In this study, the steel manufacturing waste Basic Oxygen Furnace Sludge (BOFS) was tested as permeable reactive material for the remediation of soil contaminated with chromium. The material presents a high content of elemental iron and iron oxides typical of the steel manufacturing process. Here we propose a scheme of the chemical reactions responsible for remediation process including BOFS dissolution, Cr(VI) reduction and Cr(III) precipitation. Batch reactors showed that Cr(VI) removal increases as the pH decreases. Column tests demonstrated that the simulated PRB with BOFS as the reactive media was quite effective for removing Cr(VI) from groundwater, with a sorption capability of 0.213â¯mg Cr per gram of BOFS at an initial Cr(VI) concentration of 50â¯mgâ¯L-1 at pH 5.5. A long-term test lasting 71 days confirmed the proposed mechanisms and the suitability of using BOFS in a permeable reactive barrier.
RESUMO
Recent research on novel cost-effective adsorbent materials suggests potential use of industrial wastes for effluent treatment, with the added benefit of reuse of the wastes. Waste steel materials, including blast oxygen furnace sludge (BOFS), blast furnace sludge (BFS), and blast furnace dust (BFD), were investigated as low-cost adsorbents for removal of an oil emulsion and RR195 dye. The residues were characterized by X-ray diffraction, Brunauer-Emmett-Teller area, volume and distribution of pore diameters, Mössbauer spectroscopy, X-ray fluorescence, granulometry, scanning electron microscopy/energy dispersive spectroscopy, and pHpzc. Adsorption kinetics data were obtained by UV-vis spectrophotometry at the maximum absorption wavelength of the dye solution and crude oil emulsion. The use of waste as an adsorbent was more efficient for treatment of the oil emulsion than the dye solution. BOFS had higher total organic carbon (TOC) removal efficiency than the other waste materials. For the RR195 dye, good color removal was observed for all adsorbents, >90 % within 24 h. TOC removal was poor, <10 % for BFD and BFS and a maximum of 37 % for BOFS. For the oil emulsion, 97 % TOC removal was obtained by adsorption onto BOFS and 87 % onto BFS.