RESUMO

We report on temperature dependent TmMnO3 far infrared emissivity and reflectivity spectra from 1910 K to 4 K. At the highest temperature the number of infrared bands is lower than that predicted for centrosymmetric P63/mmc (D(4)(6h)) (Z = 2) space group due to high temperature anharmonicity and possible defect induced bitetrahedra misalignments. On cooling, at ~1600 ± 40 K, TmMnO3 goes from non-polar to an antiferroelectric-ferroelectric polar phase reaching the ferroelectric onset at ~700 K. Room temperature reflectivity is fitted using 19 oscillators and this number of phonons is maintained down to 4 K. A weak phonon anomaly in the band profile at 217 cm(-1) (4 K) suggests subtle Rare Earth magneto-electric couplings at ~TN and below. A low energy collective excitation is identified as a THz instability associated with room temperature eg electrons in a d-orbital fluctuating environment. It condenses into two modes that emerge pinned to the E-type antiferromagnetic order hardening simultaneously down to 4 K. They obey power laws with TN as the critical temperature and match known zone center magnons. The one peaking at 26 cm(-1), with critical exponent ß=0.42 as for antiferromagnetic order in a hexagonal lattice, is dependent on the Rare Earth ion. The higher frequency companion at ~50 cm(-1), with ß=0.25, splits at ~TN into two peaks. The weaker band of the two is assimilated to the upper branch of the gap opening in the transverse acoustical (TA) phonon branch crossing the magnetic dispersion found in YMnO3. (Petit et al 2007 Phys. Rev. Lett. 99 266604). The stronger second band at ~36 cm(-1) corresponds to the lower branch of the TA gap. We assign both excitations as zone center magneto-electric hybrid quasiparticles, concluding that in NdMnO3 perovskite the equivalent picture corresponds to an instability which may be driven by an external field to transform NdMnO3 into a multiferroic compound by perturbation enhancing the TA phonon-magnetic correlation.

Assuntos

RESUMO

We report on the far- and mid-infrared reflectivity of NdMnO3 from 4 to 300 K. Two main features are distinguished in the infrared spectra: active phonons in agreement with expectations for the orthorhombic [Formula: see text]-Pbnm (Z = 4) space group remaining constant down to 4 K and a well defined collective excitation in the THz region due to eg electrons in a d-orbital fluctuating environment. We trace its origin to the NdMnO3 high-temperature orbital disordered intermediate phase not being totally dynamically quenched at lower temperatures. This results in minute orbital misalignments that translate into randomized non-static eg electrons within orbitals yielding a room-temperature collective excitation. Below TN ∼ 78 K, electrons gradually localize, inducing long-range magnetic order as the THz band condenses into two modes that emerge pinned to the A-type antiferromagnetic order. They harden simultaneously down to 4 K, obeying power laws with TN as the critical temperature and exponents ß âˆ¼ 0.25 and ß âˆ¼ 0.53, as for a tri-critical point and Landau magnetic ordering, respectively. At 4 K they match known zone center spin wave modes. The power law dependence is concomitant with a second order transition in which spin modes modulate orbital instabilities in a magnetoelectric hybridized orbital-charge-spin-lattice scenario. We also found that phonon profiles also undergo strong changes at TN ∼ 78 K due to magnetoelasticity.

RESUMO

We report on near normal far- and mid-infrared emission and reflectivity of NdMnO3 perovskite from room temperature to sample decomposition above 1800 K. At 300 K the number of infrared active phonons is in close agreement with the 25 calculated for the orthorhombic D(2h)(16)-Pbnm (Z = 4) space group. Their number gradually decreases as we approach the temperature of orbital disorder at ~1023 K where the orthorhombic O' lower temperature cooperative phase coexists with the cubic orthorhombic O. At above ~1200 K, the three infrared active phonons coincide with that expected for cubic Pm-3m (Z = 1) in the high temperature insulating regime. Heating samples in dry air triggers double exchange conductivity by Mn(3+) and Mn(4+) ions and a small polaron mid-infrared band. Fits to the optical conductivity single out the octahedral antisymmetric and symmetric vibrational modes as the main phonons in the electron-phonon interactions at 875 K. For 1745 K, it is enough to consider the symmetric stretching internal mode. An overdamped defect induced Drude component is clearly outlined at the highest temperatures. We conclude that rare earth manganite eg electrons are prone to spin, charge, orbital, and lattice couplings in an intrinsic orbital distorted perovskite lattice, favoring embryonic low energy collective excitations.

RESUMO

We report on electronic collective excitations in RMn(2)O(5) (R =Pr, Sm, Gd, Tb) showing condensation starting at and below ~T(N) ~T(C)~ 40-50 K. Their origin is understood as partial delocalized e(g) electron orbitals in the Jahn-Teller distortion of the pyramid dimer with strong hybridized Mn(3+)-O bonds. Our local probes, Raman, infrared, and x-ray absorption, back the conclusion that there is no structural phase transition at T(N)~T(C). Ferroelectricity is magnetically assisted by electron localization triggering lattice polarizability by unscreening. We have also found phonon hardening as the rare earth is sequentially replaced. This is understood as a consequence of lanthanide contraction. It is suggested that partially f-electron screened rare earth nuclei might be introducing a perturbation to e(g) electrons prone to delocalize as the superexchange interaction takes place.

RESUMO

An energy-dispersive X-ray absorption spectroscopy beamline mainly dedicated to X-ray magnetic circular dichroism (XMCD) and material science under extreme conditions has been implemented in a bending-magnet port at the Brazilian Synchrotron Light Laboratory. Here the beamline technical characteristics are described, including the most important aspects of the mechanics, optical elements and detection set-up. The beamline performance is then illustrated through two case studies on strongly correlated transition metal oxides: an XMCD insight into the modifications of the magnetic properties of Cr-doped manganites and the structural deformation in nickel perovskites under high applied pressure.

Assuntos

RESUMO

The new double perovskite Pb2ScSbO6 was synthesized by standard ceramic procedures; the Rietveld refinement of room temperature neutron powder diffraction data shows that the crystal structure is well defined in the space group Fm3[combining macron]m. It contains a completely ordered array of alternating ScO6 and SbO6 octahedra sharing corners; the PbO12 polyhedra present an off-center displacement of the lead atoms along the [111] direction, due to the electrostatic repulsion between the Pb2+ 6s lone pair and the Pb-O bonds of the cuboctahedron. Dielectric permittivity measurements show a peak near 343 K, with a Curie-Weiss response above this temperature, which suggests an antiferroelectric behavior. Finally we present a DFT study of the electronic structure of Pb2ScSbO6, showing a great difference between the electronic density within SbO6 and ScO6 octahedra.