RESUMO
This work evaluates the radiation shielding capabilities of the PLA-W composite for MV energy photons emitted by a linear accelerator and the feasibility of manufacturing a clinically-used collimator grid in spatially fractionated radiotherapy (SFRT) using the material extrusion (MEX) 3D printing technique. The PLA-W filament used has a W concentration of 93% w/w and a green density of 7.51 g/cm3, characteristics that make it suitable for this purpose. Relevant parameters such as the density and homogeneity distribution of W in the manufactured samples determine the mass attenuation coefficient, directly affecting the radiation shielding capacities, so different printing parameters were evaluated, such as layer height, deposition speed, nozzle temperature, and infill, to improve the protection performance of the samples. Additionally, physical and mechanical tests were conducted to ensure structural stability and spatial variability over time, which are critical to ensure precise spatial modulation of radiation. Finally, a complete collimator grid measuring 9.3 × 9.3 × 7.1 cm3 (consisting of 39 conical collimators with a diameter of 0.92 cm and center-to-center spacing of 1.42 cm) was manufactured and experimentally evaluated on a clinical linear accelerator to measure the radiation shielding and dosimetric parameters such as mass attenuation coefficient, half-value layer (HVL), dosimetric collimator field size, and inter-collimator transmission using radiochromic films and 2D diode array detectors, obtaining values of 0.04692 cm2/g, 2.138 cm, 1.40 cm, and 15.6%, respectively, for the parameters in the study. This shows the viability of constructing a clinically-used collimator grid through 3D printing.
RESUMO
This work reports an optimized method to experimentally quantify the Gd-nanoparticle dose enhancement generated by electronic brachytherapy. The dose enhancement was evaluated considering energy beams of 50 kVp and 70 kVp, determining the Gd-nanoparticle concentration ranges that would optimize the process for each energy. The evaluation was performed using delaminated radiochromic films and a Poly(methyl methacrylate) (PMMA) phantom covered on one side by a thin 2.5 µm Mylar filter acting as an interface between the region with Gd suspension and the radiosensitive film substrate. The results for the 70 kVp beam quality showed dose increments of 6±6%, 22±7%, and 9±7% at different concentrations of 10, 20, and 30 mg/mL, respectively, verifying the competitive mechanisms of enhancement and attenuation. For the 50 kVp beam quality, no increase in dose was recorded for the concentrations studied, indicating that the major contribution to enhancement is from the K-edge interaction. In order to separate the contributions of attenuation and enhancement to the total dose, measurements were replicated with a 12 µm Mylar filter, obtaining a dose enhancement attributable to the K-edge of 29±7% and 34±7% at 20 and 30 mg/mL, respectively, evidencing a significant additional dose proportional to the Gd concentration.
RESUMO
Fricke solution has a wide range of applications as radiation detector and dosimetry. It is particularly appreciated in terms of relevant comparative advantages, like tissue-equivalence when prepared in aqueous media like gel matrix, continuous mapping capability, independence of dose rate and incident direction, as well as linear dose response. This work presents the development and characterization of an improved Fricke gel system, based on modified chemical compositions, making possible its application in clinical radiology due to its improved sensitivity. Properties of standard Fricke gel dosimeter for high-dose levels are used as a starting point, and suitable chemical modifications are introduced and carefully investigated in order to attain high resolution for low-dose ranges, like those corresponding to radiology interventions. The developed Fricke gel radiation dosimeter system achieves the expected typical dose-dependency, showing linear response in the dose range from 20 up to 4000 mGy. Systematic investigations including several chemical compositions are carried out in order to obtain an adequate dosimeter response for low-dose levels. A suitable composition from among those studied is selected as a good candidate for low-dose-level radiation dosimetry consisting of a modified Fricke solution fixed to a gel matrix containing benzoic acid along with sulfuric acid, ferrous sulfate, Xylenol orange, and tridistilled water. Dosimeter samples are prepared in standard vials for in-phantom irradiation and further characterization by spectrophotometry measuring visible light transmission and absorbance before and after irradiation. Samples are irradiated using typical X-ray tubes for radiology and calibrated Farmer-type ionization chamber is used as reference to measure dose rates inside phantoms at vial locations. Once sensitive material composition is optimized, dose-response curves show significant improvement regarding overall sensitivity for low dose levels. The aim of this work consists of implementing the optimized gel dosimeter to perform direct measurements of absorbed dose in samples irradiated during microcomputed tomography scanning in order to preliminary assess dose levels for further scanning of small animals for further applications in veterinary and paleontology. As a first attempt, dose distributions were measured in water-equivalent phantoms having dimensions comparable to small animals, 100 to 1000 cm3, approximately. According to the obtained results, it is found that the proposed method shows satisfactory reliability and adequate performance for a promising gel dosimetry system.