RESUMO
Additive manufacturing and nanotechnology have been used as fundamental tools for the production of nanostructured parts with magnetic properties, expanding the range of applications in additive processes through tank photopolymerization. Magnetic cobalt ferrite (CoFe2O4) and barium ferrite (BaFe12O19) nanoparticles (NPs) with an average size distribution value (DTEM) of 12 ± 2.95 nm and 37 ± 12.78 nm, respectively, were generated by the hydroxide precipitation method. The dispersion of the NPs in commercial resins (Anycubic Green and IRIX White resin) was achieved through mechanochemical reactions carried out in an agate mortar for 20 min at room temperature, with limited exposure to light. The resulting product of each reaction was placed in amber vials and stored in a box to avoid light exposure. The photopolymerization process was carried out only at low concentrations (% w/w NPs/resin) since high concentrations did not result in the formation of pieces, due to the high refractive index of ferrites. The Raman spectroscopy of the final pieces showed the presence of magnetic NPs without any apparent chemical changes. The electron paramagnetic resonance (EPR) results of the pieces demonstrated that their magnetic properties were maintained and not altered during the photopolymerization. Although significant differences were observed in the dispersion process of the NPs in each piece, we determined that the photopolymerization did not affect the structure and superparamagnetic behavior of ferrite NPs during processing, successfully transferring the magnetic properties to the final 3D-printed piece.
Assuntos
Nanopartículas , Nanoestruturas , Nanopartículas/química , Cobalto/química , Compostos Férricos/química , Magnetismo , Fenômenos MagnéticosRESUMO
Since the elucidation of the leaching process by Mizoroki in the 1970s, the research focused on this problem has increased. As a result, it has been discovered that the leached metals can not only hinder product yield, but they can also remain as contaminants of the final products. Thus, it can be concluded that metal leaching needs to be diminished or avoided more efficiently. This problem is important for the industry and the environment because of the increases in costs and pollution. In 2014, we reported a brief review related to this important feature; now we would like to report on the latest findings on this important phenomenon, including an update on the mechanisms used to explain leaching and the reactions that support those mechanisms and including patents related to leaching in catalysis that have appeared in recent years.
RESUMO
The synthesis and solubility behaviors of four generation five (G5) triazine dendrimers are studied. While the underivatized cationic dendrimer is soluble in water, the acetylated and propanoylated derivatives undergo coacervation in water upon increasing temperature. Occurring around room temperature, this behavior is related to a liquid-liquid phase transition with a lower critical solution temperature (LCST) and is explained by differences in composition, notably, the hydrophobic nature of the terminal groups. Interestingly, the water solubility of the acetylated dendrimer is affected by the addition of selected metal ions. Titrating solutions of acetylated dendrimer at temperatures below the LCST with gold or palladium ions promoted precipitation, but platinum, iridium, and copper did not. Gold nanoparticles having diameters of 2.5 ± 0.8 nm can be obtained from solutions of the acetylated dendrimer at concentrations of gold less than that required to induce precipitation by treating the solution with sodium borohydride.
Assuntos
Dendrímeros/química , Metais/química , Nanopartículas , Temperatura , Triazinas/química , Microscopia Eletrônica de Transmissão , Análise Espectral/métodosRESUMO
Amphiphiles with a dendritic structure are attractive materials as they combine the features of dendrimers with the self-assembling properties and interfacial behavior of water-air affinities. We have synthesized three generations of polyester dendrimers and studied their interfacial properties on the Langmuir films. The behavior obtained was, as a rule, the lowest generation dendrimers behaving like traditional amphiphiles and the larger molecules presenting complicated isotherms. The Langmuir films of these compounds have been characterized by their surface pressure versus molecular area (π/A) and Brewster angle microscopy (BAM) observations.
RESUMO
One-step room-temperature synthesis of nanocrystalline Mn3O4 hausmannite, without heating posttreatment, was carried out from a simple dissolution of manganese(II) acetate in a mixture of N,N'-dimethylformamide (DMF) and water. Homogeneous nanocrystals like rods were obtained, with an average width and length of 6.6+/-1.2 nm and 17.4+/-4.1 nm, respectively, and a preferential growth along the 001 direction. Magnetization measurements on a powdered sample showed ferrimagnetic behavior at low temperatures. Under zero-field cooling (ZFC) measurement at 100 Oe, the observed blocking temperature (T(B)) was 37 K.
RESUMO
The preparation of nanostructures using porous anodic aluminum oxide (AAO) as templates involves the introduction of dissolved materials into the pores of the membranes; one way to determine which materials are preferred to fill the pores involves the measurement of the contact angles (theta) of different solvents or test liquids on the AAOs. Thus, we present measurements of contact angles of nine solvents on four different AAO sheets by tensiometric and goniometric methods. From the solvents tested, we found dimethyl sulfoxide (DMSO) and N,N(')-dimethylformamide (DMF) to interact with the AAOs, the polarity of the solvents and the surfaces being the driving force.