported. Different reaction conditions are investigated and the materials are characterized by powder X-ray diffraction, Fourier transform infrared spectroscopy, thermal analysis (simultaneous thermogravimetry and differential scanning calorimetry) and elemental analysis. The dicarboxylic acids can be grafted to the matrix slab by one carboxylate group and the second hydrated carboxylate group is hanging between the layers. Benzoate ions have also been intercalated by both ionic exchange reaction and stirring in acetonitrile. The two benzoate-intercalated materials exchange the organic moiety by sulfate ions if stirred in magnesium sulfate solution, but the sample obtained by anion exchange also allows the unusual incorporation of neutral magnesium sulfate in addition to free solvated sulfate ion. A schematic arrangement of the intercalated species between the layers is presented.