RESUMO

The aim of this study was to assess bond strength of fiberglass posts to root canal dentin irradiated with a 980 nm diode laser at different parameters of power and frequency. Fifty human maxillary canines were separated into five groups (n = 10) according to the following parameters of laser power and frequency: Group 1 (1.5 W/100 Hz), Group 2 (1.5 W/continuous wave [CW]), Group 3 (3.0 W/100 Hz), Group 4 (3.0 W/CW), and Group 5 (no irradiation). Following post cementation, samples underwent a push-out test (0.5 mm/min); next, fracture analysis was performed with a light microscope at 50x and 100x magnification. All of the irradiated groups had increased bond strength values compared to the nonirradiated group. Groups 1 and 2 demonstrated the highest bond strength values; however, statistically significant differences were observed for only the cervical third of Group 4 and the cervical/apical thirds of Group 5. Fracture analysis showed a predominance of mixed failures for Groups 1 and 2 and adhesive failures between dentin and cement for the other groups.

Assuntos

Colagem Dentária , Cavidade Pulpar/efeitos da radiação , Dentina/efeitos da radiação , Vidro/química , Lasers Semicondutores , Técnica para Retentor Intrarradicular/instrumentação , Adesividade , Bis-Fenol A-Glicidil Metacrilato/química , Cimentação/métodos , Cerâmica/química , Dente Canino/efeitos da radiação , Dente Canino/ultraestrutura , Cimentos Dentários/química , Cavidade Pulpar/ultraestrutura , Análise do Estresse Dentário/instrumentação , Dentina/ultraestrutura , Resinas Epóxi/química , Humanos , Teste de Materiais , Polietilenoglicóis/química , Ácidos Polimetacrílicos/química , Quartzo/química , Doses de Radiação , Cimentos de Resina/química , Preparo de Canal Radicular/métodos , Silanos/química , Estresse Mecânico , Propriedades de Superfície , Ápice Dentário/efeitos da radiação , Ápice Dentário/ultraestrutura , Colo do Dente/efeitos da radiação , Colo do Dente/ultraestrutura