RESUMO
The aim of this study was to evaluate the micro-shear bond strength (µSBS) of one and two steps self-etch adhesive systems after enamel bleaching with photo-activated bleaching systems of different hydrogen peroxide (HP) concentration. Occlusal enamel of forty intact human molars were flattened and assigned into four groups. GI Unbleached, GII, GIII, and GIV were bleached with Pyrenees (3.5% HP), GC TiON (20% HP), and Hi-Lite (35% HP) respectively. Enamel treatment with one and two steps self-etch adhesives (Clearfil S3 Bond- S3, and Clearfil SE Bond-SE) then micro-tubes were fixed on enamel and filled with AP-X composite (n=5). Bond was tested with the universal testing machine. Data were analyzed using two-way ANOVA and Tukey's tests at 5 % level of significance. The µSBS was significantly different between adhesives (F=154.46; p<0.05) and bleaching systems (F=77.33; p<0.05) with significant interaction. Specimens bonded with S3 shows a significantly lower µSBS than those bonded with SE (p<0.05) in all groups. For both adhesives the bleached groups demonstrate lower µSBS than unbleached except specimens bleached with Pyrenees and bonded with SE (p>0.05). A significant difference was observed between groups of the bleaching systems (p<0.05). Different peroxide concentrations photo-activated bleaching systems adversely affect µSBS of one and two steps self-etch adhesives. Low concentration system (Pyrenees) does not influence the bond strength of two steps adhesive.
Assuntos
Colagem Dentária , Peróxidos , Adesivos , Cimentos Dentários , Esmalte Dentário , Adesivos Dentinários , Humanos , Teste de Materiais , Dente Molar , Cimentos de Resina , Resistência ao CisalhamentoRESUMO
Objectives: The aim of this study was to evaluate chemical and topographical changes in the intaglio zirconia surface induced by chemical conditioning solutions using FTIR and SEM analysis. Material and method: twelve plates for each FTIR and SEM tests from each zirconia materials (UPCERA HT White, BruxZir® Solid Zirconia, and Copran® Multilayer), milled by a Yenadent CAD/CAM system, sintered and divided randomly into a three groups. A different surface conditioning was applied to the intaglio surface of each group: 30% hydrogen peroxide, 30% citric acid and control group. Result and discussion: by using of the FTIR spectroscopy, an evidence of new bands formation appeared at 1637cm-1 and 3352cm-1 due to the high oxidizing effect of hydrogen peroxide, and at 630cm-1 and 1663cm-1 due to the chelating action of citric acid, and simultaneously, SEM assessment of the surface topography took place, to identify lines, scratches, or surface dissociation that appeared on the intaglio zirconia surface after conditioning. Conclusion: such analysis provides an enhancement of new convenient, less expensive, reliable trials to improve micro-bond strength of luting cement to Y-TZP ceramics.