RESUMO
This work reports the synthesis, characterization, and in vitro release studies of pH- and temperature-sensitive Fe3O4-SiO2-poly(NVCL-co-MAA) nanocomposite. Fe3O4 nanoparticles were prepared by chemical coprecipitation, coated with SiO2 by the Stöber method, and functionalized with vinyl groups. The copolymer poly(N-vinylcaprolactam-co-methacrylic acid) (poly(NVCL-co-MAA)) was grafted onto the functionalized Fe3O4-SiO2 nanoparticles by free radical polymerization. XRD, FTIR, TGA, VSM, and TEM techniques were performed to characterize the nanocomposite. The release behavior of Doxorubicin (DOX) loaded in the nanocomposite at pH 5.8 and 7.4, and two temperatures, 25 and 37 °C, was studied. According to the release studies, approximately 55% of DOX is released in 72 h at pH 7.4, regardless of temperature. At pH 5.8, 78% of DOX was released in 48 h at 25 °C, and when increasing the temperature to 37 °C, more than 95 % of DOX was released in 24 h. The DOX release data treated with Zero-order, first-order, Higuchi, and Korsmeyer-Peppas models showed that Higuchi's model best fits the data, indicating that the DOX is released by diffusion. The findings suggest that the synthesized nanocomposite may be useful as a DOX carrier in biomedical applications.
RESUMO
The interest in multifunctional biomaterials to be implanted are also able to release drugs that reduce pain and inflammation or prevent a possible infection has increased. Bioactive materials such as silica (SiO2) containing surface silanol groups contribute to the nucleation and growth of hydroxyapatite (HAp) in a physiological environment. Regarding biocompatibility, the spherical shape of particles is the desirable one, since it does not cause mechanical damage to the cell membrane. In this work, the synthesis of SiO2 microspheres was performed by the modified Stöber method and they were used for the biomimetic growth of HAp on their surface. The effect of the type of surfactant (sodium dodecyl sulphate (SDS), cetyltrimethylammonium bromide (CTAB), and polyethylene glycol (PEG)), and heat treatment on the morphology and size of SiO2 particles was investigated. Monodisperse, spherical-shaped SiO2 microparticles with an average particle size of 179 nm, were obtained when using PEG (SiO2-PEG). The biomimetic growth of HAp was performed on this sample to improve its biocompatibility and drug-loading capacity using gentamicin as a model drug. Biomimetic growth of HAp was confirmed by FTIR-ATR, SEM-EDX and TEM techniques. SiO2-PEG/HAp sample had a better biocompatibility in vitro and gentamicin loading capacity than SiO2-PEG sample.