RESUMO
The specificity of activated carbon (AC) can be targeted by pretreatment of the precursors and/or activation conditions. Piassava (Leopoldinia piassaba and Attalea funifera Martius) are fibrous palms used to make brushes, and other products. Consolidated harvest and production residues provide economic feasibility for producing AC, a value-added product from forest and industrial residues. Corona electrical discharge and extraction pretreatments prior to AC activation were investigated to determine benefits from residue pretreatment. The resulting AC samples were characterized using elemental analyses and FTIR and tested for efficacy using methylene blue and phenol. All resulting AC had good adsorbent properties. Extraction as a pretreatment improved functionality in AC properties over Corona electrical discharge pretreatment. Due to higher lignin content, AC from L. piassaba had better properties than that from A. funifera.
RESUMO
This paper provides proof of concept that activated carbon (AC) may be readily produced using limited conversion methods and resources from sawdust of massaranduba (Manilkara huberi) wood, thereby obtaining value-added products. Sawdust was sieved and heat-treated in an oxygen-free muffle furnace at 500 °C to produce charcoal. The charcoal was activated in a tubular electric furnace at 850 °C while being purged with CO2 gas. Microstructural, thermal and physical properties of the three components: sawdust, charcoal and AC were compared by means of field emission scanning electron microscopy (FESEM), X-ray diffractometry (XRD), thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), density and water adsorption/desorption measurements. The resulting AC had a large surface area as measured by Brunauer-Emmett-Teller (BET) comparable to other such values found in the literature. The large surface area was due to pore development at the microstructural level as shown by FESEM. XRD illustrated that sawdust had a semi-crystalline structure whereas charcoal and AC evidenced mostly amorphous structures. TGA and DSC showed that AC had high reactivity to moisture compared to sawdust and charcoal.
RESUMO
The objective of this work was to prepare bio-based thin films and evaluate the additions of magnetite and glycerol on the physico-chemical (flexibility, wettability and barrier properties) and dielectric properties of cellulose/chitosan-based films. The films were prepared by solution casting and presented a suitable dispersion of the constituents observed by SEM and FTIR. The films were thermally stable up to 150 °C and had a higher flexibility, wettability and lower barrier properties upon addition of glycerol. The calculated dielectric constant (εr) for the composite films was based on measurements of capacitance, at 100 and 1000 Hz, with the additions of magnetite and glycerol more than doubling the εr increasing the charge storage capacity. The bio-based thin films have potential to be used as insulators in capacitors on the production of green electronics thus, reducing toxic and nonrenewable e-waste generation.
Assuntos
Celulose/química , Óxido Ferroso-Férrico/química , Nanofibras/química , Quitosana/química , Módulo de Elasticidade , Capacitância Elétrica , Glicerol/química , Química Verde/instrumentação , Fenômenos Magnéticos , Resistência à Tração , MolhabilidadeRESUMO
Coir fibers received three treatments, namely washing with water, alkali treatment (mercerization) and bleaching. Treated fibers were incorporated in starch/ethylene vinyl alcohol copolymers (EVOH) blends. Mechanical and thermal properties of starch/EVOH/coir biocomposites were evaluated. Fiber morphology and the fiber/matrix interface were further characterized by scanning electron microscopy (SEM). All treatments produced surface modifications and improved the thermal stability of the fibers and consequently of the composites. The best results were obtained for mercerized fibers where the tensile strength was increased by about 53% as compared to the composites with untreated fibers, and about 33.3% as compared to the composites without fibers. The mercerization improved fiber-matrix adhesion, allowing an efficient stress transfer from the matrix to the fibers. The increased adhesion between fiber and matrix was also observed by SEM. Treatment with water also improved values of Young's modulus which were increased by about 75% as compared to the blends without the fibers. Thus, starch/EVOH blends reinforced with the treated fibers exhibited superior properties than neat starch/EVOH.