RESUMO
NO2 is one of the main greenhouse gases, which is mainly generated by the combustion of fossil fuels. In addition to its contribution to global warming, this gas is also directly dangerous to humans. The present work reports the structural and gas sensing properties of the CaCu3Ti4O12 compound prepared by the sol-gel technique. Rietveld refinement confirmed the formation of the pseudo-cubic CaCu3Ti4O12 compound, with less than 4 wt% of the secondary phases. The microstructural and elemental composition analysis were carried out using scanning electron microscopy and X-ray energy dispersive spectroscopy, respectively, while the elemental oxidation states of the samples were determined by X-ray photoelectron spectroscopy. The gas sensing response of the samples was performed for different concentrations of NO2, H2, CO, C2H2 and C2H4 at temperatures between 100 and 300 °C. The materials exhibited selectivity for NO2, showing a greater sensor signal at 250 °C, which was correlated with the highest concentration of nitrite and nitrate species on the CCTO surface using DRIFT spectroscopy.
RESUMO
The structure of electrical double layers at electrified interfaces is of utmost importance for electrochemical energy storage as well as printable, flexible, and bioelectronic devices, such as ion-gated transistors (IGTs). Here we report a study based on atomic force microscopy force-distance profiling on electrical double layers forming at the interface between the ionic liquid 1-ethyl-3-methylimidazolium bis(trifluoromethylsulfonyl)imide and sol-gel films of mesoporous tungsten oxide. We successfully followed, under in operando conditions, the evolution of the arrangement of the ions at the interface with the tungsten oxide films used as channel materials in IGTs. Our work sheds light on the mechanism of operation of IGTs, thus offering the possibility of optimizing their performance.
RESUMO
In this study, individual nanofabricated SnO micro-disks, previously shown to exhibit exceptional sensitivity to NOx, are investigated to further our understanding of gas sensing mechanisms. The SnO disks presenting different areas and thickness were isolated and electrically connected to metallic electrodes aided by a Dual Beam Microscope (SEM/FIB). While single micro-disk devices were found to exhibit short response and recovery times and low power consumption, large interconnected arrays of micro-disks exhibit much higher sensitivity and selectivity. The source of these differences is discussed based on the gas/solid interaction and transport mechanisms, which showed that thickness plays a major role during the gas sensing of single-devices. The calculated Debye length of the SnO disk in presence of NO2 is reported for the first time.
RESUMO
Application of nanoscale materials in photovoltaic and photocatalysis devices and photosensors are dramatically affected by surface morphology of nanoparticles, which plays a fundamental role in the understanding of the physical and chemical properties of nanoscale materials. Zinc oxide nanoparticles with an average size of 20nm were obtained by the use of a sonochemical technique. X-ray diffraction (XRD) associated to Rietveld refinements and transmission electron microscopy (TEM) were used to study structural and morphological characteristics of the samples. An amorphous shell approximately 10nm thick was observed in the ultrasonically treated sample, and a large reduction in particle size and changes in the lattice parameters were also observed.
RESUMO
We report two novel aspects relating to the growth of oriented 3D arrays of SnO2 nanorods, based on the "purpose-built materials" (PBM) strategy. Under controlled conditions, the substrate acted as a topographic template and the growth direction of the 3D arrays of SnO2 nanorods was unrelated to the crystallographic characteristic of the substrate. A growth process based on the oriented attachment mechanism was proposed to explain this behavior, and this findings, reported here for SnO2, can be extended to include other metal oxides.