RESUMO
BACKGROUND: Dual mobility (DM) articulations were introduced for total hip arthroplasty to reduce the risk of instability for patients who have a high risk of dislocation. The use of DM constructs in both primary and revision total hip arthroplasty has been steadily increasing, leading to concerns regarding potential risks of fretting corrosion, polyethylene wear, metal release, and failure due to component positioning. METHODS: A total of 56 retrieved DM constructs were collected. The inner and outer polyethylene liner surfaces were assessed for 7 damage mechanisms, and fretting corrosion was evaluated for the femoral stem, head, and modular liner. Three polyethylene liners with the greatest amounts of embedded debris were examined using scanning electron microscopy. Energy-dispersive X-ray spectroscopy was used to determine the elemental content of the debris. Acetabular cup orientation was analyzed radiographically using the EBRA (Einzel-Bild-Roentgen-Analyse) method. RESULTS: The devices were revised most frequently for infection (36%), loosening (21%), and instability/dislocation (18%). The most common polyethylene damage mechanisms were scratching, pitting, burnishing, and embedded debris, and no difference in total damage was found between primary and revision cases. Scanning electron microscopy/energy-dispersive X-ray spectroscopy revealed that debris morphology and composition were consistent with porous titanium coating, resulting from cup loosening or broken screws and augments. A total of 71% and 50% of the constructs were determined to be within the Lewinnek safe zone for inclination and anteversion, respectively. CONCLUSION: The most notable mechanisms of surface damage were due to third-body debris, especially for the polyethylene surfaces which articulate against cobalt-chromium femoral heads and acetabular liners. Scratching of the femoral head and the metal liner from this debris may support the clinical use of ceramic for DM bearing surfaces in the future.
Assuntos
Artroplastia de Quadril , Prótese de Quadril , Artroplastia de Quadril/efeitos adversos , Corrosão , Prótese de Quadril/efeitos adversos , Humanos , Polietileno , Desenho de Prótese , Falha de PróteseRESUMO
BACKGROUND: In order to improve oxidation resistance, antioxidants such as vitamin-E are added to polyethylene used in the bearing surfaces of orthopedic components. Currently, little is known about the efficacy of this treatment in vivo. This study therefore reports on the reasons for revision, surface damage mechanisms, and oxidation of retrieved vitamin E-stabilized highly crosslinked polyethylene (HXLPE) for total knee arthroplasty. METHODS: We examined 103 retrieved knee inserts fabricated from vitamin E (VE)-stabilized HXLPE and 67 fabricated from remelted HXLPE as a control. The implantation times were 1.2 ± 1.3 and 1.5 ± 1.3 years for the VE and control cohorts, respectively. The inserts were evaluated for 7 surface damage mechanisms using a semiquantitative scoring method and analyzed for oxidation using Fourier-transform infrared spectroscopy. Reasons for revision were also assessed using operative notes created at time of retrieval. RESULTS: Both groups were revised primarily for instability, infection, and loosening. Burnishing, pitting, and scratching were the most common damage mechanisms observed, with the VE cohort demonstrating less surface damage than the control. Measured oxidation for the cohort was low, with a median oxidation index of 0.09 ± .05 for the articulating surface, 0.05 ± 0.06 for the backside, 0.08 ± 0.06 for the anterior/posterior surfaces, and 0.08 ± 0.05 for the stabilizing post. As compared to the control cohort, oxidation tended to be less for the VE group at the articulating (P < .001) and backside (P = .003) surfaces, although the median differences were minimal and may not be clinically significant. CONCLUSION: The results indicate positive fatigue damage resistance and oxidation resistance for the retrieved VE-stabilized total knee arthroplasty inserts.
Assuntos
Antioxidantes/farmacologia , Prótese do Joelho , Polietileno/química , Falha de Prótese/etiologia , Vitamina E/farmacologia , Idoso , Artroplastia do Joelho/instrumentação , Feminino , Humanos , Articulação do Joelho/cirurgia , Masculino , Pessoa de Meia-Idade , Oxirredução , Desenho de Prótese , Espectroscopia de Infravermelho com Transformada de FourierRESUMO
BACKGROUND: Clinical concern exists regarding fretting corrosion and material loss from taper junctions in orthopedic devices, with previous research focusing on the modular components from total hip arthroplasty. Comparatively little has been published regarding the fretting corrosion and material loss in modular knee devices. The purpose of this study is to evaluate fretting corrosion damage and quantify material loss for conical total knee arthroplasty taper interfaces. METHODS: Stem tapers of 166 retrieved modular knee devices were evaluated for fretting corrosion using a semiquantitative scoring method. High precision profilometry was then used to determine volumetric material loss and maximum wear depth for a subset of 37 components (implanted for 0.25-18.76 years). Scanning electron microscopy and energy-dispersive X-ray spectroscopy were used to characterize the observed damage. RESULTS: Mild to severe fretting corrosion was observed on the majority of tapers, with 23% receiving a maximum visually determined damage score of 4. The median rate of volumetric material loss was 0.11 mm3/y (range 0.00-0.76) for femoral components (both cone and bore taper surfaces combined) and 0.01 mm3 (range 0.00-8.10) for tibial components. Greater rates of material loss were associated with mixed metal pairings. There was a strong correlation between visual fretting corrosion score and calculated material loss (ρ = 0.68, P < .001). Scanning electron microscopy revealed varying degrees of scratching, wear, fretting corrosion, and instances of cracking with morphology not consistent with fretting corrosion, wear, or fatigue. CONCLUSION: Although visual evidence of fretting corrosion damage was prevalent and correlated with taper material loss, the measured volumetric material loss was low compared with prior reports from total hip arthroplasty.