RESUMO

Aim: The use of chemical agents in the surface treatment of glass fiber posts can improve their bond strength to the root canal. The aim of this study was to assess the bond strength and failure mode of glass fiber posts that received different surface treatments prior to silanization. Materials and Methods: In this cross-sectional and in vitro experimental study, 50 human lower premolar roots were randomly divided into five groups and subsequently prepared to receive the cementation of a fiberglass post prior to silanization. They were distributed as group 1 (with 24% hydrogen peroxide), group 2 (with 37% phosphoric acid), group 3 (with 1.23% acidulated phosphate fluoride for 2 minutes), group 4 (with 1.23% acidulated phosphate fluoride for 6 minutes), and group 5 (without pretreatment). After cementation, the roots were sectioned into two discs for each cervical, middle, and apical region. Bond strength was assessed using the push out technique. Adhesive, mixed, and cohesive failure modes were also assessed. For data analysis, ANOVA and Tukey's post hoc tests were used, as well as Pearson's chi-square test. A significance of P < 0.05 was considered in all statistical analyses. Results: When comparing the bond strength of root regions, significant differences were obtained in groups pretreated with phosphoric acid (P = 0.018) and acidulated phosphate fluoride for 2 and 6 minutes (P = 0.001 and P = 0.000, respectively). Furthermore, significant differences were obtained between posts treated only with silane and those that received phosphoric acid pretreatment (P = 0.006) and acidulated phosphate fluoride for 6 minutes (P = 0.001). Significant association of mixed failure mode was observed with hydrogen peroxide (P = 0.014) and phosphoric acid (P = 0.006) pretreatments. Cohesive failure was significantly associated with acidulated phosphate fluoride pretreatment for 2 minutes (P = 0.032) and with posts that did not receive treatment prior to silanization (P = 0.000). Conclusion: Posts treated only with silane and pretreated with hydrogen peroxide and acidulated phosphate fluoride for 2 minutes presented significantly higher bond strength with respect to those pretreated with phosphoric acid and acidulated phosphate fluoride for 6 minutes. However, acidulated phosphate fluoride for 2 minutes and silane were associated with a better bonding type.

RESUMO

The aim of this study was to evaluate the influence of different activation protocols for chelating agents used after chemo-mechanical preparation (CMP), for smear layer (SL) removal. Forty-five single-rooted human premolars with straight canals and fully formed apex were selected. The specimens were randomly divided into three groups depending on the chelating agent used for smear layer removal: distilled water (DW, control group); 17% ethylenediaminetetraacetic acid (EDTA); and 10% citric acid (CA). Each group was further divided into three subgroups according to the activation protocol used: no-activation (NA), manual dynamic activation (MDA), or sonic activation (SA). After CMP, all specimens were sectioned and processed for observation of the apical thirds by using scanning electron microscopy (SEM). Two calibrated evaluators attributed scores to each specimen. The differences between activation protocols were analyzed with Kruskal-Wallis and Mann-Whitney U tests. Friedman and Wilcoxon signed rank tests were used for comparison between each root canal third. When chelating agents were activated, either by MDA or SA, it was obtained the best cleaning results with no significant difference between EDTA and CA (P > 0.05). Sonic activation showed the best results when root canal thirds were analyzed, in comparison to MDA and NA groups (P < 0.05). The activation of chelating agents, independent of the protocol used, benefits smear layer removal from root canals.

Assuntos

RESUMO

The aim of this study was to evaluate the antimicrobial activity of Uncaria tomentosa (Willd.) DC (cat's claw) against Enterococcus faecalis, Staphylococcus aureus, and Candida albicans. Suspensions with 10(8) cells/ml of each microorganism were plated in triplicate on Mueller-Hinton agar. Wells in the agar were made and filled with 2% chlorhexidine (CHX) gel, 2% cat's claw (CC) gel, 2% CHX+CC, and 1% hydroxyethylcellulose (NAT) gel. Inhibition halos were measured after 24 h at 37°C and differences were analyzed using one-way ANOVA. The mean diameter of the microbial growth inhibition zones of 2% CHX+CC against the tested microbial strains ranged from 21.7 to 33.5 mm. This was the most effective substance against E. faecalis and C. albicans, followed by CHX and CC. Against S. aureus, CHX+CC, CHX, and CC showed similar antimicrobial activity (P > 0.05). The results indicate that all the investigated compounds had antimicrobial activity against microorganisms frequently found in infected root-filled teeth.

Assuntos